Search

In previous papers, several hipoeutectoide carbon steels in quenched condition showed values of Young's modulus inferior to values corresponding to tempered condition. In all cases, Young's modulus was measured by ultrasound techniques. In fact, modulus of C22E steel (EN 10083) increases from 209 GPa (quenched condition) up to 211 GPa (tempered to 650 °C); for C45E steel, modulus increases from 199 GPa to 211 GPa (tempered to 500 °C), and for C55E steel Young's modulus varies from 202 GPa to 209 GPa for tempered steel to 650 °C. The present work focuses on the microstructural characterization of these steels at different heat conditions using reflection optical microscopy and also scanning electronic microscopy and the authors propose an explanation of the modulus variation using the behaviour of the dislocations array and their interaction with solute atoms and other dislocations present in steel.En trabajos anteriores se ha constatado que varios aceros al carbono hipoeutectoides, en estado de temple, presentan valores del módulo de Young inferiores a los correspondientes en estado de revenido. En todos los casos la determinación se ha realizado mediante ultrasonidos. En concreto, para el acero C22E (EN 10083), el módulo se incrementa ligeramente desde 209 GPa (material templado) hasta 211 GPa (revenido a 650 °C), para el acero C45E el módulo aumenta desde 199 GPa hasta 211 GPa (revenido a 500 °C) y para el acero C55E el módulo varía desde 202 GPa hasta 209 GPa para el acero revenido a 650 °C. El presente trabajo se centra en la caracterización estructural de los tres aceros mencionados a los distintos estados de tratamiento térmico, utilizando las técnicas de microscopía óptica de reflexión y microscopía electrónica de barrido, y se propone una explicación de la variación del módulo a partir del comportamiento de las dislocaciones y su interacción con átomos de soluto y con otras dislocaciones.

El diseño de circuitos digitales forma parte de las competencias básicas de los nuevos Grados en Ingeniería Informática e Ingeniería de Telecomunicaciones. Un obstáculo importante para el aprendizaje de dichas competencias es que las herramientas académicas existentes para el diseño de circuitos no permiten validar si un diseño se ajusta a la especificación de partida. En este artículo, se describe un entorno de autoaprendizaje para que los estudiantes puedan realizar ejercicios de diseño de circuitos y recibir un feedback continuo.

After a decade of intensive investigation, peer-to-peer computing has established itself as an accepted research field in the general area of distributed systems. peer-to-peer computing can be seen as the democratization of computing-overthrowing the old regime of hierarchies as in client-server systems-largely brought about by last-mile network improvements which have made individual PCs first-class citizens in the computer world. Initially, much of the focus in peer-to-peer systems was on best-effort file sharing. However, over the last few years, research has also been directed at trying to make peer-to-peer systems satisfy properties and have functionality as exhibited by more traditional forms of distributed systems. Examples of such properties and functionality, which in principle run counter to the disorganized nature of peer-to-peer systems, are certain levels of security and providing reliable distributed storage such as required by databases.

In previous papers, several hipoeutectoide carbon steels in quenched condition showed values of Young's modulus inferior to values corresponding to tempered condition. In all cases, Young's modulus was measured by ultrasound techniques. In fact, modulus of C22E steel (EN 10083) increases from 209 GPa (quenched condition) up to 211 GPa (tempered to 650 °C); for C45E steel, modulus increases from 199 GPa to 211 GPa (tempered to 500 °C), and for C55E steel Young's modulus varies from 202 GPa to 209 GPa for tempered steel to 650 °C. The present work focuses on the microstructural characterization of these steels at different heat conditions using reflection optical microscopy and also scanning electronic microscopy and the authors propose an explanation of the modulus variation using the behaviour of the dislocations array and their interaction with solute atoms and other dislocations present in steel. En trabajos anteriores se ha constatado que varios aceros al carbono hipoeutectoides, en estado de temple, presentan valores del módulo de Young inferiores a los correspondientes en estado de revenido. En todos los casos la determinación se ha realizado mediante ultrasonidos. En concreto, para el acero C22E (EN 10083), el módulo se incrementa ligeramente desde 209 GPa (material templado) hasta 211 GPa (revenido a 650 °C), para el acero C45E el módulo aumenta desde 199 GPa hasta 211 GPa (revenido a 500 °C) y para el acero C55E el módulo varía desde 202 GPa hasta 209 GPa para el acero revenido a 650 °C. El presente trabajo se centra en la caracterización estructural de los tres aceros mencionados a los distintos estados de tratamiento térmico, utilizando las técnicas de microscopía óptica de reflexión y microscopía electrónica de barrido, y se propone una explicación de la variación del módulo a partir del comportamiento de las dislocaciones y su interacción con átomos de soluto y con otras dislocaciones.

