Search

Background.: This study assessed the effect of repeated preheating of three types of composite resins and a giomer on their color stability. Methods.: In this in vitro study, 128 composite resin and giomer specimens with a 10-mm diameter and a 2-mm height were evaluated in eight groups (n=16) of Heliomolar microfilled, Brilliant Enamel microhybrid, and Tetric N-Ceram nanohybrid composite resins, and Beautifil II giomer used at room temperature and also after preheating of the tube in a water bath at 55‒60 °C for 40 times. After preparing the specimens, their color parameters were measured by a spectrophotometer. The specimens were immersed in a tea solution for 3 hours/day for 40 days and underwent spectrophotometric color assessment again. The color change (∆E) was calculated and analyzed by two-way ANOVA (α=0.05). Results.: The effects of composite resin type (P <0.001)>P<0.001)>P<0.001)>P<0.05).>P=0.003) and microhybrid composite resin (P =0.004). Conclusion.: Repeated preheating of giomer, microhybrid, and nanohybrid composite resin specimens to 55‒60 °C for 40 times adversely affected their color stability in the tea solution. The color change was significantly greater for giomer. [ABSTRACT FROM AUTHOR]

Aim: This study compared the effects of hydrogel and solution forms of sodium ascorbate (SA) with two different application times on bracket bond strength subsequent to bleaching. Materials and Methods: A total of 72 sound premolars were randomly divided into six groups (n = 12): An unbleached control group (group one) and five experimental groups of carbamide peroxide. Specimens in group two were bonded immediately after bleaching; specimens in groups three and four were bleached, then treated with SA solution for ten minutes and three hours, respectively, and then bonded. In groups five and six, SA hydrogel was used and the specimens were prepared similar to groups three and four, respectively. Following debonding, bond strengths were recorded in MPa. To evaluate the amount of resin left on the enamel surfaces, adhesive remnant index (ARI) scores were used. Statistical Analysis: The bond strength data were analyzed with ANOVA and pairwise comparisons were made by Tukey test. The ARI data were subjected to Kruskal-Wallis test and two-by-two comparisons were made by the Mann-Whitney U test. Results: There were significant differences in bond strengths between the groups ( P < 0.0005). However, the differences between groups three, four, five and six were not significant. Furthermore, there were no significant differences between group one and groups four and six, whereas the differences between the other groups were significant ( P < 0.05). Regarding ARI, there were significant differences among the groups ( P = 0.004). Conclusion: Bleaching significantly decreased the bracket bond strength. Compromised bonding was reversed with a three-hour application of both forms of SA.

Background: Cention N has been introduced as an alternative material for amalgam. The purpose was to investigate the flexural strength and microhardness of this material in self-cure and dual-cure modes before and after thermocycling. Materials and Methods: In this experimental study, 40 samples of Cention N were prepared in order to determine and compare the microhardness. Half of the samples were set by self-cure method and the other half with dual-cure method. The Vickers microhardness test was performed once after 24 h and again after 10000 thermocyclings. Three-point flexural test was used to determine and compare the flexural strength of 52 rod-shaped samples. Half of the samples were set by self-cure method and the other half with dual-cure method. Among 26 samples in each group, 13 samples were randomly selected and three-point flexural test was performed after 24 h and for another 13 samples after 10,000 thermocyclings. Data were analyzed using two-way ANOVA and paired samples t-test (P < 0.05). Results: There was a statistically significant difference between the mean of microhardness values in two curing methods (P < 0.001) and in two storage conditions (P < 0.001). The mean of dual-cure microhardness (100.99 ± 7.22) was higher than that of self-cure (64.61 ± 12.51) and the mean value associated with pre-thermocycling (89.75 ± 15.84) was higher than that of the post-thermocycling (76.44 ± 23.56). There was no statistically significant difference between the mean flexural strength in the two curing methods (self-cure [72.85 ± 16.26], dual cure [79.87 ± 23.07]; [P > 0.05]). However, the mean flexural strength without thermocycling (85.98 ± 21.74) was higher than that of the thermocycled group (64.24 ± 6.40) (P < 0.001). Conclusion: The microhardness of Cention N in dual-cure mode was higher than that of self-cure mode, but the flexural strength of dual-cure was not significantly different from that of self-cure. Thermocycling had a significant effect on the microhardness and flexural strength. [ABSTRACT FROM AUTHOR]

