Hard Ti1-xAlxN thin films are of importance for metal-cutting applications. The hardness, thermal stability, and oxidation resistance of these coatings can be further enhanced by alloying with TaN. We use a hybrid high-power pulsed and dc magnetron co-sputtering (HIPIMS/DCMS) technique to grow dense and hard Ti0.41Al0.51Ta0.08N alloys without external heating (Ts<150 °C). Separate Ti and Al targets operating in the DCMS mode maintain a deposition rate of ~50 nm/min, while irradiation of the growing film by heavy Ta+/Ta2+ ions from the HIPIMS-powered Ta target, using dc bias synchronized to the metal-ion-rich part of each HIPIMS pulse, provides effective near-surface atomic mixing resulting in densification. The substrate is maintained at floating potential between the short bias pulses to minimize Ar+ bombardment, which typically leads to high compressive stress. Transmission and scanning electron microscopy analyses reveal dramatic differences in the microstructure of the co-sputtered HIPIMS/DCMS films (Ta-HIPIMS) compared to films with the same composition grown at floating potential with all targets in the DCMS mode (Ta-DCMS). The Ta-DCMS alloy films are only ~70% dense due to both inter- and intra-columnar porosity. In contrast, the Ta-HIPIMS layers exhibit no inter-columnar porosity and are essentially fully dense. The mechanical properties of Ta-HIPIMS films are significantly improved with hardness and elastic modulus values of 28.0 and 328 GPa compared to 15.3 and 289GPa for reference Ta-DCMS films. [ABSTRACT FROM AUTHOR]

Copyright of Materialwissenschaft und Werkstoffechnik is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)