In this study, ultrasound treatment was used to exfoliate commercially available graphite flakes into reduced graphene oxide (rGO) dispersed in ethanol. After centrifugation, solid copper chloride trihydrate was added, resulting in a green liquor containing Cu(II), Cu(I), and rGO. These liquors exhibited good and rapid photocatalytic activity in the degradation of eosin and bromophenol blue dyes (elimination in a few seconds) under visible-light irradiation. UV–visible spectroscopy confirmed the presence of rGO and Cu species. The size and morphology of the rGO sheets were investigated by several methods (SAXS, wide-angle XRD, SEM, and TEM). Negative UV peaks indicated light emission, which was independently verified by fluorescence. Intense plasmon peaks, with absorbances greater than 10, were observed after adding copper chloride salt. These plasmons were eliminated by a high dilution before the described catalytic tests were performed. [ABSTRACT FROM AUTHOR]

Catalysts enriched in Zinc ferrite (ZFO) were synthesized using coprecipitation and hydrothermal methods. Mixtures of crystalline nanoparticles (ZFO and α-Fe2O3, several allotropic varieties of FeO) were characterized by various techniques such as X-ray diffraction (XRD), transmission electron microscopy (TEM, SEM), N2 sorption, UV-visible spectrophotometry (UV-Vis) and X-ray photoelectron spectroscopy (XPS). After detailed characterizations, the catalytic performance of the solids (1 g/L) in the degradation of amoxicillin (AMX) (10 mg/L) as an antibiotic pollutant in water was evaluated. In addition, we used air as the oxygen source and adjusted the pH to 5.0. Consequently, the catalysts obtained via the hydrothermal method HT-ZFO had a high activity (100% of AMX removal in less than 100 min when an LED (75 W) light was used) compared to a similar mixture of oxides with graphene HT-ZFO-GO (a longer time of 150 min) that was necessary for the complete degradation of AMX. Impregnation with an aqueous solution containing 80 mg of GO obtained using Hummer's method, reduced into RGO by an ultrasound treatment, enhances the initial reaction rate but is associated with a prolonged time for complete AMX removal (10 ppm in water) that we attribute to its spontaneous corrosion. [ABSTRACT FROM AUTHOR]