Background: This in vitro study was conducted to compare the effect of universal bonding application strategy (i.e., self-etch and etch-and-rinse) on marginal adaptation of bulk-fill and conventional composite resins in Class II restorations. Materials and Methods: In this in vitro study sixty sound premolars extracted for orthodontic reasons were selected. The samples were allocated to four groups based on the universal bonding application strategy (self-etch and etch and rinse) and type of composite (bulk-fill and conventional). In each group, boxes were prepared with a depth of 4 mm on the mesial surfaces. Finally, the marginal adaptation of the samples was evaluated under a stereomicroscope. Two-way ANOVA was used to compare the marginal adaptation data in the study. Statistical significance was set at P < 0.05. Results: Considering the type of universal bonding application strategy, there was a statistically significant difference in marginal adaptation. Etch-and-rinse strategy showed better marginal adaptation compared to self-etch strategy (P < 0.001). However, there was no statistically significant difference in marginal adaptation between the two composite resins (P = 0.829). Furthermore, the interaction between the two factors (type of universal bonding application strategy and type of composite resin) was not statistically significant (P = 0.629). Conclusion: Etch-and-rinse bonding application strategy in both the bulk-fill and conventional composite resins exhibited better marginal adaptation compared to self-etch bonding application strategy. However, the difference of marginal adaptation between the two types of composite resins (bulk and conventional) was not significant. [ABSTRACT FROM AUTHOR]

Background. The use of bleaching agents might result in microstructural changes in tooth structure and in restorative materials. This study compared the effects of bleaching with %15 carbamide peroxide and %35 hydrogen peroxide on the flexural strength of Cention N restorative material using the self-cured and dual-cured polymerization modes. Methods. Sixty bar-shaped samples of Cention N restorative material were included in this in vitro study and assigned to three groups (n=20) randomly: control, bleaching with %15 carbamide peroxide and bleaching with %35 hydrogen peroxide. Each group was divided into two subgroups: samples polymerized in the self-cured mode and samples polymerized in the dual-cured mode. Then the flexural strengths of the samples were determined. Two-way ANOVA was used to compare flexural strengths between the three groups in two polymerization modes, followed by post hoc Tukey test. Statistical significance was defined at P<0.05. Results. The difference in the mean flexural strength was significant in terms of the bleaching regimen (P<0.001), with significantly lower flexural strength in the two bleaching groups compared to the control group. However, the mean flexural strengths were not significantly different in terms of the polymerization mode applied (P=0.14). Conclusion. The application of %15 carbamide peroxide and %35 hydrogen peroxide bleaching agents decreased the flexural strength of Cention N restorative material. Irrespective of the bleaching regimen, there was no significant difference in the flexural strength of Cention N between the self-curing and dual-curing polymerization modes. [ABSTRACT FROM AUTHOR]

This study explores the synthesis and characterization of two novel antibacterial dendritic methacrylate-based dental monomers. For this purpose, two dendritic esters have been synthesized via condensation reaction and then reacted with methacryloyl chloride to afford methacrylate-end caped dendritic esters. These compounds are subsequently converted to quaternary ammonium fluoride monomers (QAFMs) with decyl substituted side chain to produce two novel antibacterial dendreticdental monomers. The chemical structures of synthesized samples have been characterized using Fourier transform infrared (FTIR) and proton nuclear magnetic resonance (¹H NMR) spectroscopies. The obtained monomers can be used to replace 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropyl)-phenyl]propane (Bis-GMA) as the base monomer of universal resin-based dental composites in the presence of a diluting monomer (e.g.,triethyleneglycoldimethacrylate; TEGDMA), mainly due to their superior characteristics such as multifunctionalities as well as antibacterial activities. [ABSTRACT FROM AUTHOR]

Purpose: To compare shear bond strengths of three different self-etching adhesive systems of different pH values to enamel bleached with carbamide peroxide, treated with casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), or treated with CPP-ACP subsequent to bleaching with carbamide peroxide. Materials and Methods: Thirty-six human third molars were cut into 4 sections and randomly assigned to 4 groups (n = 36): group I: no treatment; group II: bleaching; group III: CPP-ACP; group IV: bleaching and CPP-ACP. After surface treatments, the samples of each group were further divided into three subgroups (n = 12) based on the adhesive used. The adhesives Clearfil SE Bond (CSE), AdhesE (ADE), and Adper SE Plus (ADP) were applied, and resin composite cylinders with a diameter of 2 mm and a height of 4 mm were bonded to the enamel. Then the specimens were subjected to shear bond strength testing. Two-way ANOVA and a post-hoc Tukey's test were used for statistical analysis (α = 0.05). Results: There were significant differences between the adhesive systems (p < 0.001) and surface treatments (p < 0.001), but no significant interactions were observed between these variables (p = 0.78). The CSE adhesive system showed the highest bond strength, and the bleaching procedure reduced bond strengths (p = 0.001). Furthermore, there were no significant differences in shear bond strength values between the control and CPP groups. However, the differences between other groups were statistically significant (p < 0.05). Conclusion: Bleaching reduced shear bond strength to enamel, but CPP-ACP application did not affect the bond strength to intact and previously bleached enamel. The bond strength of adhesives with different pH values to enamel was material dependant. [ABSTRACT FROM AUTHOR]

