Search

Although transition metal sulfides have prodigious potential for use as electrode materials because of their low electronegativities, their large volume changes inhibit broad application. Moreover, there is only limited knowledge of the ageing processes of these materials at the nanoscale. Herein, nano-C/FeS2 materials were prepared via one-pot syntheses from green biodegradable carbon precursors, followed by activation and sulfidation. The increased activation/sulfidation time led to an increase in the size of the nanoparticles (7 to 17 nm) and their aggregation, as well as in an increase in the specific surface area. The materials were then used as electrodes in 2-electrode symmetric supercapacitors with 2 M KOH. The activation process resulted in improved capacitance (60 F g−1 at 0.1 A g−1) and rate capability (36%) depending on the composite porosity, conductivity, and size of the FeS2 particles. The ageing of the FeS2 nanoparticles was investigated under air, and a progressive transformation of the nano-FeS2 into hydrated iron hydroxy sulfate with a significant morphological modification was observed, resulting in drastic decreases in the capacitance (70%) and retention. In contrast, the ageing of nano-FeS2 during cycling led to the formation of a supplementary iron oxyhydroxide phase, which contributed to the enhanced capacitance (57%) and long-term cycling (132% up to 10,000 cycles) of the device. [ABSTRACT FROM AUTHOR]

C‐rich graphitic carbonitride materials (CNx) with a large range of compositions have been prepared thanks to the self‐assembly, in different ratios, of melamine (M) and a panel of polycarboxylic acids (A) such as oxalic, tartaric and citric acid. The thermal conversion of the formed adducts (MAy), led to CNx phases, with x ranging from 0.66 to 1.4 (x=1.33 for g‐C3N4 for comparison). The properties of these materials were examined by different techniques (XRD, Raman spectroscopy, TEM, TGA, XPS and DRIFT). It appears that the increase in the C content is associated with the disappearance of the long‐range order of heptazine units and an increase in the sub‐nanometer carbon‐rich cluster size within the graphitic g‐C3N4 structure. This trend is followed by a significant increase in the interlayer spacing and a lower proportion of N=C−N bonds compared to C=C bonds. The thermal stability under an inert atmosphere of these phases and their UV‐Visible absorbance properties were also investigated. [ABSTRACT FROM AUTHOR]

The properties of the final product resulting from plasma polymerization strongly depend on the operating conditions and they impact the final application of the plasma polymer coating. Low‐pressure pulsed plasma polymerization of maleic anhydride was investigated at two different positions in relation to the glow discharge in a 1‐m‐long tubular reactor. Interestingly, competition was observed in the deposition of maleic anhydride plasma polymer in the form of a smooth thin film versus that in the form of nanoparticles. The possibility of a spatiotemporal control of plasma polymerization enabled the deposition of a plasma coating with tunable morphological properties depending on the sample position from the glow discharge and on the plasma pulse parameters (on‐time and off‐time). [ABSTRACT FROM AUTHOR]

The impact of surface chemistry on the morphogenesis of maleic anhydride plasma polymer is investigated on silicon wafers with very well‐controlled surface chemistries (i.e., native oxide, hydroxyl‐rich, and alkyl‐rich). A particular attention is paid to characterize the early stages of growth. Two different morphologies of polymer films are obtained, depending on the hydrophilic or hydrophobic nature of the substrate surface, even though the chemical composition is very similar. Homogeneous and dense polymer films are formed on hydrophilic substrates due to the strong affinity of plasma species toward the surface. Elongated nanostructures resulting in a less dense polymer film grow on the hydrophobic surface, which are assumed to be the result of the low affinity of plasma species. [ABSTRACT FROM AUTHOR]

Nanostructured silicon carbide (SiC) is an exceptional material with numerous applications, for example, in catalysis, biomedicine, high‐performance composites, and sensing. In this study, a fast and scalable method of producing nanostructured SiC from plant materials by magnesiothermic reduction via self‐propagating high‐temperature synthesis (SHS) route was developed. The produced biogenic material possessed a high surface area above 200 m2/g with a SiC crystallite size below 10 nm, which has not been done previously by SHS. This method enables affordable synthesis of the material plant‐based precursors in a reaction that only takes a few seconds, thereby paving a way for nanostructured SiC production in high volumes using renewable resources. The material was also functionalized with carboxylic acid and bisphosphonate moieties, and its use as metal adsorbent in applications such as wastewater remediation was demonstrated. [ABSTRACT FROM AUTHOR]

Potassium vanadium oxyfluoride phosphate of composition KVPO 4 F 0.5 O 0.5 was modified by a carbon coating to enhance its electrochemical performance. Two distinct methods were used, first, chemical vapor deposition (CVD) using acetylene gas as a carbon precursor and second, an aqueous route using an abundant, cheap, and green precursor (chitosan) followed by a pyrolysis step. The formation of a 5 to 7 nm-thick carbon coating was confirmed by transmission electron microscopy and it was found to be more homogeneous in the case of CVD using acetylene gas. Indeed, an increase of the specific surface area of one order of magnitude, low content of C sp 2 , and residual oxygen surface functionalities were observed when the coating was obtained using chitosan. Pristine and carbon-coated materials were compared as positive electrode materials in potassium half-cells cycled at a C/5 (C = 26.5 mA g -1 ) rate within a potential window of 3 to 5 V vs K + /K. The formation by CVD of a uniform carbon coating with the limited presence of surface functions was shown to improve the initial coulombic efficiency up to 87% for KVPFO 4 F 0.5 O 0.5 -C 2 H 2 and to mitigate electrolyte decomposition. Thus, performance at high C-rates such as 10 C was significantly improved, with ∼50% of the initial capacity maintained after 10 cycles, whereas a fast capacity loss is observed for the pristine material.

C-rich graphitic carbonitride materials (CN x ) with a large range of compositions have been prepared thanks to the self-assembly, in different ratios, of melamine (M) and a panel of polycarboxylic acids (A) such as oxalic, tartaric and citric acid. The thermal conversion of the formed adducts (MA y ), led to CN x phases, with x ranging from 0.66 to 1.4 (x=1.33 for g-C 3 N 4 for comparison). The properties of these materials were examined by different techniques (XRD, Raman spectroscopy, TEM, TGA, XPS and DRIFT). It appears that the increase in the C content is associated with the disappearance of the long-range order of heptazine units and an increase in the sub-nanometer carbon-rich cluster size within the graphitic g-C 3 N 4 structure. This trend is followed by a significant increase in the interlayer spacing and a lower proportion of N=C-N bonds compared to C=C bonds. The thermal stability under an inert atmosphere of these phases and their UV-Visible absorbance properties were also investigated., (© 2022 Wiley-VCH GmbH.)