This review aims to provide a technical roadmap and progress update for backplane thin film transistors (TFTs) used in organic light emitting diodes flat panel displays and next-generation flexible displays. In the introduction, we provide a general overview as well as trends in research on backplane TFTs. The main section describes current technical level and future prospects for amorphous metal oxide, semiconducting carbon nanotube, 2D transition metal dichalcogenide, and organic TFTs. The summary and prospects are provided in the conclusion.

In this study, a high-photoresponsivity self-powered deep ultraviolet (DUV) photodetector based on an Ag2O/β-Ga2O3 heterojunction was fabricated by depositing a p-type Ag2O thin film onto an n-type β-Ga2O3 layer. The device characteristics after post-annealing at temperatures ranging from 0 to 400 °C were investigated. Our DUV devices exhibited typical rectification characteristics. At a post-annealing temperature of 300 °C, the as-fabricated device had a low leakage current of 4.24 × 10−11 A, ideality factor of 2.08, and a barrier height of 1.12 eV. Moreover, a high photo-responsivity of 12.87 mA/W was obtained at a 100 μW/cm2 light intensity at a 254 nm wavelength at zero bias voltage, the detectivity was 2.70 × 1011 Jones, and the rise and fall time were 29.76, 46.73 ms, respectively. Based on these results, the Ag2O/β-Ga2O3 heterojunction photodetector operates without an externally applied voltage and has high responsivity, which will help in the performance improvement of ultraviolet sensing systems.

In this work, a self-powered, solar-blind photodetector, based on InZnSnO (IZTO) as a Schottky contact, was deposited on the top of Si-doped β-Ga2O3 by the sputtering of two-faced targets with InSnO (ITO) as an ohmic contact. A detailed numerical simulation was performed by using the measured J–V characteristics of IZTO/β-Ga2O3 Schottky barrier diodes (SBDs) in the dark. Good agreement between the simulation and the measurement was achieved by studying the effect of the IZTO workfunction, β-Ga2O3 interfacial layer (IL) electron affinity, and the concentrations of interfacial traps. The IZTO/β-Ga2O3 (SBDs) was tested at a wavelength of 255 nm with the photo power density of 1 mW/cm2. A high photo-to-dark current ratio of 3.70×105 and a photoresponsivity of 0.64 mA/W were obtained at 0 V as self-powered operation. Finally, with increasing power density the photocurrent increased, and a 17.80 mA/W responsivity under 10 mW/cm2 was obtained.