Si3N4/TaC composite MAO coatings were fabricated by microarc oxidation (MAO) on a Ti–6Al–4V (TC4) alloy in a phosphate-based electrolyte containing Si3N4/TaC mixed particles. The influence of the amount of Si3N4/TaC particles on the microstructure, composition, tribological behavior, and corrosion properties of the MAO coatings has been investigated. Morphological research of the MAO coatings was carried out using scanning electron microscopy (SEM), with the surface porosity analyzed by ImageJ software. X-ray diffraction (XRD) was used for the detection of the phase characteristic of the MAO coatings, and an abrasive wear test and electrochemical measurements were conducted in the artificial seawater solution by the ball-on-disc friction tester and the electrochemical workstation, respectively. The results showed that Si3N4/TaC particles could be successfully incorporated into the composite coatings, and the addition of Si3N4/TaC particles greatly reduced the porosity of the coatings, thus improving both tribological and corrosion properties of the composite MAO coatings. The composite MAO coating with the addition of 1 g/L Si3N4 + 0.5 g/L TaC particles showed the best tribological property and the optimum corrosion properties. [ABSTRACT FROM AUTHOR]

AlCoCrFeNiZrx (x = 0, 0.1, 0.2, 0.3, and 0.5) high-entropy alloys (HEAs) were prepared by a non-consumable vacuum arc melting technology, and the microstructure and corrosion behavior were investigated by XRD, SEM, immersion tests, and electrochemical measurements. The results indicate that galvanic corrosion of the AlCoCrFeNiZrx alloys occurred in 0.5 M H2SO4 solution, and only 0.1 mol of the added Zr could greatly improve the corrosion resistance of the alloys. The corrosion properties of the AlCoCrFeNiZrx HEAs had similar change tendencies with the increase in the Zr content in the immersion tests, potentiodynamic polarization measurements, and electrochemical impedance analysis, that is, the corrosion resistance of the AlCoCrFeNiZrx alloys in a 0.5 M H2SO4 solution first increased and then decreased with the increase in the Zr content. The Zr0.1 alloys were found to have the best selective corrosion and general corrosion resistance with the smallest corrosion rate, whereas the Zr0.3 alloys presented the worst selective corrosion and general corrosion resistance with the highest corrosion rate from both the immersion tests and the potentiodynamic polarization measurements. [ABSTRACT FROM AUTHOR]