Search

Ordered carbonaceous growth typically requires high-energy methods such as arc discharge [1] or decomposition of hydrocarbon-based precursors using laser [2–4], plasma [3], or thermolytic techniques [4]. For the latter technique, temperature regimes on the order of 600–1000° C are most common, with a few recent reports citing lower temperatures using halogenated precursors [5–7], or through alkali-metal catalyzed transformation of bulk carbon allotropes [8,9]. Sailor etal. have reported the first growth of non-amorphous carbon deposits at room temperature [10]. However, their electrochemical synthesis did not produce nanostructural carbon; due to the absence of nanosized catalytic seeds, the diameters of their fibers were > 5μm, and contained copious amounts of Cl, H, N, and O impurities.

We report the deposition of aluminum oxide and aluminosilicate thin films onto carbon fiber substrates, at temperatures of 200° and 250°C, respectively. For aluminosilicate films, the Al/Si ratio of the resultant film varied concomitantly with the composition of the liquid precursor mixture. The growth rate for the oxide films was 15–17 A/min, comparable with other methods carried out at higher temperatures. Cross-section SEM images indicate that the deposited films are conformal, following the complex topography of the carbon fiber substrate. Preliminary gas-phase IR analysis suggests that the coatings decompose the nerve agent simulant dimethyl methylphosphonate at temperatures as low as 35°C, suggesting the utility of the reported methodology for the design/fabrication of actively protective fabrics and clothing.

We describe the growth of amorphous carbon nanofibers (CNFs) from iron-encapsulated dendrimer catalysts at ambient temperature and pressure conditions. Both fourth-generation poly (propyleneimine) (PPI) and poly(amidoamine) (PAMAM) dendrimers were suitable macromolecular hosts for the catalytic species. Average nanofiber diameters range from 10 - 15 nm, with lengths in excess of 20 microns.

Multiwall carbon nanotubes (MWNTs) were synthesized via the decomposition of CCl4 in supercritical CO2 at 175 degrees C and 27.6 MPa using an iron-encapsulated dendrimer as a growth catalyst. The average diameter of resultant nanotubes was 20-25 nm, obtained after a 24-h reaction time. Our conditions represent the first application for CX4 precursors, as well as the lowest-reported temperature regime for carbon nanotube growth, allowing the use of other temperature-sensitive catalytic substrates.

Though the diversity of applications involving supercritical fluids (SCFs) continue to mount in virtually every sector of the scientific workplace, this environmentally-friendly medium is only briefly mentioned in undergraduate curricula; most often without hands-on laboratory experience. A new experimental module featuring this technology was introduced into an undergraduate inorganic chemistry laboratory. Nanoparticles of copper and aluminum oxide were formed using a variety of novel procedures, with scanning electron microscopy (SEM–EDS) and transmission electron microscopy (TEM) utilized for characterization. While particles of aluminum oxide were found to average 100 nm with sufficient aggregation, the copper nanoparticles were much smaller in diameter, with less agglomeration. A discussion of overall student sentiment and pedagogical outcomes from this module is also provided.