CuO nanowires were grown on Cu foils at 600 °C, coated with Cu and converted into Cu3N/Cu2O core–shell nanowires under NH3:H2 at 400 °C. The structural and optical properties are described in detail as well as its potential for energy applications.

Cu3N layers with a thickness of 40 nm were deposited by reactive sputtering using Ar: 10% N2 and 100% N2, after which they were annealed under NH3/H2 between 300 and 500 °C. These exhibited distinc...

Cu3N layers prepared by annealing, under NH3 O2 flow, of Cu sputtered on Si, fused SiO2, and soda lime glass were studied by Raman and N K edge Near Edge X ray Absorption Fine Structure NEXAFS spectroscopy. The annealing temperatures were ranging from 300 to 800 C. Benefiting from resonance effects on the Raman peak intensities when different excitation wavelengths are used, the contribution in the Raman signal of copper oxides, which provide peaks lying close to those of Cu3N, is more easily discriminated. The formation of Cu2O surface oxide is observed in almost all the samples even for annealing at low temperatures. CuO is generally formed at higher temperatures with the onset depending on the amount of O2 in the NH3 O2 mixture. However, high temperature is necessary to grow larger crystallites, as it is deduced from the decrease in the width of the high frequency Raman peak at ca. 650 cm amp; 8722;1 of Cu3N, in accordance with Scanning Electron Microscopy observations. The formation of CuO is accompanied by the creation of N2 trapped in the sample, which is directly detected by the NEXAFS measurements. N2 is most probably formed by the N atoms originating from the dissociation of the Cu N bonds