Search

This paper deals with the testing of three materials for special heat exchanger for short-time application. Mechanical and microstructural properties after aging at 650 and 850 °C were tested and analysed. The results will serve as an input data for the design and construction of plate heat exchanger.

This work deals with the fabrication of one low density steel by mixing AISI S2 tool steel and AlSi10Mg powders using powder-based directed energy deposition (P-DED) technique. Two approaches of mixing powders were compared-continuous mixing during the process (in-situ) and mixing the powder prior to the process (premixed). The P-DED sample was characterised by a variety of techniques such as optical microscopy, scanning electron microscopy, electron backscatter diffraction, X-ray diffraction, and hardness measurement. Our findings demonstrate the successful achievement of steel with a 8 wt. % AlSi10Mg addition when two dissimilar powders are premixed, resulting in approximately 12% reduction in the density of S2 steel. Optimizing the powder feed rate and the ratio of AlSi10Mg powder contribute to an improvement of printability, eliminating materials separation, leading to a homogenous deposited part. Compared to the in-situ mixing case, the premixed process within the current process window generates a more homogeneous microstructure consisting of three phases: Ferrite, Fe 3 Al and Fe 3 AlC carbide. Whereas, the in-situ sample exhibits only two phases Ferrite and Fe 3 Al. The hardness of the premixed sample is found to be slightly higher compared to the in-situ sample., (© 2023. The Author(s).)

The creep properties of a laser-directed energy deposition (L-DED) technique manufactured Inconel 718 (IN718) was investigated at 650 °C/700 MPa. Microstructure and creep properties of L-DED IN718 samples were tailored by various post heat treatments involving homogenization heat treatment with temperature ranging from 1080 to 1180 °C + double aging and hot isostatic pressing (HIP). Microstructural changes and their influence on the creep behavior and fracture mechanism were observed and discussed. The results show that L-DED sample heat treated by a simple double aging exhibits a 49% increase in creep lifetime t r and a comparable creep elongation ɛ f when compared to the wrought material, due to the reserved coarse dislocation cell substructure from the L-DED process. The loss of dislocation cell structure and the coarsening of grains at higher temperature of heat treatments contributes to a shorter t r, ε f , but faster ε̇ min (minimum creep rate). The present work demonstrates that a simultaneous improvement of creep strength and creep elongation can be achieved in the case of a coarse-grained L-DED IN718 by a double aging treatment which can preserve both the strengthening precipitates and an appropriate size of dislocation cells.

In the present study, the effect of material deposition at the elevated temperature baseplate on the microstructure and mechanical properties was investigated and correlated to the unique thermal history by using numerical simulation. Numerical results agreed well with the experimental results of microstructure and mechanical properties. Numerical results revealed a significant decrease in temperature gradient and a 40% decrease in thermal stress due to material deposition on the elevated temperature baseplate. The reduced thermal stress and temperature gradient resulted in coarser grain features, which in turn led to a decrease in hardness and tensile strength, especially for the bottom region near the baseplate. Meanwhile, no significant effect could be found for ductility. In addition, an elevated temperature baseplate promoted less heterogeneity in hardness and tensile properties along the building direction. The current work demonstrates a collective and direct understanding of the baseplate preheating effect on thermal stress, microstructure and mechanical properties and their correlations, which is believed beneficial for the better utilization of baseplate preheating positive effects.

Continuous cooling transformation (CCT) diagrams are widely used when heat treating steels and represent which type of phase will occur in a material as it is cooled at different cooling rates. CCT diagrams are constructed on the basis of dilatometry measurements on relatively small testing samples (cylindrical shape with diameter of 4mm and length of 11 mm in this study). The main aim of this work was to demonstrate the possibility of evaluating the tensile test properties using mini-tensile tests from miniature volumes (1.4 × 10 -7 m 3 for one sample) subsequent to determination of the CCT diagram and to extend a standard CCT diagram with information about strength, ductility and the estimated value of the work-hardening coefficient. Mini-tensile tests (MTT) were recently developed due to the low availability of experimental material and have already been successfully used for local mechanical property characterization of metals. CCT diagrams were constructed for 42CrMo4 steel prepared by the laser-directed energy deposition (L-DED) process, for commercially available 42CrMo4 steel conventionally manufactured (for comparison of traditional processing and AM preparation) and for H13 tool steel deposited by the selective laser melting (SLM) process.

