Search

These elements are innovative and of interest to many researchers for the reinforcement of wooden elements. For the reinforced beam elements, the effect of the reinforcement factor, FRP and steel elastic modulus or FRP and steel arrangement of the reinforcement on the performance of the flexural elements was determined, followed by reading the load-displacement diagram of the reinforced beam elements. The finite element model was then developed and verified with the experimental results, which was mainly related to the fact that the general theory took into account the typical tensile failure mode, which can be used to predict the flexural strength of reinforced timber beams. From the tests, it was determined that reinforced timber beam elements had relatively ductile flexural strengths up to brittle tension for unreinforced elements. As for the reinforcements of FRP, the highest increase in load-bearing capacity was for carbon mats at 52.47%, with a reinforcement grade of 0.43%, while the lowest was for glass mats at 16.62% with a reinforcement grade of 0.22%. Basalt bars achieved the highest stiffness, followed by glass mats. Taking into account all the reinforcements used, the highest stiffness was demonstrated by the tests of the effectiveness of the reinforcement using 3 mm thick steel plates. For this configuration with a reinforcement percentage of 10%, this increase in load capacity was 79.48% and stiffness was 31.08%. The difference between the experimental and numerical results was within 3.62–27.36%, respectively.

This article presents experimental results from the bending of technical-scale models of beams reinforced in the tension zone with CFRP (Carbon Fiber Reinforced Polymers) materials, with a focus on the benefits resulting from the increased ductility in the tension zone of these beams. In experimental tests, the mechanical properties of reinforced beams were compared with unreinforced beams in terms of the maximum load, deflection, images of damage, stiffness, and distribution of deformation. The results showed that the proposed reinforcement solution was advantageous due to its strength and stiffness, and the safety of the structure. Based on this analysis, it was concluded that the reinforcement of wood with CFRP materials has a positive effect on the behavior and safety of structures. Also, a method of analytical checking of strengthened beams with small cross-sections was presented in the article.

This paper presents a discussion of the problem of compressive strength in a direction perpendicular to the grains based on test results of the joints made by timber posts and sill plate. These tests accompanied a larger series of full-scale tests of timber frame walls. The test elements were made of solid softwood (spruce). The wood moisture was low, which corresponds to the real working conditions of these elements in the walls of a building (low humidity is typical for dry wood in the built-in wall of a real building). In the tests, the compression strength of timber perpendicular to the grain was exceeded in the sill plate in the area in contact with the posts. Shortly before reaching the state of failure, large displacements in the sill plate were measured on the contact surface with the post, and the grains in the sill plates were cut off at the edge of the post. The full-scale test results showed an overestimation of the load-bearing capacity in compression perpendicular to the grain when calculated on the basis of EN 1995-1-1+A1:2008 (Eurocode 5), and, therefore, the need to modify the current approach for determining it.

The article presents the testing designating the impact of structural non-uniformity on the effectiveness of reinforcing bent wooden beams reinforced with basalt fibre (BFRP—Basalt Fibre Reinforced Polymers) rods. The obtained results demonstrate a positive impact of the strengthening in improving the bearing capacity and rigidness of the wooden beams. The article presents the impact of selected physical and chemical properties of wooden elements on the achieved strengthening reliability, increase in bearing capacity and the estimation of the reduction of deflections and stresses of bent beams, made from various wood quality classes and reinforced using BFRP rods. The conducted testing featured an analysis of the ability of using lower quality class lumber to strengthen the beams with pre-stressed basalt fibre rods. This solution allows for reducing the cross-section or lower the class of used wood with simultaneous maintenance of comparable rigidity and bending strength of beams, as in the non-strengthened beams.