Background. The aim of this study was to investigate the effect of preheating methacrylate- and silorane-based composite resins on their color stability up to 40 times at 55-60°C. Methods. Seventy-six methacrylate and silorane-based composite resin samples, with a diameter of 10 mm and a height of 2 mm, were divided into 4 groups (n=19). After the samples were prepared, their color parameters were determined using a reflective spectrophotometer. The composite resin samples were separately stored in a solution of tea for 40 consecutive days. Then the samples underwent a color determination procedure again using a spectrophotometer and color changes were recorded. Finally two-way ANOVA was used to study the effect of composite temperature on its staining (P<0.05). Independent- samples t-test was used to evaluate changes in conversion rates of preheated composite resin samples compared to non-heated samples at P=0.005 and P=0.029 for silorane-based and Z250 composite resin samples, respectively. Results. Both composite resin type (P=0.014) and preheating (P<0.001) had significant effects on ÄE. Conclusion. Repeated preheating of methacrylate- and silorane-based composite resin samples, up to 55-60°C for 40 rounds, resulted in more color changes compared with unheated composite resin samples. After storage in a solution of tea the color change rate in the composite resin samples of silorane-based was higher than the Z250 composite resin samples. [ABSTRACT FROM AUTHOR]

Background: Streptococcus mutans is one of the species in the biofilm adjacent to cariogenic lesions. Photo-activated disinfection (PAD) is a new method which reduces cariogenic bacterial without common side effects. The success of PAD depends on the sensitivity of the organism, type of dyes, a dose of dyes, and the depth of emitted laser. In this study, effect of PAD on S. mutans reduction using indocyanine green (ICG) compared with methylene blue was evaluated. Materials and Methods: The standard turbidity (0.5 McFarland) of S. mutans suspension was prepared. Bacterial suspensions were transferred to the wells. Then, samples were subsequently divided into 7 groups. 1: Negative control, 2: Only methylene blue without laser, 3: Only 640 nm laser, 4: PAD by methylene blue, 5: Indocyanine without laser, 6: Only 810 nm laser, and 7: PAD by ICG. Subsequently, the bacterial suspension from each well was cultured, colony counts were determined, and data were analyzed using one-way ANOVA and Tukey's tests (P < 0.05). Results: There was a significant decrease of S. mutans colony counts after PAD using by both methylene blue and ICG photosensitizers. The highest decreased amount belonged to the ICG (PAD group). Methylene blue group (without laser application) also had a significant decrease of S. mutans colony counts (less effective than both PAD groups). Other groups (laser applications alone and ICG dye without laser) showed no significant bacterial reduction. Conclusion: With the parameters of this study PAD by ICG seems to be more effective than PAD by methylene blue, in reducing S. mutans bacteria as etiological factors of dental caries. [ABSTRACT FROM AUTHOR]

Background. This study evaluated the effect of two prophylaxis techniques on the marginal gap of CI V resin-modified glass-ionomer restorations. Methods. Standard Cl V cavities were prepared on the buccal surfaces of 48 sound bovine mandibular incisors in this in vitro study. After restoration of the cavities with GC Fuji II LC resin-modified glass-ionomer, the samples were randomly assigned to 3 groups of 16. In group 1, the prophylactic procedures were carried out with rubber cup and pumice powder and in group 2 with air-powder polishing device (APD). In group 3 (control), the samples did not undergo any prophylactic procedures. Then the marginal gaps were measured. Two-way ANOVA was used to compare marginal gaps at the occlusal and gingival margins between the groups. Post hoc Tukey test was used for two-by-two comparisons. Statistical significance was set at P < 0.05. Results. There were significant differences in the means of marginal gaps in terms of prophylactic techniques (P < 0.001), with significantly larger marginal gaps in the APD group compared to the pumice and rubber cup group, which in turn exhibited significantly larger marginal gaps compared to the control group (P < 0.0005). In addition, the means of marginal gaps were significant in terms of the margin type (P < 0.001), with significantly larger gaps at gingival margins compared to the occlusal margins (P < 0.0005). Conclusion. The prophylactic techniques used in this study had a negative effect on the marginal gaps of Cl V resinmodified glass-ionomer restorations. [ABSTRACT FROM AUTHOR]