Search

High‐temperature piezoelectric sensing is usually used in the aerospace, automotive, and power plant fields. High temperature piezoelectric ceramics are considered the key materials in these fields. In this paper, Ca1−x(Ba1/2Sr1/2)xBi2Nb1.985(W3/4Mn1/4)0.015O9 (x = 0.05, 0.10, 0.15 and 0.20) (C1−xBSxBNWM) has been synthesized by a traditional solid state reaction method. The effects of substitution of calcium at the A‐site by barium and strontium on phase evolution and piezoelectric properties of the CaBi2Nb2O9 orthorhombic Aurivillius phases were investigated. The crystal structure of piezoelectric ceramics was characterized by XRD, Rietveld refinement, and Raman spectroscopy. Co‐substitution of barium/strontium (Ba2+/Sr2+) and tungsten/manganese (W6+/Mn4+) resulted in lattice distortion of C1−xBSxBNWM ceramics. The results induce that the tetragonal crystal structure increase with increasing the co‐substitution cations. Isothermal impedance spectroscopy confirmed intrinsic thermally activated conduction in the system. The C1−xBSxBNWM ceramics with x = 0.15 exhibit a very high Curie temperature (TC ∼ 923°C), a reasonable piezoelectric coefficient (d33 = 13.3 pC/N). Remarkably, even after thermal annealing at temperatures up to 800°C, it still retains a high d33 of 13 pC/N. In addition, the C0.85BS0.15BNWM ceramic had a relatively high resistivity (3.82 × 106 Ω·cm, 500°C). The Ca0.85(Ba1/2Sr1/2)0.15Bi2Nb1.985(W3/4Mn1/4)0.015O9 ceramics make possible their application in high‐temperature acceleration transducers. [ABSTRACT FROM AUTHOR]

The effects of geometric configuration and external force on piezocatalytic properties of BaTiO3 were investigated through experimental and finite element analyses. The simulated results indicate that the piezopotential is linearly related to the sample length of Z-axis of BaTiO3 and the magnitude of applied stress. Then, BaTiO3 single crystal fibers were prepared by using a hydrothermal method with K2Ti4O9 nanowires as the templet. By adjusting the hydrothermal temperature and Ba/Ti ratio in the precursor, BaTiO3 fibers exhibit different crystallinity and morphologies. Compared with BaTiO3 fibers with low aspect ratio, BaTiO3 fibers with high aspect ratio exhibit high piezocatalytic efficiency. Furthermore, the external force is tailored by changing the ultrasonic power during the piezocatalytic reaction. The increase in ultrasonic power is beneficial to improve piezocatalytic efficiency. Therefore, this work provides further insights on the relationship between piezocatalytic performances and morphology of catalysts as well as their working conditions. [ABSTRACT FROM AUTHOR]

In this paper, screen-printed electrodes are asymmetrically fabricated on three different dielectrics (multi-layered polyimide, quartz, and alumina). Supplied with AC power, sustainable surface dielectric barrier discharge (SDBD) plasma is generated in atmospheric pressure. During plasma processing, different changes of material degradation and discharge images are observed. The corresponding electrical and optical characteristics are investigated by optical emission spectra (OES) and Lissajous figure analysis, respectively. It is found that both dielectric degradation and electrode erosion occur on the surface of the polyimide based SDBD device, while there is only electrode erosion for the quartz and alumina based devices, which results in different changes of electrical characteristics. OES calculated results show that with an increase of discharge aging time, electron temperature increases for the polyimide based SDBD device and decreases for quartz and alumina based SDBD devices, while all the gas temperatures of three dielectrics increase with the aging time. Furthermore, compared to vibrational temperature and gas temperature, the distribution of electron temperature is more suitable for evaluating the changes in discharge uniformity during plasma processing. [ABSTRACT FROM AUTHOR]

High‐performance colossal‐permittivity (CP) materials have huge potential applications in the miniaturization of electronic components and high‐energy storage applications. Here, we report CP behavior in rare‐earth Ln‐doped BaTiO3 (Ln = La, Ce, Pr, Nd, Sm, Gd, Dy, Ho, and Er) ceramics. CP (>1 × 105) and low loss (<5% at 1 kHz) were achieved. Additionally, all ceramic samples with excellent temperature stability over a wide temperature range (25–250°C). X‐ray photoelectron spectroscopy verified the existence of point defects (Ti3+ and VO••$V_{\rm{O}}^{{\rm{ \bullet \bullet }}}$) in Ln‐doped BaTiO3 ceramic samples annealed in an N2 atmosphere. Electron paramagnetic resonance further demonstrated the existence of Ti3+. The coupling of point defects forms an electron‐pinned defect‐dipoles (EPDD) effect and induces strong hopping polarization. In addition, an internal barrier layer capacitance (IBLC) effect and a surface barrier layer capacitor (SBLC) effect are identified by impedance spectroscopy and DC bias voltage. The CP is attributed to the combined effect of EPDD, IBLC, and SBLC. Furthermore, the high‐temperature stability of CP is related to the strong coupling of defect‐dipole complexes. [ABSTRACT FROM AUTHOR]

The existence of polar nanoregions (PNRs) is the most important characteristic of ferroelectric relaxors; however, the size determination and the dynamic of PNRs remain uncertain. Herein, it is revealed that a re‐entrant relaxor behavior and ferroelectric–paraelectric transition coexist in complex perovskite oxide 0.6Bi(Mg1/2Ti1/2)O3‐0.4PbTiO3. Two dielectric anomalies, 1) the low‐temperature re‐entrant relaxor transition and 2) the high‐temperature diffuse phase transition (DPT), are described by the phenomenological statistical model. The sizes of the two kinds of PNRs corresponding to two ferroelectric states were obtained. The dynamics of PNRs are analyzed using isothermal electrical modulus, which shows three critical temperatures associated with the DPT, the formation, and freezing of PNRs, respectively. The temperature evolution of the PNRs evolution depends on the stoichiometry of bismuth. The results provide new insights into the dynamic behavior of PNRs and the modification way of re‐entrant relaxor behavior. [ABSTRACT FROM AUTHOR]

Among Aurivillius-phase ferroelectric ceramics, CaBi2Nb2O9 is considered as the best candidate with potential applications in ultrahigh-temperature piezoelectric devices due to the highest Tc (∼940 °C). This paper reports that BiMn co-substitution at A and B sites gives rise to dramatic enchantments in ferroelectricity, piezoelectricity, and electrical resistivity of CaBi2Nb2O9 ceramics. The optimum composition (Ca0.97Bi2.03Nb1.99Mn0.01O9) with a Tc of 953 ± 3°C shows a high ferroelectric remnant polarization (Pr), field-induced strain (S33), piezoelectric activity d33 and d 33 ∗ with values of ∼11.1 µC/cm2, 4.9 × 10−4, 20.8 and 26.1 pC/N, respectively, which are about two to three times those of CaBi2Nb2O9. Significant ferroelectric remnant polarization (Pr = 11.1 µC/cm2), field-induced strain (S33 = 4.9 × 10−4), and piezoelectric activity (d33 = 20.8 pC/N, d 33 ∗ = 26.1 pC/N) are simultaneously induced in ultrahigh Tc CaBi2Nb2O9 piezoceramics by BiMn substitution. [ABSTRACT FROM AUTHOR]