This research article focused on the blending of poly(lactic acid)/poly(methyl methacrylate) (PLA/PMMA) polymer materials to overcome PLA's inherent weaknesses, such as low glass transition temperature, brittleness, and lack of melt strength. Consolidated feasible characteristic investigations, such as mechanical, thermal, and aging behavior, were carried out for PLA/PMMA blended polymer materials. Initially, the miscibility of PLA/PMMA blend filaments was prepared at various blend ratios (91/9, 82/18, and 73/27) and samples were printed by fused deposition modeling (FDM). Differential scanning calorimetry (DSC) and Fourier infrared spectroscopy (FTIR) analysis have been utilized to evaluate the glass transition temperature (Tg) and intermolecular interaction, respectively, on blended polymer materials. Experimental tensile, compression, and flexural strength testing were performed on neat polymers and blended polymer composites. Compared to neat PLA materials, blended composites had 13.24% and 19.07% higher flexural and compression strengths. Besides, the interfacial interaction of neat and blended polymers has been done using dynamic mechanical analysis (DMA). Furthermore, Tg, storage modulus, and aging behavior of blended polymer materials have significantly improved over neat PLA materials. Altogether, the development of PMMA/PLA blends as sustainable biomaterials for dental applications aligns with environmental concerns and the need for biocompatible materials in dentistry. Highlights: Blending of PLA and PMMA helps mitigate the inherent constraints of PLA.Blended composites exhibited greater compressive and flexural strengths.Better glass transition temperature and intermolecular interaction.Excellent thermal stability and water aging imply viable dental biomaterials. [ABSTRACT FROM AUTHOR]

The aim of this study is to investigate the effect of isopropyl triisostearoyl titanate (KR-TTS) as a titanate coupling agent (TCA) on surface modification of TiO2 nanotube (TNT) material. From the physical and chemical studies that have been performed on the modified TiO2 nanotube, scanning electron microscope micrographs, energy-dispersive X-ray and viscosity indicated that there was significant reduction in particle aggregation of the modified TiO2 Nanotube. FTIR spectroscopy confirmed that the functional group of the TCA reacted with the hydroxyl groups present on the surface of TiO2 nanotube resulting in an altered surface property from being hydrophilic to hydrophobic. X-ray diffraction indicated that crystalline structure did not change upon the modification with the coupling agent. Isopropyl triisostearoyl titanate (KR-TTS) is found to be superior in performance and has a significant effect on the dispersion and resolving of agglomeration. This paper presents the effect of surface modification with the TCA of isopropyl triisostearoyl titanate (KR-TTS) type on the TiO2 nanotube material. [ABSTRACT FROM AUTHOR]