Search

RESUMO Filmes finos de VOX (camada e multicamadas) foram fabricados por pulverização catódica com rádiofrequência assistida por campo magnético constante para aplicação em detectores de radiação infravermelha do tipo bolômetro. As amostras foram fabricadas sem quebra de vácuo a partir de três alvos: V2O3; VO2 e V2O5. Um sistema de pulverização catódica com três catodos foi construído para a realização deste trabalho. Os resultados mostraram que ambas as configurações, camadas e multicamadas, apresentaram TCR semelhantes, da ordem de 2 %/K, e resistência de folha inferior a 20 kΩ/quad, sendo ambas recomendadas para emprego em bolômetros. ABSTRACT VOX thin films (single and multilayers) were fabricated by RF magnetron sputtering for application in bolometers. The samples were deposited without vacuum break from three targets: V2O3; VO2 and V2O5. A RF magnetron sputtering system with three cathodes was built to carry out the depositions. The results showed that both configurations, single layers and multilayers, presented similar values of TCR, roughly 2%/K, and sheet resistance less than 20 kΩ/sq, being recommended for application in bolometers.

RESUMO Filmes finos de VOX (camada e multicamadas) foram fabricados por pulverização catódica com rádiofrequência assistida por campo magnético constante para aplicação em detectores de radiação infravermelha do tipo bolômetro. As amostras foram fabricadas sem quebra de vácuo a partir de três alvos: V2O3; VO2 e V2O5. Um sistema de pulverização catódica com três catodos foi construído para a realização deste trabalho. Os resultados mostraram que ambas as configurações, camadas e multicamadas, apresentaram TCR semelhantes, da ordem de 2 %/K, e resistência de folha inferior a 20 kΩ/quad, sendo ambas recomendadas para emprego em bolômetros.

RESUMO Este trabalho compara as propriedades de diversos óxidos transparentes condutores para serem utilizados como contatos frontais de células solares de filmes finos de CdTe. Os filmes foram depositados à temperatura ambiente, por pulverização catódica com rádio frequência, sem tratamento térmico posterior, com o objetivo de reduzir o número de etapas do processo de fabricação. A relação resistência/transmitância foi avaliada através de uma figura de mérito, de forma a propor os materiais candidatos a atuar como eletrodo frontal da célula solar. Os óxidos investigados foram divididos em dois grupos: os de baixa resistividade e os de alta resistividade. Eletrodos fabricados com os diversos óxidos foram submetidos a testes de estabilidade térmica nas temperaturas de processamento da célula solar. Os resultados mostraram que os filmes de ZnO e Zn2SnO4 são óxidos de alta resistividade (> 0,5 (.cm), enquanto que os de SnO2, In2O3, In2O3:Sn, Cd2SnO4 e ZnO:Al são de baixa resistividade (< 5,0 x 10-3 (.cm) e alta transmitância (> 85%). Os filmes de In2O3:Sn e ZnO:Al apresentaram-se como as melhores opções para fabricação dos eletrodos, pois possuem resistividades na faixa de 10-3-10-4 (.cm e transmitâncias entre 85-92%. No entanto, levando-se em consideração questões de custo e escassez associadas ao índio, filmes de ZnO:Al são os mais adequados para esta aplicação, pois além de possuírem valores de condutividade e transmitância elevados, apresentaram elevada estabilidade térmica nas temperaturas de processamento da célula. ABSTRACT This work compares the properties of different transparent conducting oxides for use as frontal contact in CdTe thin films solar cells. The films were deposited at room temperature by radio frequency sputtering without heat treatment, in order to reduce the manufacturing process steps. The resistance/transmittance relation was evaluated using a figure of merit, in order to propose the best material to act as front electrode of the solar cell. The oxides investigated in this work were separated into two groups: low-resistivity and high-resistivity oxides. Electrodes were prepared with these oxides and were subjected to thermal stability tests at the elevated temperatures involved in the solar cell processing. The results showed that ZnO and Zn2SnO4 films are high-resistivity oxides (> 0,5 (.cm), while SnO2, In2O3, In2O3:Sn, Cd2SnO4, and ZnO:Al are low-resistivity (< 5,0 x 10-3 (.cm) and high transmittance (> 85%) oxides. The In2O3:Sn and ZnO:Al films were the best options for the production of the electrodes, as their resistivity and transmittance values ranged from 10-3-10-4 (.cm and 85-92%, respectively. However, taking into consideration the cost and shortage issues, ZnO:Al films are the suitable choice for this application, because in addition to having high values of conductivity and transmittance, they have demonstrated thermal stability at elevated temperatures.

