Search

While ball-milling is becoming one of the common tools used by synthetic chemists, an increasing number of studies highlight that it is possible to further expand the nature and number of products which can be synthesized, by heating the reaction media during mechanochemical reactions. Hence, developing set-ups enabling heating and milling to be combined is an important target, which has been looked into in both academic and industrial laboratories. Here, we report a new approach for heating up reaction media during ball-milling reactions, using induction heating (referred to as i-BM). Our set-up is attractive not only because it enables a very fast heating of the milling medium (reaching ≈80 °C in just 15 s), and that it is directly adaptable to commercially-available milling equipment, but also because it enables heating either the walls of the milling jars or the beads themselves, depending on the choice of the materials which compose them. Importantly, the possibility to heat a milling medium "from the inside" (when using for example a PMMA jar and stainless steel beads) is a unique feature compared to previously proposed systems. Through numerical simulations, we then show that it is possible to finely tune the properties of this heating system (e.g. heating rate and maximum temperature reached), by playing with the characteristics of the milling system and/or the induction heating conditions used. Lastly, examples of applications of i-BM are given, showing how it can be used to help elucidate reaction mechanisms in ball-milling, to synthesize new molecules, and to control the physical nature of milling media. [ABSTRACT FROM AUTHOR]

In recent years, there has been increasing interest in developing cost‐efficient, fast, and user‐friendly 17O enrichment protocols to help to understand the structure and reactivity of materials by using 17O NMR spectroscopy. Here, we show for the first time how ball milling (BM) can be used to selectively and efficiently enrich the surface of fumed silica, which is widely used at industrial scale. Short milling times (up to 15 min) allowed modulation of the enrichment level (up to ca. 5 %) without significantly changing the nature of the material. High‐precision 17O compositions were measured at different milling times by using large‐geometry secondary‐ion mass spectrometry (LG‐SIMS). High‐resolution 17O NMR analyses (including at 35.2 T) allowed clear identification of the signals from siloxane (Si−O−Si) and silanols (Si−OH), while DNP analyses, performed by using direct 17O polarization and indirect 17O{1H} CP excitation, agreed with selective labeling of the surface. Information on the distribution of Si−OH environments at the surface was obtained from 2D 1H−17O D‐HMQC correlations. Finally, the surface‐labeled silica was reacted with titania and using 17O DNP, their common interface was probed and Si−O−Ti bonds identified. [ABSTRACT FROM AUTHOR]

In recent years, there has been increasing interest in developing cost-efficient, fast, and user-friendly 17 O enrichment protocols to help to understand the structure and reactivity of materials by using 17 O NMR spectroscopy. Here, we show for the first time how ball milling (BM) can be used to selectively and efficiently enrich the surface of fumed silica, which is widely used at industrial scale. Short milling times (up to 15 min) allowed modulation of the enrichment level (up to ca. 5 %) without significantly changing the nature of the material. High-precision 17 O compositions were measured at different milling times by using large-geometry secondary-ion mass spectrometry (LG-SIMS). High-resolution 17 O NMR analyses (including at 35.2 T) allowed clear identification of the signals from siloxane (Si-O-Si) and silanols (Si-OH), while DNP analyses, performed by using direct 17 O polarization and indirect 17 O{ 1 H} CP excitation, agreed with selective labeling of the surface. Information on the distribution of Si-OH environments at the surface was obtained from 2D 1 H- 17 O D-HMQC correlations. Finally, the surface-labeled silica was reacted with titania and using 17 O DNP, their common interface was probed and Si-O-Ti bonds identified., (© 2021 The Authors. Chemistry - A European Journal published by Wiley-VCH GmbH.)