Incorporating graphene oxide (GO) with controlled localization into poly(butylene adipate‐co‐terephthalate) (PBAT) blends with poly(ethylene vinyl alcohol) (EVOH) aimed to improve barrier properties, biodegradability, and mechanical strength of PBAT. The PBAT/EVOH/GO nanocomposites containing 0 to 1 wt% of GO were prepared by a reactive mixing process in internal mixer. Microscopic images confirmed that the GO nanoplatelets are mainly localized in PBAT phase and then at the interface, contrary to the thermodynamic affinity of GO toward EVOH. The reactive nature of PBAT/EVOH/GO nanocomposites was confirmed via time‐sweep rheological studies where specific changes were observed in melt viscosity over time. The results of microscopic studies, rheometry, tensile test, and dynamic mechanical thermal analysis (DMTA) confirmed that localizing GO at the interface establishes strong interactions between PBAT and EVOH. By the addition of 0.75 wt% GO, tensile and yield strength were improved by 19% and 45%, respectively. Increasing GO significantly increased the hydrolysis degradation rate of the nanocomposites. Furthermore, the addition of GO considerably decreased the oxygen and water vapor permeability of the blends by up to 40% at 1 wt% GO. [ABSTRACT FROM AUTHOR]

Polymeric methylene diphenyl isocyanate (pMDI) was used as a reactive compatibilizer to improve the mechanical properties of the PBAT/EVOH blend. Initially, pMDI was blended with pure polymers. Adding pMDI led to a 10‐fold rise in the viscosity of PBAT/pMDI compared to pure PBAT, with an enhancement in tensile properties, attributed to pMDI's chain‐extending effect in the PBAT phase. Conversely, a reduction in the elongation at the break of EVOH/pMDI indicated a cross‐linking role for pMDI in the EVOH phase. Notably, the blend with 1 wt% of pMDI showed a high tensile strength of 38 MPa by route II, much above 13.5 MPa for the one prepared by route I, and 14 MPa for the blank PBAT/EVOH blend without pMDI. Fourier transform infrared (FTIR) spectra, FE‐SEM images, and dynamic mechanical thermal analysis (DMTA) results confirmed the occurrence of effective reactions in route II. Modification of the blend with pMDI decreased the crystallinity of EVOH, the size of EVOH droplets, and the oxygen transmission rate (OTR) of the blends. However, an increase in the pMDI content above 0.5 wt% decreased OTR. Therefore, the modified blends of PBAT/EVOH with pMDI can be used as an efficient compatibilizer or adhesive layer in PBAT/EVOH blends or multilayer films for agricultural or food packaging applications. [ABSTRACT FROM AUTHOR]