The high-temperature corrosion behavior of anode current collectors in liquid Ag under an oxidizing atmosphere was investigated. The weight gain in oxygen was higher than that of liquid Ag because of the effective barrier formed by Ag-rich layer coated on the corrosion layer. The thickness of the corrosion layer under oxygen was approximately twice that of the layer developed under liquid Ag because of the effective barrier originating from the Ag-rich layer. The corrosion products on the surface of the specimens in both oxygen and liquid Ag were Al2O3 and FeAl2O4 from 24 to 168 h. The surface morphology that was developed on the scale of the corroded layer represented a buckle structure in liquid Ag and a convoluted structure in oxygen, which resulted from the lateral growth of the oxide. This study proved the improved stability and cost-effectiveness of using FeCrAl alloy as a current collector in a solid oxide membrane system. [ABSTRACT FROM AUTHOR]

Abstract This paper reports the preparation of Ti microparticles that are angular and spherical in shape through the combustion of a TiO 2 + αCa (where α is moles of Ca) exothermic mixture in an inert atmosphere. The relationship between the combustion parameters and the properties of the resultant Ti particles is discussed with consideration of the effect of Ca concentration. Using excess amounts of Ca in the experiment was effective in modifying the shape of the particles from angular to spherical. The Ti powder was found to be well-dispersed and the diameter of individual particles ranged from 5 µm to 50 µm. Based on the combustion parameters, the activation energy for the redox reaction was calculated as ∼ 138 kJ/mol. This paper discusses the chemistry of the reduction process and highlights the effects of combustion temperature and the amount of liquid calcium on the characteristics of the Ti particles. Graphical abstract The combustion process in TiO 2 + Ca mixture developed a maximum temperature of about 1820 °C and resulted in Ti spherical particles. fx1 [ABSTRACT FROM AUTHOR]