Search

Biomass‐derived feedstocks play a vital role in sustainable economies for renewable energy, waste management, energy security, and commercial prospects. This study focused on promoting the ring hydrogenation of furfural (FAL) into tetrahydrofurfuryl alcohol (THFA) in an aqueous solution using a potential Ni−Re‐supported hydrotalcite‐derived MgAl catalyst at different Ni : Re molar ratios. Structural analyses, such as an in situ time‐resolved X‐ray absorption near edge structure, under H2 reduction elucidated the simultaneous transformation of Re6+ and Re7+ to Re0 with the remaining highly stable Ni2+. The construction of Ni−Re on hydrotalcite‐derived MgAl catalyst resulted in the alleviated H2 reduction behavior, facilitated H2 adsorption and desorption processes, and suitable catalyst acidity detected by H2 temperature‐programmed reduction, and H2 and NH3 temperature‐programmed desorption experiments, respectively. Under optimized conditions, a maximum THFA yield of 78 % with a complete FAL conversion was attained using Ni1Re0.16/MgO−Al2O3 catalyst at a reaction temperature of 140 °C, H2 pressure of 20 bar, catalyst loading of 20 %, and reaction time of 2 h in a H2O system. Isotopic deuterium (D2O) labeling revealed that D substitution was notably pronounced through isotopic exchange between the D atom from D2O and H atom in FAL during its hydrogenation to THFA. [ABSTRACT FROM AUTHOR]

In this study, nickel supported on various metal oxides were prepared by simple impregnation and the performance for CO2 methanation was tested. The oxide supports were all prepared by thermal decomposition of metal salts to provide comparable oxide properties such as surface area. Among the investigated oxides, nickel supported on CeO2 and Y2O3 showed the highest CO2 conversion of 90% at 320 °C with highest CH4 selectivity of 99%. The order of catalyst activity (XCO2@320°C) was reported: Ni/CeO2 ~ Ni/Y2O3 > > Ni/La2O3 > Ni/ZrO2 > Ni/Al2O3 > Ni/MgO > Ni/CaO > > Ni/MnO. The physicochemical properties of the catalysts were analyzed by TEM, BET, XRD, ICP, H2-TPR, CO2-TPD, H2 chemisorption, TGA, Raman, and XPS. From the characterization results, the catalyst activity was independent to specific surface area of catalyst and crystallite size of Ni. The amount of oxygen vacancies and weak-to-medium basic sites exhibited major roles for enhancing catalyst activity. The CeO2 and Y2O3 as reducible oxide supports not only provided abundant oxygen vacancies / basic sites, but also promoted Ni dispersion with appropriate interaction between metal and support, resulting in higher reducibility at low temperature. The reduction of catalyst at high temperature can significantly improve the performance of Ni supported on non-reducible MgO. However, the Ni/CeO2 and Ni/Y2O3 reduced at high temperature suffered from coalescence of CeO2 and Y2O3, though Ni crystallite sizes are well preserved from sintering. [ABSTRACT FROM AUTHOR]

Catalytic thermochemical conversion offers a sustainable method to upgrade oil‐based feedstocks into highly valuable biofuel, aligning with the modern biorefinery concept. Herein, a series of IrRe/SAPO‐11 catalysts with different Ir to Re molar ratios compared to reference Ir/SAPO‐11 and Re/SAPO‐11 catalysts was prepared using a wetness impregnation method. These catalysts were used for the direct production of sustainable aviation fuels (SAFs) via efficient hydrodeoxygenation and hydroisomerization of triglycerides. The catalyst screening confirmed that the optimum IrRe/SAPO‐11 catalyst, with an equivalent Ir to Re molar ratio, exhibited the highest hydrodeoxygenation activity under milder operation conditions than the conditions used in previous studies. Increasing the reaction temperature up to 330 °C enhanced the formation of iso‐alkanes in the liquid product, achieving a freezing point of −31.4 °C without additional cold flow improvers. Furthermore, a long‐term stability experiment demonstrated that the developed Ir−Re system exhibited exceptional performance over 150 h. This excellent catalytic activity and stability of the bifunctional IrRe/SAPO‐11 catalyst was owing to its suitable interface between metallic and oxide sites, mixed mesoporous structures, reduced catalyst size, and increased Lewis acid ratio, as confirmed by our comprehensive characterizations. [ABSTRACT FROM AUTHOR]

