Search

This work reports a method of producing flexible cobalt nanowires (NWs) directly from the chemical conversion of bulk precursors at room temperature. Chemical reduction of Li6CoCl8 produces a nanocomposite of Co and LiCl, of which the salt is subsequently removed. The dilute concentration of Co in the precursor combined with the anisotropic crystal structure of the hcp phase leads to 1D growth in the absence of any templates or additives. The Co NWs are shown to have high saturation magnetization (130.6 emu g-1). Our understanding of the NW formation mechanism points to new directions of scalable nanostructure generation.

Lithium (Li) metal serving as an anode has the potential to double or triple stored energies in rechargeable Li batteries. However, they typically have short cycling lifetimes due to parasitic reactions between the Li metal and electrolyte. It is critically required to develop early fault-detection methods for different failure mechanisms and quick lifetime-prediction methods to ensure rapid development. Prior efforts to determine the dominant failure mechanisms have typically required destructive cell disassembly. In this study, non-destructive diagnostic method based on rest voltages and coulombic efficiency are used to easily distinguish the different failure mechanisms-from loss of Li inventory, electrolyte depletion, and increased cell impedance-which are deeply understood and well validated by experiments and modeling. Using this new diagnostic method, the maximum lifetime of a Li metal cell can be quickly predicted from tests of corresponding anode-free cells, which is important for the screenings of electrolytes, anode stabilization, optimization of operating conditions, and rational battery design.

While powder diffraction methods are routinely utilized to optimize structural models for compounds whose crystal structures are known, the determination of unknown structures is far more challenging. When the unknown structure is large, structure solution can become a virtually intractable problem using standard structure solution methodologies, especially when the space group cannot be unambiguously resolved. One such system is the promising Na-ion battery cathode material Na3V2(PO4)2F3, whose high-temperature and room-temperature structures were previously solved, but whose more complex low-temperature structure could not be determined. Here, a novel materials genomic approach is demonstrated for the solution of the unknown 100 K structure of Na3V2(PO4)2F3 in which enumeration methods are first used to generate a large number (∼3000) of trial structures based on plausible orderings of Na ions and then automated Rietveld refinements are carried out to optimize each of these trial structures. Based on both the analysis of the ensemble of optimized trial structures and the density functional theory energy minimization of selected trial structures, the 100 K structure of Na3V2(PO4)2F3 is best described as belonging to the space group A21am with unit cell dimensions of a = 9.01928(4), b = 27.1379(1), and c = 10.73307(5). The 100 K unit cell has a large volume of 2627.07(2) Å3 with Z = 12 and 33 independent crystallographic sites (9 Na, 3 V, 3 P, 12 O, and 6 F) that is 3× and 6× larger than the room- and high-temperature polymorphs of this phase, respectively. The novel methods described here will be generally applicable for the solution of the complex cation-ordered structures that commonly occur for battery materials.

Although the determination of site occupancies is often a major goal in Rietveld refinement studies, the accurate refinement of site occupancies is exceptionally challenging due to many correlations and systematic errors that have a hidden impact on the final refined occupancy parameters. Through the comparison of results independently obtained from neutron and synchrotron powder diffraction, improved approaches capable of detecting occupancy defects with an exceptional sensitivity of 0.1% (absolute) in the class of layered NMC (Li[NixMnyCoz]O2) Li-ion battery cathode materials have been developed. A new method of visualizing the diffraction parameter space associated with crystallographic site scattering power through the use of f* diagrams is described, and this method is broadly applicable to ternary compounds. The f* diagrams allow the global minimum fit to be easily identified and also permit a robust determination of the number and types of occupancy defects within a structure. Through a comparison of neutron and X-ray diffraction results, a systematic error in the synchrotron results was identified using f* diagrams for a series of NMC compounds. Using neutron diffraction data as a reference, this error was shown to specifically result from problems associated with the neutral oxygen X-ray atomic form factor and could be eliminated by using the ionic O2- form factor for this anion while retaining the neutral form factors for cationic species. The f* diagram method offers a new opportunity to experimentally assess the quality of atomic form factors through powder diffraction studies on chemically related multi-component compounds.

MgMnB2O5, Mg2/3Mn4/3B2O5, and Mg4/3Mn2/3B2O5 pyroborates have been prepared via a ceramic method. When charging MgMnB2O5 vs Li, all of the Mg2+ can be removed, and with subsequent cycles, 1.4 Li ions, corresponding to a capacity of 250 mAhg-1, can be reversibly intercalated. This is achieved at a C/25 rate with 99.6% Coulombic efficiency. Significant capacity is retained at high rates with 97 mAhg-1 at a rate of 2C. Continuous cycling at moderate rates gradually improves performance leading to insertion of 1.8 Li, 314 mAhg-1 with a specific energy of 802 Whkg-1, after 1000 cycles at C/5. Ex situ X-ray and neutron diffraction demonstrate the retention of the pyroborate structure on cycling vs Li and a small volume change (1%) between the fully lithiated and delithiated structures. Mg2/3Mn4/3B2O5 and Mg4/3Mn2/3B2O5 are also shown to reversibly intercalate Li at 17.8 and 188.6 mAhg-1, respectively, with Mn ions likely blocking Mg/Li transport in the Mg2/3Mn4/3B2O5 material. The electrochemical ion-exchange of polyanion materials with labile Mg ions could prove to be a route to high energy density Li-ion cathodes.

Improved methods for the flux growth of single crystals of the important battery material LiFePO4 have been developed, allowing the facile preparation of single crystals up to 1 cm across with well-developed facets at relatively low temperatures. The structural characterization of these samples by both powder X-ray diffraction and single crystal diffraction (X-ray and neutron) indicates that the samples are typically stoichiometric with a very low concentration of Fe defects on the Li site, though crystals with larger concentrations of defects can be specifically grown using Fe-rich fluxes. These defects occur through the formation of a Fe-rich (Li1-2xFe x)FePO4 partial solid solution, in contrast to the antisite defects more commonly discussed in the literature which would preserve the ideal LiFePO4 stoichiometry. The LiFePO4 defects are shown to be sarcopside-like (2 Li+ → Fe2+ + vacancy) based on compositions refined from single crystal diffraction data, the observed dependence of unit cell parameters on defect concentration, and their observed phase behavior (defects only appear in growths from fluxes which are Fe-rich relative to stoichiometric LiFePO4). The distribution of defects has been studied by aberration corrected scanning transmission electron microscopy and was found to be highly inhomogenous, suggesting that defect-containing crystals may consist of endotaxial intergrowths of olivine LiFePO4 and sarcopside Fe3(PO4)2 in a manner that minimizes the detrimental influence of FeLi defects on the rate of Li-ion transport within crystallites. © 2013 American Chemical Society.

The detection of nitroaromatics and 2,3-dimethyl-2,3-dinitrobutane (DMNB) is possible by fluorescent sensors such as (salophen) zinc complex. The quenching of fluorescent ZnL involves binding to axial positions.