In this study, the effect of different weight percentages (wt. %) of halloysite nanotubes (HNTs) on the mechanical performance of glass laminate aluminum (Al) reinforced epoxy (GLARE) was investigated. GLARE (3/2) laminates with quasi-isotropic lay-up, [ Al /[(0°/90°)/(45°/−45°)]s/ Al /[(0°/90°)/(45°/−45°)]s/ Al ] filled with 0, 0.25, 0.5, 1, 2 and 3 wt. % of HNTs were fabricated using hand lay-up followed by compression molding. To explore the effect of HNTs on the mechanical properties, tensile, flexural, in-plane shear, interlaminar shear, bearing and impact tests were conducted. Results demonstrated that the inclusion of 1 wt. % of HNTs into GLARE leads to maximum improvements of 35.67, 8.50, 28.85, 50.47, 50.27, 30.43, 23.73, 72.08, 30.74, and 51.52% in tensile strength, tensile strain, Young's modulus, modulus of toughness, flexural strength, flexural strain, in-plane shear strength, interlaminar shear strength, bearing strength, and impact strength, respectively, compared to pristine GLARE. An enhancement of 38.89% in the flexural modulus was attained by adding 0.5 wt. % of HNTs to GLARE compared to pristine GLARE. The tensile strength, tensile strain, modulus of toughness, flexural strength, flexural modulus, flexural strain, in-plane shear strength, and interlaminar shear strength of GLARE filled with 3 wt. % of HNTs are 0.91, 0.88, 0.91, 0.91, 0.71, 0.83, 0.85, and 0.91 times those of the original GLARE. But Young's modulus, bearing strength, and impact strength are 1.10, 1.15 and 1.20 times those of the original GLARE. To investigate the fracture mechanism, field emission scanning electron microscope (FE-SEM) and energy-dispersive X-ray spectroscopy (EDX) were used. The microscopic images revealed that adding HNTs lead to the improvement in the interaction between the epoxy matrix and glass fiber, thereby improving the mechanical properties. [ABSTRACT FROM AUTHOR]

An experimental investigation on the mechanical performance of interlayer hybrid flax-basalt-glass woven fabrics reinforced epoxy composite laminates has been performed. The tensile, flexural, in-plane shear, interlaminar shear, bearing, and impact properties of the fabricated laminates were investigated. Test specimens were fabricated using vacuum bagging process. Failure modes of all specimens were recorded and discussed. Results proved that the mechanical properties of flax-basalt-glass hybrid laminates are highly dominated by the reinforcement combinations and plies stacking sequence. Hybridizing flax fiber reinforced composite with basalt and/or glass fabrics provides an effective method for enhancing its tensile, flexural, in-plane shear, interlaminar shear, and bearing properties as well as controls the impact strength of the composite. The fabricated hybrids are found to have good specific mechanical properties benefits. Amongst the studied flax/basalt/glass hybrids, FBGs has the highest tensile properties, GBFs has the highest flexural and impact properties, and GFBs has the best shear and bearing properties. Flax-basalt-glass hybrid composites with different layering sequence seem to be an appropriate choice for lightweight load bearing structures. [ABSTRACT FROM AUTHOR]