In order to conduct a comprehensive roughness analysis, around sixty 3D roughness parameters are created to describe most of the surface morphology with regard to specific functions, properties or applications. In this paper, a multiscale surface topography decomposition method is proposed with application to stainless steel (AISI 304), which is processed by rolling at different fabrication stages and by electrical discharge tool machining. Fifty-six 3D-roughness parameters defined in ISO, EUR, and ASME standards are calculated for the measured surfaces. Then, expert software "MesRug" is employed to perform statistical analysis on acquired data in order to find the most relevant parameters characterizing the effect of both processes (rolling and machining), and to determine the most appropriate scale of analysis. For the rolling process: The parameter Vmc (the Core Material Volume--defined as volume of material comprising the texture between heights corresponding to the material ratio values of p = 10% and q = 80%) computed at the scale of 3 µm is the most relevant parameter to characterize the cold rolling process. For the EDM Process, the best roughness parameter is SPD that represents the number of peaks per unit area after segmentation of a surface into motifs computed at the scale of 8 µm., (© Wiley Periodicals, Inc.)

Dynamic evolution of surface roughness and influence of initial roughness (S(a) = 0.282-6.73 µm) during friction and wear processes has been analyzed experimentally. The mirror polished and rough surfaces (28 samples in total) have been prepared by surface polishing on Ti-6Al-4V and AISI 1045 samples. Friction and wear have been tested in classical sphere/plane configuration using linear reciprocating tribometer with very small displacement from 130 to 200 µm. After an initial period of rapid degradation, dynamic evolution of surface roughness converges to certain level specific to a given tribosystem. However, roughness at such dynamic interface is still increasing and analysis of initial roughness influence revealed that to certain extent, a rheology effect of interface can be observed and dynamic evolution of roughness will depend on initial condition and history of interface roughness evolution. Multiscale analysis shows that morphology created in wear process is composed from nano, micro, and macro scale roughness. Therefore, mechanical parts working under very severe contact conditions, like rotor/blade contact, screws, clutch, etc. with poor initial surface finishing are susceptible to have much shorter lifetime than a quality finished parts., (© Wiley Periodicals, Inc.)