The parameters hardness, yield strength, ultimate tensile strength, toughness and Young's modulus of carbon steel C45E, EN 10083 (AISI 1045) annealed, quenched and tempered at various temperatures have been determined. Young's modulus has also been measured from ultrasonic techniques and also from the tension test; elastic deformation has been determined by the electric gaugue method. A metallographic study by scanning electron microscopy has also been carried out to confirm the results of the thermal treatment. Hardness, yield strength and ultimate tensile strength increases as it is with the thermal treatment. In addition Young=s modulus increases from 199-200 GPa (quenched) state to 211-212 GPa (tempered 500 °C, 1 h.). The annealed steel presents a Young's modulus of 206-207 GPa. A good agreement between Young's modulus values obtained by ultrasonic measurements and by tension test has been observed. This behaviour has been correlated with the distribution of dislocations in the material under the various states. Se han determinado distintas propiedades mecánicas del acero C45E según norma EN10083 (AISI 1045) reconocido, templado y revenido a distintas temperaturas. Las propiedades mecánicas analizadas han sido: dureza, límite elástico convecional, resistencia a la tracción, resiliencia y módulo de Young. Esta última propiedad se determinó por ultrasonidos y a partir de curvas tensión-deformación midiendo ésta mediante extensometría eléctrica.En todos los casos se ha comprobado la bondad del tratamiento aplicado madiante observaciones metalográficas por microscopía eléctronica de barrido. Los valores de dureza, límite elástico convecional y resistencia a la tracción presentan las variaciones esperadas después de los distintos tratamientos térmicos aplicados. Sorprendentemente, el módulo de Young se incrementa desde valores de 199-200 GPa para el acero templado hasta 211-212 GPa para el acero templado y revenido a 500ºC durante una hora; el acero en estado de recocido presenta un valor de módulo de 206-207GPa. Se detectó una muy buena concordancia entre los valores de módulo obtenidos por ultrasonidos y los obtenidos a partir de las curvas tensión-deformación. Se ha correlacionado este comportamiento con la distribución de dislocaciones en el material bajo diferentes estados.

Change of longitudinal and transverse residual stresses was studied by X Ray diffraction method as the applied plastic deformation, measured as A %, was increased in a standard tension test. The starting material, hot rolling Armco iron, has values close to 0 MPa in longitudinal direction, but it reaches 600 MPa with only A = 1,5 %, this value remains constant until necking is produced. In transverse direction the starting values are -300 MPa, changes are small and residual stresses remain compressive until the end of tension test. In addition, studies of the changes of residual stresses with time and with misalignment between incident X Ray and drawing direction are presented. Se ha estudiado la variación de las tensiones residuales longitudinales y transversales, mediante difracción de Rayos X, a medida que se aumenta el porcentaje de deformación plástica, medida como alargamiento porcentual (A %), en un ensayo de tracción convencional. El material original, hierro Armco laminado en caliente, tiene valores de tensión residual cercanos a cero en la dirección longitudinal y alcanza valores de hasta 600 MPa a partir de A = 1,5 %, manteniéndose este valor constante hasta la aparición de la estricción. En la dirección transversal los valores iniciales son de -300 MPa, las variaciones son menores y la tensión residual permanece siempre compresiva. Se presenta además un estudio de la variación de la tensión residual con el tiempo y con el diferente grado de desalineamiento entre el rayo incidente y la dirección de estirado.

The changes in the elastic constants at 298 K of polycrystalline samples of pure aluminium (99.5 %) with different levels of cold-working have been determined. The deformation process has been carried out in a tension machine. The properties measured are: Young modulus, E, Poisson ratio, v, and yield strength, σ0,2. The Young modulus diminishes from 70 to 63 GPa for 0-2.5 % deformation (elongation) and then increases with the successive cold-working passes. The Poisson ratio shows a similar behavior whereas the yield strength increases with cold-work. Pure aluminium behavior is similar to that obtained for pure iron (Armco) and for F-1140 annealed steel. Se ha determinado, a 298 K, la variación de las constantes elásticas de muestras policristalinas de aluminio puro (99,5 %) deformado en frío por estirado. El proceso de deformación se ha llevado a cabo en una máquina de tracción. Se han medido las siguientes propiedades: módulo de Young, E, coeficiente de Poisson, ν, y límite elástico del 0,2 % (σ0,2). El valor del módulo de Young disminuye entre el 0 y 2,5 % de deformación (alargamiento porcentual) desde 70 GPa hasta 63 GPa y, después, se recupera alcanzando los valores del material original con el sucesivo trabajo en frío. Se ha observado un comportamiento similar para el coeficiente de Poisson, mientras que el límite elástico del 0,2 % se incrementa con el trabajo en frío, tal como cabía esperar. El comportamiento observado para el aluminio puro es similar al determinado previamente para el hierro puro (Armco) y para el acero F-1140 recocido.

Currently there is an increasing trend to implement functionalities that allow for the development of applications based on Cloud computing. In education there are high expectations for Learning Management Systems since they can be powerful tools to foster more effective collaboration within a virtual classroom. Tools can also be integrated with these systems that can provide assistance to students on any topic covered in class through the proliferation and popularity of publicly available Web APIs. However, generally most students and teachers still face technological barriers to access these resources and integrate them into their educational systems. This paper discusses an effort to overcome this problem by proposing a method of resource access through linked data, which is explicitly defined with semantic annotations related to the learning environment. Doing so, we are able to decorate the Cloud providers API's, thus providing easy integration into learning applications and important benefits for learning. The effectiveness of our approach has been measured and evaluated through usability methods and cognitive load theory principles.

Varón de 3 añios y 9 meses de edad, remitido por su Pediatra, por hallazgo casual de masa torácica tras práctica de radiografía de tórax, con motivo de una infección respiratoria intercurrente....