Search

One-stage synthesis technology for preparing carbon adsorbents with tailored porosity from agricultural waste is worthwhile due to their extensive application value. Thermal gravimetric analysis, low-temperature N2 adsorption, X-ray diffraction (XRD), small-angle X-ray scattering (SAXS), and Raman spectroscopy were used to record the structure transformations of carbon materials, namely pore development, proceeding in the course of the step-wise pyrolysis of renewable and low-cost raw materials such as walnut shells (WNSs), which was carried out within a temperature range of 240–950 °C in a CO2 flow. The minimum threshold carbonization temperature for preparing nanoporous carbon materials from WNSs, determined by the examination of the N2 adsorption data, was 500 °C. The maximum specific micropore volume and BET surface achieved in the process without holding a material at a specified temperature were only 0.19 cm3/g and 440 m2/g, respectively. The pyrolysis at 400–600 °C produced amorphous sp2 carbon. At a temperature as high as 750 °C, an increase in the X-ray reflection intensity indicated the ordering of graphite-like crystallites. At high burn-off degrees, the size of coherently scattering domains becomes smaller, and an increased background in X-ray patterns indicates the destruction of cellulose nanofibrils, the disordering of graphene stacks, and an increase in the amount of disordered carbon. At this stage, pores develop in the crystallites. They are tentatively assigned to crystallites with sizes of 15–20 nm and to micropores. According to the Raman spectra combined with the XRD and SAXS data, the structure of all the pyrolysis products is influenced by the complex structure of the walnut shell precursor, which comprises cellulose nanofibrils embedded in lignin. This structure was preserved in the initial stage of pyrolysis, and the graphitization of cellulose fibrils and lignin proceeds at different rates. Most of the pores accessible for gas molecules in the resulting carbon materials are associated with former cellulose fibrils. [ABSTRACT FROM AUTHOR]

Capture and storage of LNG vapors in the adsorbed state is envisioned as an effective way to improve the LNG terminal performance. A synthetic carbon xerogel was proposed as a promising adsorbent for methane vapors in the LNG terminal combined with an adsorbed natural gas (ANG) module. The textural properties of the adsorbent were investigated by X-ray diffraction, scanning electron microscopy, and low-temperature nitrogen adsorption. An approach based on the theories of volume filling of micropores, a monolayer capacity on the mesopore surface, and the capillary condensation in the mesopores was applied to the experimental data on methane adsorption to evaluate the adsorption capacity of the adsorbent over the sub- and supercritical P,T-ranges. It was found that the capillary condensation of methane in mesopores ensured an extraordinary adsorption capacity of the adsorbent, achieving 540 m3(NTP)·m−3 at the boiling point. The adsorption- and temperature-induced deformation of the adsorbent, and the thermal effects arising during adsorption were examined with a view of the performance of the LNG terminal combined with the adsorber for capturing and accumulating LNG vapors. The ANG tank loaded with the carbon xerogel ensured the maximum amount of gas supplied to the consumer at temperatures close to 140 K. A comparison of the adsorption performances of the carbon xerogel and a commercial activated carbon characterized by a wider pore size distribution made it possible to identify a difference in the optimal operational conditions of their application for the LNG–ANG technology. [ABSTRACT FROM AUTHOR]

Adsorption-based carbon dioxide capture, utilization, and storage technologies aim to mitigate the accumulation of anthropogenic greenhouse gases that cause climate change. It is assumed that porous carbons as adsorbents are able to demonstrate the effectiveness of these technologies over a wide range of temperatures and pressures. The present study aimed to investigate the temperature-induced changes in the dimensions of the microporous carbon adsorbent Sorbonorit 4, as well as the carbon dioxide adsorption, by using in situ dilatometry. The nonmonotonic changes in the dimensions of Sorbonorit 4 under vacuum were found with increasing temperature from 213 to 573 K. At T > 300 K, the thermal linear expansion coefficient of Sorbonorit 4 exceeded that of a graphite crystal, reaching 5 × 10−5 K at 573 K. The CO2 adsorption onto Sorbonorit 4 gave rise to its contraction at low temperatures and pressures or to its expansion at high temperatures over the entire pressure range. An inversion of the temperature dependence of the adsorption-induced deformation (AID) of Sorbonorit-4 was observed. The AID of Sorbonorit-4 and differential isosteric heat of CO2 adsorption plotted as a function of carbon dioxide uptake varied within the same intervals of adsorption values, reflecting the changes in the state of adsorbed molecules caused by contributions from adsorbate–adsorbent and adsorbate–adsorbate interactions. A simple model of nanoporous carbon adsorbents as randomly oriented nanocrystallites interconnected by a disordered carbon phase is proposed to represent the adsorption- and temperature-induced deformation of nanocrystallites with the macroscopic deformation of the adsorbent granules. [ABSTRACT FROM AUTHOR]