In this study, the improvement of heat transfer was applied to eliminate hotspots of a highly exothermic reaction, Fischer–Tropsch synthesis (FTS), by means of two facile methods: (I) adding high thermal conductive materials media diluted in catalysts (SiC and Al chips), and (II) using structured reactors equipped with well-designed structured catalysts with advantages of heat dissipation/removal. The 20%Co/SiO2 catalyst powder prepared by simple impregnation was employed for constructing structured catalysts and granular packed bed catalysts. The structured catalyst was prepared by coating method of Co/SiO2 slurry on an aluminum spiral and plate substrate. The catalytic performance of as-prepared catalysts was then tested for FTS in a fixed-bed reactor at 210–230 °C, 20 bar. Both gaseous and liquid products were collected and analyzed. The heat transfer improvement of packed bed catalytic system and structured catalytic system were compared and discussed. As a result, the structured catalytic system with spiral structured catalyst can provide the best improvement of heat/mass transfer, resulting in enhanced diesel selectivity, though the oil production rate was unsatisfactory. Meanwhile, among the packed bed catalytic systems, SiC media possessed the best heat removal material, producing the highest oil yield. In addition, the fresh and spent catalysts were analyzed by several techniques including TEM, SEM, XRD, BET, ICP-OES, H2–TPR, and TGA to relate the physicochemical properties of the prepared catalysts and its FTS performance. [ABSTRACT FROM AUTHOR]

Direct conversion of biogas via the integrative process of dry reforming of methane (DRM) and catalytic methane decomposition (CDM) has received a great attention as a promising green catalytic process for simultaneous production of syngas and carbon nanotubes (CNTs). In this work, the effects of reaction temperature of 700–1100 °C and CH4/CO2 ratio of biogas were investigated over NiMo/MgO catalyst in a fixed bed reactor under industrial feed condition of pure biogas. The reaction at 700 °C showed a rapid catalyst deactivation within 3 h due to the formation of amorphous carbon on catalyst surface. At higher temperature of 800–900 °C, the catalyst can perform the excellent performance for producing syngas and carbon nanotubes. Interestingly, the smallest diameter and the highest graphitization of CNTs was obtained at high temperature of 1000 °C, while elevating temperature to 1100 °C leads to agglomeration of Ni particles, resulting in a larger size of CNTs. The reaction temperature exhibits optimum at 800 °C, providing the highest CNTs yield with high graphitization, high syngas purity up to 90.04% with H2/CO ratio of 1.1, and high biogas conversion (XCH4 = 86.44%, XCO2 = 95.62%) with stable performance over 3 h. The typical composition biogas (CH4/CO2 = 1.5) is favorable for the integration process, while the CO2 rich biogas caused a larger grain size of catalyst and a formation of molybdenum oxide nanorods (MoO3). The long-term stability of NiMo/MgO catalyst at 800 °C showed a stable trend (> 20 h). The experimental findings confirm that NiMo/MgO can perform the excellent activity and high stability at the optimum condition, allowing the process to be more promising for practical applications. [ABSTRACT FROM AUTHOR]

Selective hydrogenation and hydrogenolysis of 5‐hydroxymethylfurfural (HMF) to 2,5‐bis(hydroxymethyl)furan (BHMF) and 2,5‐dimethylfuran (DMF) were explored by regulating the nanosized Pt on Co/Al2O3 catalysts. Characterization results revealed that the catalyst acidity was influenced by adjusting the Co/Pt composition, while the addition of more Pt loading on Co/Al2O3 catalysts resulted in a facilitation of H2 reduction process. Lower size of catalyst particles was obtained for the Co−Pt system in comparison to the monometallic Co/Al2O3 catalyst. Additionally, the structural characterizations by XRD, XANES, and XPS established the co‐existences between metallic Pt0/Co0 and oxophilic PtO2/CoOx, acting as the active components for the reactions. Operated under a full HMF conversion, the Co1Pt0.050Al catalyst with high Pt loading gave >99.9 % BHMF selectivity at 40 °C; whereas, an 86.7 % of DMF selectivity was noticeable over low Pt loading of the Co1Pt0.013Al catalyst at 160 °C. This investigation evidenced that the selective production of BHMF or DMF towards hydro‐conversion of HMF was relied on the amount of Pt contents on Co/Al2O3 catalyst, in which the metal sizes and acidity had meaningful effects on the hydrogenation and hydrogenolysis processes. [ABSTRACT FROM AUTHOR]

