Search

In this paper we report the synthesis of a library of phospho-amino acid analogues, via a novel single-step allyl-phosphoester protection/Pd-mediated deprotection strategy. These phosphoserine and phosphotyrosine analogues were then applied as additives to create adhesive calcium phosphate cements, allowing us to probe the chemical origins of the increased surface binding strength. We demonstrate the importance of multiple calcium binding motifs in mediating adhesion, as well as highlighting the crucial role played by substrate hydrophobicity and orientation in controlling binding strength.

A new class of materials, bone adhesives, could revolutionise the treatment of highly fragmented fractures. We present the first biological safety investigation of a bio-inspired bone adhesive. The formulation was based upon a modified calcium phosphate cement that included the amino acid phosphoserine. This material has recently been described as substantially stronger than other bioresorbable calcium phosphate cements. Four adhesive groups with the active substance (phosphoserine) and two control groups without phosphoserine were selected for in vitro and in vivo biocompatibility testing. The test groups were subject for cell viability assay and subcutaneous implantation in rats that was followed by gene expression analysis and histology assessment after 6 and 12 weeks. All adhesive groups supported the same rate of cell proliferation compared to the alpha-TCP control and had viability between 45-64% when compared to cell control. There was no evidence of an increased immune response or ectopic bone formation in vivo. To conclude, this bio-inspired bone adhesive has been proven to be safe, in the present study, without any harmful effects on the surrounding soft tissue., De två första författarna delar förstaförfattarskapet.

Phosphoserine-modified cements (PMCs) are a family of wet-field tissue adhesives that bond strongly to bone and biomaterials. The present study evaluated variations in the adhesive strength using a scatter plot, failure mode, and a regression analysis of eleven factors. All single-factor, continuous-variable correlations were poor (R2 < 0.25). The linear regression model explained 31.6% of variation in adhesive strength (R2 = 0.316 p < 0.001), with bond thickness predicting an 8.5% reduction in strength per 100 μm increase. Interestingly, PMC adhesive strength was insensitive to surface roughness (Sa 1.27–2.17 μm) and the unevenness (skew) of the adhesive bond (p > 0.167, 0.171, ANOVA). Bone glued in conditions mimicking the operating theatre (e.g., the rapid fixation and minimal fixation force in fluids) produced comparable adhesive strength in laboratory conditions (2.44 vs. 1.96 MPa, p > 0.986). The failure mode correlated strongly with the adhesive strength; low strength PMCs (<1 MPa) failed cohesively, while high strength (>2 MPa) PMCs failed adhesively. Failure occurred at the interface between the amorphous surface layer and the PMC bulk. PMC bonding is sufficient for clinical application, allowing for a wide tolerance in performance conditions while maintaining a minimal bond strength of 1.5–2 MPa to cortical bone and metal surfaces.

There are clinical situations in fracture repair, e.g. osteochondral fragments, where current implant hardware is insufficient. The proposition of an adhesive enabling fixation and healing has been considered but no successful candidate has emerged thus far. The many preclinical and few clinical attempts include fibrin glue, mussel adhesive and even “Kryptonite” (US bone void filler). The most promising recent attempts are based on phosphorylating amino acids, part of a common cellular adhesion mechanism linking mussels, caddis fly larvae, and mammals. Rapid high bond strength development in the wetted fatty environment of fractured bone, that is sustained during biological healing, is challenging to prove both safety and efficacy. Additionally, there are no “predicate” preclinical animal and human models which led the authors to develop novel evaluations for an adhesive candidate “OsStictm” based on calcium salts and amino acids. Adhesive formulations were evaluated in both soft (6/12 weeks) and hard tissue (3,7,10,14 & 42 days) safety studies in murine models. The feasibility of a novel adhesiveness test, initially proven in murine cadaver femoral bone, is being assessed in-vivo (3,7,10,14 & 42 days) in bilateral implantations with a standard tissue glue as the control. In parallel an ex-vivo human bone model using freshly harvested human donor bone is under development to underwrite the eventual clinical application of such an adhesive. This is part of a risk mitigation project bridging between laboratory biomaterial characterisation and a commercial biomaterial development where safety and effectiveness have to meet today´s new medical device requirements.

peer-reviewed, Premixed calcium phosphate cements (CPC's) are becoming the material of choice for injectable cements as a result of their effective delivery to the target implantation site. For orthopaedic use, it is of vital importance that the attributes of these CPC's are not compromised by irradiation sterilization. Therefore, the aim of this study is to determine the influence of irradiation sterilization on a range of premixed CPC's, with an emphasis on improving product shelf life through the use of optimal packaging configurations and annealing steps. Electron spin resonance (ESR) confirmed the presence of free radicals in the inorganic phase of the CPC paste following irradiation. The inclusion of a 24-h annealing step was the only successful method in reducing the degree of free radical formation. Based on the results of injectability force testing, it was revealed that an annealing step greater than 24-h significantly altered the viscosity, however; at 24-h the key attributes of the CPC paste were minimally effected. Overall, it was established that vacuum packing the CPC paste, placing the contents into a foil pouch, gamma irradiating at the minimal dose required and using an annealing step of ≤ 24-h, has the potential to extend the shelf life of the cement.