Two series of polycrystalline zinc oxide (ZnO) layers, from Zn or ZnO targets, were grown on silicon (1 1 1) substrates by pulsed laser deposition (PLD) at ambient oxygen pressure levels, stepwise increased from 1 to 35 Pa. For ablation of targets, a pulsed Nd:YAG laser was used. The structural and morphological properties of the layers were investigated by scanning electron microscopy (SEM), atomic force microscopy (AFM), and secondary ion mass spectrometry (SIMS). The SEM images of ZnO layers in SE mode show a uniform granular structure and modified surface morphology, depending on oxygen pressure. The mean grain size in height and lateral directions decreases with an increase of oxygen pressure from 1 to 5 Pa, while a subsequent rise of oxygen pressure from 5 to 35 Pa will cause an increase in the grain size. The AFM measurement revealed that the surface structures of zinc oxide layers grown from different targets were similar, and the layers formed at an ambient oxygen pressure of 5 Pa exhibited the smallest values of calculated roughness and granularity. SIMS depth profiling analyses confirmed that the ZnO composition was homogenous across the layer, up to the abrupt change of chemical composition at the interface between the ZnO layer and the Si substrate. [ABSTRACT FROM AUTHOR]

Minimizing the foreign body reaction to polyimide-based implanted devices plays a pivotal role in several biomedical applications. In this work, we propose materials exhibiting nonbiofouling properties and a Young's modulus reflecting that of soft human tissues. We describe the synthesis, characterization, and in vitro validation of poly(carboxybetaine) hydrogel coatings covalently attached to polyimide substrates via a photolabile 4-azidophenyl group, incorporated in poly(carboxybetaine) chains at two concentrations of 1.6 and 3.1 mol %. The presence of coatings was confirmed by attenuated total reflectance Fourier transform infrared spectroscopy. White light interferometry was used to evaluate the coating continuity and thickness (between 3 and 6 μm under dry conditions). Confocal laser scanning microscopy allowed us to quantify the thickness of the swollen hydrogel coatings that ranged between 13 and 32 μm. The different hydrogel formulations resulted in stiffness values ranging from 2 to 19 kPa and led to different fibroblast and macrophage responses in vitro. Both cell types showed a minimum adhesion on the softest hydrogel type. In addition, both the overall macrophage activation and cytotoxicity were observed to be negligible for all of the tested material formulations. These results are a promising starting point toward future advanced implantable systems. In particular, such technology paves the way for novel neural interfaces able to minimize the fibrotic reaction, once implanted in vivo, and to maximize their long-term stability and functionality.