Submitted by Morgana Andrade (morgana.andrade@ufes.br) on 2016-04-11T20:49:17Z No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Dissertação_Jean.pdf: 1797995 bytes, checksum: b603b8c2f1c6e995111923a3d87928d5 (MD5) Approved for entry into archive by Patricia Barros (patricia.barros@ufes.br) on 2016-05-16T14:48:42Z (GMT) No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Dissertação_Jean.pdf: 1797995 bytes, checksum: b603b8c2f1c6e995111923a3d87928d5 (MD5) Made available in DSpace on 2016-05-16T14:48:42Z (GMT). No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Dissertação_Jean.pdf: 1797995 bytes, checksum: b603b8c2f1c6e995111923a3d87928d5 (MD5) Financiadora de Estudos e Projetos - FINEP, CNPq, CAPES, FAPES A meleira, causada pelo Papaya meleira virus (PMeV), é uma doença importante no Brasil e no México devido as grandes perdas econômicas que ela causa. Estudos para avaliar a interação patógeno-hospedeiro em nível histológico são fundamentais para compreender os mecanismos responsáveis pela resistência natural das plantas. Neste estudo foram coletadas folhas de mamoeiros saudáveis e sintomáticos para meleira e observou-se a topografia e a dureza da parede celular dessas plantas por microscopia de força atômica (AFM). As imagens em duas dimensões obtidas a partir de diferentes áreas da parede celular mostraram que as paredes celulares das plantas saudáveis são mais uniformes do que as paredes de plantas doentes. As plantas saudáveis também apresentaram características constitutivas da parede celular mais elevadas do que as de plantas doentes e a média da força de adesão máxima observada foi maior em plantas saudáveis do que em plantas doentes. Estes resultados indicam que o PMeV promove alterações nas paredes das células, tornando-as mais frágeis e suscetíveis à ruptura. Estas alterações, associadas ao aumento da captação de água e aumento da pressão interna dos laticíferos, provocam o rompimento celular que leva à exsudação espontânea do látex e facilita a disseminação de PMeV para outros laticíferos. Os resultados deste trabalho fornecem novas percepções sobre a interação mamoeiro-PMeV que podem revelar-se úteis no que se refere a entender e controlar a meleira do mamoeiro. Papaya sticky disease, caused by Papaya meleira virus (PMeV), is an important papaya disease in Brasil and Mexico due the severe economic losses it causes. Studies to assess the pathogen-host interaction at a histological are fundamental in order to understand the mechanisms that underlie natural resistance. In this study we collected leaves of healthy and symptomatic papaya sticky diseased plants and observed the topography and mechanical properties of plant cell walls by atomic force microscopy (AFM). Two-dimensional images obtained from different areas of the cell wall showed that the cell walls of healthy plants are smoother than the walls of sticky diseased plants. Also healthy plants displayed higher constitutive characteristics of the cell wall than diseased plants and the average maximum adhesion force was higher on healthy plants than on diseased plants. PMeV promotes changes on cell walls, making them more fragile and susceptible to breakage. These changes, associated with increased water uptake and internal pressure of laticifers causes cell disruption that leads to spontaneous exudation of latex and facilitates the spread of PMeV to other laticifers. The results of this work provide new insights on the interaction papaya-PMeV which could prove helpful when trying to understand and control the papaya sticky disease.