Adsorbed natural gas (ANG) storage systems are based on nanoporous adsorbents with a tailored porous structure. Activated carbons are among the most promising and widely used candidates for this application, which is explained by the availability and abundance of raw material resources. In the present work, several series of activated carbons prepared from various precursors (coconut shell, peat, polymers, silicon carbide, and mineral coal) by different routes of physical and thermochemical activation were considered in the context of the adsorbed natural gas storage applications. Based on the Dubinin theory of volume filling of micropores and BET method, the porous structure of these adsorbents was evaluated from standard adsorption isotherms. The XRD, SAXS, and SEM measurements revealed variations in the textural and morphological properties of the adsorbents and their dependence on the precursor and synthesis procedure. The pore sizes evaluated from the adsorption and SAXS data were compared. Experimental data on methane adsorption at the temperature of 303 K and pressures of 0.1, 3.5, and 10 MPa made it possible to identify the most effective adsorbents. It was shown that the adsorption properties of ACs prepared from peat and mineral coal are determined by surface chemistry inherited from the precursor and activating agent. In contrast, the adsorption performance of ACs from polymer and coconut shell depends solely on the pore volume and pore dimensions. The adsorption effectiveness of each AC varies with pressure as a function of textural properties. Thus, a selection of an optimal adsorbent should be adjusted for thermodynamical coditions of ANG system. [ABSTRACT FROM AUTHOR]

An activated carbon prepared from silicon carbide by thermochemical synthesis and designated as SiC-AC was studied as an adsorbent for xenon. The examination of textural properties of the SiC-AC adsorbent by nitrogen vapor adsorption measurements at 77 K, powder X-ray diffraction, and scanning electron microscopy revealed a relatively homogeneous microporous structure, a low content of heteroatoms, and an absence of evident transport macropores. The study of xenon adsorption and adsorption-induced deformation of the Si-AC adsorbent over the temperature range of 178 to 393 K and pressures up to 6 MPa disclosed the contraction of the material up to −0.01%, followed by its expansion up to 0.49%. The data on temperature-induced deformation of Si-AC measured within the 260 to 575 K range was approximated by a linear function with a thermal expansion factor of (3 ± 0.15) × 10−6 K−1. These findings of the SiC-AC non-inertness taken together with the non-ideality of an equilibrium xenon gaseous phase allowed us to make accurate calculations of the differential isosteric heats of adsorption, entropy, enthalpy, and heat capacity of the Xe/SiC-AC adsorption system from the experimental adsorption data over the temperature range from 178 to 393 K and pressures up to 6 MPa. The variations in the thermodynamic state functions of the Xe/SiC-AC adsorption system with temperature and amount of adsorbed Xe were attributed to the transitions in the state of the adsorbate in the micropores of SiC-AC from the bound state near the high-energy adsorption sites to the molecular associates. [ABSTRACT FROM AUTHOR]

The present work focused on the experimental study of the performance of a scaled system of adsorbed natural gas (ANG) storage and transportation based on carbon adsorbents. For this purpose, three different samples of activated carbons (AC) were prepared by varying the size of coconut shell char granules and steam activation conditions. The parameters of their porous structure, morphology, and chemical composition were determined from the nitrogen adsorption at 77 K, X-ray diffraction (XRD), small-angle X-ray scattering (SAXS), and scanning electron microscopy (SEM) measurements. The methane adsorption data measured within the temperature range from 178 to 360 K and at pressures up to 25 MPa enabled us to identify the most efficient adsorbent among the studied materials: AC-90S. The differential heats of methane adsorption on AC-90S were determined in order to simulate the gas charge/discharge processes in the ANG system using a mathematical model with consideration for thermal effects. The results of simulating the charge/discharge processes under two different conditions of heat exchange are consistent with the experimentally determined temperature distribution over a scaled ANG storage tank filled with the compacted AC-90S adsorbent and equipped with temperature sensors and heat-exchanger devices. The amounts of methane delivered from the ANG storage system employing AC-90S as an adsorbent differ from the model predictions by 4–6%. Both the experiments and mathematical modeling showed that the thermal regulation of the ANG storage tank ensured the higher rates of charge/discharge processes compared to the thermal insulation. [ABSTRACT FROM AUTHOR]

Two activated carbons (ACs) were prepared from peat using thermochemical K2SO4 activation at 1053–1133 K for 1 h, and steam activation at 1173 K for 30 (AC-4) and 45 (AC-6) min. The steam activation duration affected the microporous structure and chemical composition of ACs, which are crucial for their adsorption performance in the methane storage technique. AC-6 displays a higher micropore volume (0.60 cm3/g), specific BET surface (1334 m2/g), and a lower fraction of mesopores calculated from the benzene vapor adsorption/desorption isotherms at 293 K. Scanning electron microscopy (SEM), X-ray diffraction (XRD), and small-angle X-ray scattering (SAXS) investigations of ACs revealed their heterogeneous morphology and chemical composition determined by the precursor and activation conditions. A thermodynamic analysis of methane adsorption at pressures up to 25 MPa and temperatures from 178 to 360 K extended to impacts of the nonideality of a gaseous phase and non-inertness of an adsorbent made it possible to evaluate the heat effects and thermodynamic state functions in the methane-AC adsorption systems. At 270 K and methane adsorption value of ~8 mmol/g, the isosteric heat capacity of the methane-AC-4 system exceeded by ~45% that evaluated for the methane-AC-6 system. The higher micropore volume and structural heterogeneity of the more activated AC-6 compared to AC-4 determine its superior methane adsorption performance. [ABSTRACT FROM AUTHOR]