Commercial austenitic stainless steel SUS304H with small amount of vanadium addition was used in this study. Small punch (SP) creep and uniaxial tensile creep tests were conducted at 650, 700, and 750 °C to measure creep lives and the minimum displacement rates or the minimum creep strain rates. The measured parameters were compared between the two test methods, seeking empirical relationships among the parameters using Larson-Miller Parameter and Monkman-Grant relation. Magnitude of the applied stress (MPa) in the uniaxial tensile creep test was approximately equal to the applied load value (N) in the SP creep test at all test temperatures. It was shown that during the creep deformation of the SP creep specimen, crack initiation and accompanying crack growth occur simultaneously. Competing failure mechanisms of creep deformation and crack growth may affect the SP creep life and consequently determine the proportionality function, α, in the relation between the SP load and the tensile creep rupture stress in creep tests. [ABSTRACT FROM AUTHOR]

The high-temperature creep fracture behaviour and creep strength of SUS 304H containing a minor addition of V were investigated in this study. A series of small punch (SP) creep and uniaxial creep tests were performed at 700 °C. The load and punch displacement rates obtained from the SP creep tests were used to derive conversion equations to determine the equivalent stress and creep strain rates. A converting equation is suggested in this study so that Norton’s secondary power law creep constants obtained from the SP creep testing can be in agreement with those obtained from the uniaxial tensile creep tests. The creep strength of the modified SUS 304H steel containing V was shown to be superior to that without V based on the current results and other available results for type 304H steel. [ABSTRACT FROM PUBLISHER]