Additive manufacturing (AM) becomes a more and more standard process in different fields of industry. There is still only limited knowledge of the relationship between measured material data and the overall behaviour of directed energy deposition (DED)-processed complex structures. The understanding of the structural performance, including flow curves and local damage properties of additively manufactured parts by DED, becomes increasingly important. DED can be used for creating functional surfaces, component repairing using multiple powder feeders, and creating a heterogeneous structure with defined chemical composition. For thin parts that are used with the as-deposited surface, this evaluation is even highly crucial. The main goal of the study was to predict the behaviour of thin-walled structures manufactured by the DED process under static loading by finite element analysis (FEA). Moreover, in this study, the mechanical performance of partly machined and fully machined miniaturized samples produced from the structure was compared. The structure studied in this research resembles a honeycomb shape made of austenitic stainless steel AISI 316L, which is characterized by high strength and ductility. The uncoupled damage models based on a hybrid experimental-numerical approach were used. The microstructure and hardness were examined to comprehend the structural behaviour.

The microstructural morphology in additive manufacturing (AM) has a significant influence on the building structure. High-energy concentric heat source scanning leads to rapid heating and cooling during material deposition. This results in a unique microstructure. The size and morphology of the microstructure have a strong directionality, which depends on laser power, scanning rate, melt pool fluid dynamics, and material thermal properties, etc. The grain structure significantly affects its resistance to solidification cracking and mechanical properties. Microstructure control is challenging for AM considering multiple process parameters. A preheating base plate has a significant influence on residual stress, defect-free AM structure, and it also minimizes thermal mismatch during the deposition. In the present work, a simple single track deposition experiment was designed to analyze base plate preheating on microstructure. The microstructural evolution at different preheating temperatures was studied in detail, keeping process parameters constant. The base plate was heated uniformly from an external heating source and set the stable desired temperature on the surface of the base plate before deposition. A single track was deposited on the base plate at room temperature and preheating temperatures of 200 °C, 300 °C, 400 °C, and 500 °C. Subsequently, the resulting microstructural morphologies were analyzed and compared. The microstructure was evaluated using electron backscattered diffraction (EBSD) imaging in the transverse and longitudinal sections. An increase in grain size area fraction was observed as the preheating temperature increased. Base plate preheating did not show influence on grain boundary misorientation. An increase in the deposition depth was noticed for higher base plate preheating temperatures. The results were convincing that grain morphology and columnar grain orientation can be tailored by base plate preheating.

Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies. This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of parts produced by additive manufacturing (shortly, AM parts) with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and the residual stresses. Based on these aspects, basic concepts are reviewed and critically discussed specifically for AM materials: Criteria for damage tolerant component design;Criteria for the determination of fatigue and fracture properties;Strategies for the determination of the fatigue life in dependence of different manufacturing conditions;Methods for the quantitative characterization of microstructure and defects;Methods for the determination of residual stresses;Effect of the defects and the residual stresses on the fatigue life and behaviour. We see that many of the classic concepts need to be expanded in order to fit with the particular microstructure (grain size and shape, crystal texture) and defect distribution (spatial arrangement, size, shape, amount) present in AM (in particular laser powder bed fusion). For instance, 3D characterization of defects becomes essential, since the defect shapes in AM are diverse and impact the fatigue life in a different way than in the case of conventionally produced components. Such new concepts have immediate consequence on the way one should tackle the determination of the fatigue life of AM parts; for instance, since a classification of defects and a quantification of the tolerable shapes and sizes is still missing, a new strategy must be defined, whereby theoretical calculations (e.g. FEM) allow determining the maximum tolerable defect size, and non-destructive testing (NDT) techniques are required to detect whether such defects are indeed present in the component. Such examples show how component design, damage and failure criteria, and characterization (and/or NDT) become for AM parts fully interlinked. We conclude that the homogenization of these fields represents the current challenge for the engineer and the materials scientist., Competing Interests: Declaration of interests The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.