Search

Polyetheretherketone (PEEK) is a promising polymer material for tribological applications. Friction and wear tests of PEEK samples versus steel with different melt flow indices (MFI) were studied. The results showed dependencies of the friction force on the sliding velocity, either decreasing or increasing depending on whether the normal load exceeds the yield strength of the polymer. The data can be well fitted with the assumption of the two-component friction law involving the Amontons component and an adhesional component. With a decrease in MFI, i.e., with an increase in viscosity of polymer, the adhesive component of friction increases with increasing viscosity while the abrasive wear decreases. At high loads, the plastic displacement increases with an increase in the viscosity and plasticity of the polymer. The wear does not show a clear correlation with the viscosity.

In the present study, powder of FeCoCrNiMo0.5Al1.3 HEA was manufactured by gas atomization process, and then used for laser powder bed fusion (L-PBF) and microplasma spraying (MPS) technologies. The processes of phase composition and microstructure transformation during above mentioned processes and subsequent heat treatment were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and differential thermal analysis (DTA) methods. It was found that gas atomization leads to a formation of dendrites of body centered cubic (BCC) supersaturated solid solution with insignificant Mo-rich segregations on the peripheries of the dendrites. Annealing leads to an increase of element segregations till to decomposition of the BCC solid solution and formation of σ-phase and B2 phase. Microstructure and phase composition of L-PBF sample are very similar to those of the powder. The MPS coating has a little fraction of face centered cubic (FCC) phase because of Al oxidation during spraying and formation of regions depleted in Al, in which FCC structure becomes more stable. Maximum hardness (950 HV) is achieved in the powder and L-PBF samples after annealing at 600 °C. Elastic modulus of the L-PBF sample, determined by nanoindentation, is 165 GPa, that is 12% lower than that of the cast alloy (186 GPa).

A series of unidirectional thermoplastic tapes (UD tapes) specimens based on carbon fibers and polyamide filled with fullerene soot in a concentration of up to 4 wt. % was made. A study of the tribological properties by the 3 Ball on Plate test and Ring on Plate test and was made. Shown that the introduction of fullerene soot up to 2 wt. % decreases scatter of CoF in both ranges of load and velocity. Also, this concentration decreases wear rate almost 2.5 times compare to unfilled specimen. Mechanism of friction and wear was suggested. The obtained tribological results are well consistent with mechanical properties, and agree with previously suggested theory of the effect of fullerene soot on adhesion between polymer and fibers.

The paper experimentally studies the effect of meta and para- substitution of the amino groups in the diamine used in the synthesis of multiblock copolymers. The way for synthesis of new multiblock copolymers with the possibility of replacing the diamine in the polymer structure was shown. Thermal and mechanical properties of synthesized copolymers had been characterized by means of differential scanning calorimetry, thermogravimetric analysis, dynamic mechanical thermal analysis and by nanoindentation and tensile test.

A series of unidirectional thermoplastic tapes (UD tapes) specimens based on carbon fibers and polyamide filled with fullerene soot in a concentration of up to 4 wt. % was made. From the obtained tapes by the method of hot pressing, composite materials (CM) specimens with 0/0 and 90/90 ply orientations were made. A study of the mechanical properties of the samples obtained by the 3-point bending test was made. Shown that the introduction of fullerene soot up to 2 wt. % can significantly increase the strength and modulus of elasticity of both longitudinal and transverse reinforcement directions. Further increase in the concentration of soot leads to a decrease in properties. A theory that describes the effect of fullerene soot on the properties of CM, including the increase and further decrease in properties, depending on the concentration of nanoparticles was proposed.