Search

Magnetic microwires with amorphous structures can present a unique combination of excellent magnetic softness and giant magnetoimpedance (GMI) effects together with reduced dimensions and good mechanical properties. Such unique properties make them suitable for various technological applications. The high GMI effect, observed in as-prepared Co-rich microwires, can be further optimized by postprocessing. However, unexpected magnetic hardening and a transformation of the linear hysteresis loop into a rectangular loop with a coercivity on the order of 90 A/m were observed in several Co-rich microwires upon conventional annealing. Several routes to improve magnetic softness and GMI effect in Fe- and Co-rich magnetic microwires are provided. We observed that stress annealing could remarkably improve the magnetic softness and GMI ratio of Co-rich microwires. Thus, almost unhysteretic loops with a coercivity of 2 A/m and a magnetic anisotropy field of about 70 A/m are achieved in Co-rich microwires stress annealed at appropriate conditions. The observed change in hysteresis loops and the GMI effect is explained by stress-annealing-induced anisotropy, which is affected by the stresses applied during annealing and by the annealing temperature. While as-prepared Fe-rich amorphous microwires present a low GMI effect, appropriate postprocessing (annealing and stress annealing) allows for a remarkable GMI ratio improvement (an order of magnitude). The evaluated dependence of the maximum GMI ratio on frequency allows the identification of the optimal frequency band for the studied samples. The origin of stress-annealing-induced anisotropy and related changes in hysteresis loops and the GMI effect are discussed in terms of the relaxation of internal stresses, “back-stresses”, as well as structural anisotropy.

As-prepared Fe-rich microwires with perfectly rectangular hysteresis loops present magnetization reversal through fast domain wall propagation, while the giant magnetoimpedance (GMI) effect in Fe-rich microwires is rather low. However, the lower cost of Fe-rich microwires makes them attractive for magnetic sensors applications. We studied the effect of conventional (furnace) annealing and Joule heating on magnetic-propertied domain wall (DW) dynamics and the GMI effect in two Fe microwires with different geometries. We observed that magnetic softness, GMI effect and domain wall (DW) dynamics can be substantially improved by appropriate annealing. Observed experimental results are discussed considering the counterbalance between the internal stresses relaxation and induced magnetic anisotropy associated with the presence of an Oersted magnetic field during Joule heating.

In this article, we study the effect of annealing temperature and applied stress on the magnetic properties of Fe71.80B13.27Si11.02Nb2.99Ni0.92 and Co65.34Si12.00B10.20Cr8.48Fe3.90Mo0.08 microwires. An anomalous behavior of the coercive field is observed while applying stress, indicating nontrivial changes in the microwire magnetic anisotropy. The effect of applied stimuli on the magnetic anisotropy and magnetostriction constant in both microwires is also discussed.

In this article we evaluate the possibility of using glass coated magnetic microwires as an alternative to optical fiber devices in structural health monitoring in the railway industry. The effect of applied stress on hysteresis loops of Fe71.80B13.27Si11.02Nb2.99Ni0.92 and Co65.34Si12.00B10.20Cr8.48Fe3.90Mo0.08 microwires has been studied and analyzed. An interpolation function has been obtained relating the coercitivity Hc with the applied stress.

In the current study, we have succeeded to fabricate Co2FeSi Heusler alloy glass-covered microwires with magnetic core nucleus diameter d = 4.36 mu m and total diameter D = 17.55 mu m, with high Curie temperature (T-e > 1100 K) and well-defined magnetic anisotropy for high temperature spintronic devices application. The magnetic properties of as-prepared and annealed at different temperature (873 K, 973 K and 1073 K for 1 h) of Co2FeSi Heusler alloy glass-covered microwires have been investigated. Strong dependence of the magnetic properties on the annealing conditions has been indicated. Anomalous magnetic behavior for annealed samples at 873 K and 973 K has been found and structural properties of such samples have been analyzed. Critical temperatures 155 K and 250 K have been detected for annealed samples at 873 K and 973 K, respectively, where the behavior of M-H loops and coercivity changed. Below the critical point the M -H curve shows "kink or wasp-waisted" magnetic behavior and complex magnetic reversal mechanism is supposed. The anomalous magnetic behavior is due to the martensitic phases induced by annealing con-ditions below the room temperature. This unusual magnetization behavior provides opportunities to un-derstand the phenomena of different types of magnetic domain structures in the preferred crystallographically oriented Co2FeSi Heusler alloy glass-coated micro-wires, essentially helpful for de-signing the devices based on magnetization switching.