The upgradation of methane in biogas by hydrogenation of CO2 has been currently recognized as a promising route for efficient full utilization of renewable biogas with potential benefits for storage of renewable hydrogen energy and abatement of greenhouse gas emission. As a main constituent of biogas, CO2 can act as a backbone for the formation of additional CH4 by hydrogenation, then producing higher amounts of biomethane. In this work, the upgradation process was investigated in a prototype reactor of double pass operation with vertical alignment using an optimized Ni-Ce/Al-MCM-41 catalyst. The experimental results show that the double pass operation that removes water vapor during the run can significantly increase CO2 conversion, resulting in higher CH4 production yield. As a result, the purity of biomethane increased by 15% higher than a single pass operation. In addition, search for optimum condition of the process was carried out within an investigated range of conditions including flowrate (77–1108 ml min−1), pressure (1 atm–20 bar), and temperature (200–500 °C). The durability test for 458 h was performed using the obtained optimum condition, and it shows that the optimized catalyst can perform excellent stability with negligible influence by the observed change in catalyst properties. The comprehensive characterization on physicochemical properties of fresh and spent catalysts was performed, and the results were discussed. [ABSTRACT FROM AUTHOR]

A series of activated carbons (ACs) derived from spent disposable wooden chopsticks was prepared via steam activation and used to separate carbon dioxide (CO2) from a CO2/hydrogen (H2) mixed gas at atmospheric pressure. A factorial design was employed to investigate the effects of the activation temperature and time as well as their interactions on the production yield of ACs and their CO2 adsorption capacity. The activation temperature exhibited a much higher impact on both the production yield and the CO2 adsorption capacity of ACs than the activation time. The interaction of both parameters did not significantly affect the yield of ACs, but did affect the CO2 adsorption capacity. The optimal preparation condition provided ACs with a desirable yield of around 23.18% and a CO2 adsorption capacity of 85.19 mg/g at 25 °C and 1 atm and consumed the total energy of 225.28 MJ/kg AC or 116.4 MJ/g-mol CO2. A H2 purity of greater than 96.8 mol% was achieved from a mixed gas with low CO2 concentration (< 20 mol%) during the first 3 min of adsorption and likewise around 90 mol% from a mixed gas with a high CO2 concentration (> 30 mol%) during the first 2 min. The CO2 adsorption on the as-prepared ACs proceeded dominantly via multilayer physical adsorption and was affected by both the surface area and micropore volume of the ACs. The adsorption capacity was diminished by around 18% after six adsorption/desorption cycles. The regeneration of the as-prepared chopstick-derived ACs can be easily performed via heating at a low temperature and ambient pressure, suggesting their potential application in the temperature swing adsorption process. [ABSTRACT FROM AUTHOR]

Keywords: Hydrodeoxygenation; Isomerization; NiRe catalyst; Palm oil; Synthetic diesel EN Hydrodeoxygenation Isomerization NiRe catalyst Palm oil Synthetic diesel 1 1 1 10/12/23 20231006 NES 231006 B The Front Cover b illustrates an artwork design for showcasing the developed bifunctional NiRe/SAPO-11 catalyst along with "KHON", the masked dance drama in Thailand. Hydrodeoxygenation, Isomerization, NiRe catalyst, Palm oil, Synthetic diesel Front Cover: Enhancing the Hydrodeoxygenation and Isomerization using Re Nanoparticles Decorated on Ni/SAPO-11 Catalysts for Direct Production of Low-Cold Flow Diesel from Triglycerides (ChemCatChem 19/2023). [Extracted from the article]