Ti-6Al-4V titanium alloy is known as one of the most difficult metallic materials to machine, and the machined surface residual stress distribution significantly affects properties such as static strength, fatigue strength, corrosion resistance, etc. This study utilized finite element software Abaqus 2020 to simulate the two-step cutting process of titanium alloy, incorporating stages of cooling, unloading, and de-constraining of the workpiece. The chip morphology and cutting force obtained from orthogonal cutting tests were used to validate the finite element model. Results from the orthogonal cutting simulations revealed that with increasing cutting speed and the tool rake angle, the residual stress undergoes a transition from compressive to tensile stress. To achieve greater residual compressive stress during machining, it is advisable to opt for a negative rake angle coupled with a lower cutting speed. Additionally, in two-step machining of titanium alloy, the initial cutting step exerts a profound influence on the subsequent cutting step, thereby shortening the evolution time of the Mises stress, equivalent plastic strain, and stiffness damage equivalent in the subsequent cutting step. These results contribute to optimizing titanium alloy machining processes by providing insights into controlling residual stress, ultimately enhancing product quality and performance of structural part of titanium alloy. [ABSTRACT FROM AUTHOR]

A kind of multiscale β-sialon grain-reinforced Al2O3 matrix composite ceramic tool material, named ASN, was prepared and studied. For the ASN, β-sialon (molecular formula: Si4Al2O2N6) was synthesized in situ by a hot-pressing and solid-solution reaction process. A total of six samples were prepared at varying sintering temperatures and holding times under vacuum conditions. The solid solution reaction mechanism of β-sialon, the phase composition, mechanical properties, microstructure, and strengthening and toughening mechanisms of the composite ASN were investigated. As a result, within the experimental parameters, an optimal ASN tool material was obtained under a pressure of 32 MPa and at a temperature of 1550 °C for 20 min. The tested mechanical properties of the optimal sample were as follows: flexural strength 997 ± 59 MPa, fracture toughness 6.4 ± 0.3 MPa·m1/2, Vickers hardness 18.2 ± 0.4 GPa, and relative density 98.1 ± 0.2%. According to crystal defect theory, the solid solution reaction mechanism of in-situ-synthesized β-sialon in an Al2O3 matrix involves a double mechanism of unequivalence (or hetero-valence) and interstitial filling. The multiscale β-sialon grains mainly consisted of four grains, which were elongated β-sialon grains with a diameter of 0.3–0.4 μm and an aspect ratio of 6–9, elongated β-sialon grains with a diameter of 70 nm and an aspect ratio of 10, β-sialon whiskers with a diameter of 0.2 μm and an aspect ratio of 12–15, and intragranular β-sialon whiskers with a diameter of 70 nm. The mechanical properties were improved due to strengthening and toughening mechanisms, such as mixed structure mode (intergranular and transgranular), elongated grain pullout, interface bonding, crack reflection, pinning, and bridging. [ABSTRACT FROM AUTHOR]