Search

In this paper, macroporous high‐entropy spinel oxide (HESO) (Fe0.2Ni0.2Co0.2Mn0.2Zn0.2)3O4 monoliths were successfully fabricated via a sol–gel method followed by calcination. Appropriate polyacrylic acid and propylene oxide contents allow the formation of three‐dimensional co‐continuous xerogel monoliths, and the water/glycerol ratio controls the macropore size of monoliths. Subsequent calcination achieves the precipitation of HESO (Fe0.2Ni0.2Co0.2Mn0.2Zn0.2)3O4 with a singular phase and exceptional structural stability. The macroporous HESO (Fe0.2Ni0.2Co0.2Mn0.2Zn0.2)3O4 demonstrates remarkable performance in the oxygen evolution reaction (OER) with an overpotential of 333 mV at 100 mA cm−2 and a Tafel slope of 43.2 mV dec–1, surpassing that of RuO2 (391 mV) under identical conditions. Furthermore, the catalytic stability of the HESO catalyst remains superior even after 24 h of testing. This process offers a promising avenue for the development of macroporous high‐entropy oxide OER catalysts for overall water splitting. [ABSTRACT FROM AUTHOR]

The purpose of this study is to prepare monodisperse silica mesoporous microspheres with narrow pore size distribution to promote their application in the field of liquid chromatography. An improved emulsion method was used to prepare silica mesoporous microspheres, and the rotary evaporation temperature, emulsification speed, dosage of porogen DMF, and dosage of the catalyst NH3·H2O were optimized. Subsequently, these microspheres were respectively treated by alkali–heating, calcination, and sieving. The D50 (particle size at the cumulative particle size distribution percentage of 50%) of as–prepared silica mesoporous microspheres is 26.3 μm, and the D90/D10 (the ratio of particle size at a cumulative particle size distribution percentage of 90% to a cumulative particle size distribution percentage of 10%) is 1.94. The resultant silica mesoporous microspheres have distinctive pore structures, with a pore volume of more than 1.0 cm3/g, an average pore size of 11.35 nm, and a median pore size of 13.4 nm. The silica mesoporous microspheres with a large particle size, uniform particle size distribution, large average pore size and pore volume, and narrow mesopore size distribution can basically meet the requirements of preparative liquid chromatographic columns. [ABSTRACT FROM AUTHOR]

Silicon carbide (SiC) ceramics with high bending strength were prepared by hot pressing sintering (HPS) with yttrium aluminum garnet (Y3Al5O12, YAG) as sintering additive, and the effects of YAG content and sintering temperature on the sintering behavior, microstructure and mechanical properties of SiC ceramics were investigated in detail. The uniform distribution of YAG to form a liquid phase and the driving force provided by hot pressing sintering decrease the sintering temperature, improve the densification of SiC ceramics, and refine the crystal size. By means of suitable sintering conditions with the additional amount of YAG of 5 wt%, the sintering temperature of 1950 °C and a pressure of 30 MPa, the resultant SiC/YAG composite ceramics possesses high sintering and mechanical properties with the relative density of 98.53%, the bending strength of 675 MPa, the Vickers hardness of up to 17.92 GPa, and the elastic modulus of 386 GPa. The as-prepared SiC/YAG composite ceramics are promisingly used as the dry gas seal materials in the centrifugal compressors. [ABSTRACT FROM AUTHOR]