Search

Resin-modified glass ionomer cements may prevent dental cavities. These cements are used in dental fillings. Forty children with at least two cavities received resin-modified glass ionomer cement in one tooth and a traditional amalgam filling in the other. They were followed for up to three years. When the teeth were finally lost, examination revealed that those with a resin-modified glass ionomer cement had less enamel demineralization. This process is the precursor to cavity formation.

Purpose: To use shear bond strength (SBS) and shear fatigue strength (SFS) testing to determine the influence of phosphoric acid pre-etching times prior to application of self-etch adhesives on enamel bonding. Materials and Methods: Two single-step self-etch universal adhesives (Prime&Bond Elect and Scotchbond Universal), a conventional single-step self-etch adhesive (G-ӕnial Bond), and a conventional two-step self-etch adhesive (OptiBond XTR) were used. The SBS and SFS were obtained with phosphoric acid pre-etching for 3, 10, or 15 s prior to application of the adhesives, and without pre-etching (0 s) as a control. A staircase method was used to determine the SFS with 10 Hz frequency for 50,000 cycles or until failure occurred. The mean demineralization depth for each treated enamel surface was also measured using a profilometer. Results: For all the adhesives, the groups with pre-etching showed significantly higher SBS and SFS than groups without pre-etching. However, there was no significant difference in SBS and SFS among groups with > 3 s of preetching. In addition, although the groups with pre-etching showed significantly deeper demineralization depths than groups without pre-etching, there was no significant difference in depth among groups with > 3 s of pre-etching. Conclusion: Three seconds of phosphoric acid pre-etching prior to application of self-etch adhesive can enhance enamel bonding effectiveness. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the effectiveness of several acoustic measures in predicting breathiness ratings. Recordings were made of eight normal men and seven normal women producing normally phonated, moderately breathy, and very breathy sustained vowels. Twenty listeners rated the degree of breathiness using a direct magnitude estimation procedure. Acoustic measures were made of: (a) signal periodicity, (b) first harmonic amplitude, and (c) spectral tilt. Periodicity measures provided the most accurate predictions of perceived breathiness, accounting for approximately 80% of the variance in breathiness ratings. The relative amplitude of the first harmonic correlated moderately with breathiness ratings, and two measures of spectral tilt correlated weakly with perceived breathiness.

Objective: The purpose of this study was to use wear simulation to develop wear rates far two modern composite systems and then compare these rates with clinical studies on the same materials. Method and materials: A spring-loaded piston wear simulator was used to generate localized wear rates for P50 and Z100 at 100,000, 200,000, 300,000, and 400,000 cycles. Clinical studies on P50 and Z100 conducted at Creighton University and the Catholic University of Leuven were used for comparison of clinical wear to the laboratory values. Regression analysis was employed to define the wear rates. Results: The laboratory wear rates determined with simulation for P50 and Z100 were similar. Clinical occlusal contact area (OCA) wear for P50 and Z100 had small differences and were pooled to provide comparison with laboratory data. Wear rates determined from linear regression analysis provided equivalency factors between laboratory localized wear and clinical OCA wear that could be used for future studies. Further regression analysis comparing OCA and generalized clinical wear allowed a conversion factor of 4.5 to be determined. Conclusion: Localized wear from laboratory simulation may be a useful predictor of localized clinical wear and also clinical generalized wear using a conversion factor. (Quintessence Int 2004:35: 269-274) [ABSTRACT FROM AUTHOR]

The purpose of this study was to determine the enamel bond durability of three universal adhesives in different etching modes through fatigue testing. The three universal adhesives used were Scotchbond Universal, Prime&Bond Elect universal dental adhesive, and All-Bond Universal light-cured dental adhesive. A single-step self-etch adhesive, Clearfil S3 Bond Plus was used as a control. The shear bond strength (SBS) and shear fatigue strength (SFS) to human enamel were evaluated in total-etch mode and self-etch mode. A stainless steel metal ring with an internal diameter of 2.4 mm was used to bond the resin composite to the flat-ground (4000-grit) tooth surfaces for determination of both SBS and SFS. For each enamel surface treatment, 15 specimens were prepared for SBS and 30 specimens for SFS. The staircase method for fatigue testing was then used to determine the SFS of the resin composite bonded to the enamel using 10-Hz frequencies for 50,000 cycles or until failure occurred. Scanning electron microscopy was used to observe representative debonded specimen surfaces and the resin-enamel interfaces. A two-way analysis of variance and the Tukey post hoc test were used for analysis of the SBS data, whereas a modified t-test with Bonferroni correction was used for the SFS data. All adhesives in total-etch mode showed significantly higher SBS and SFS values than those in self-etch mode. Although All-Bond Universal in self-etch mode showed a significantly lower SBS value than the other adhesives, there was no significant difference in SFS values among the adhesives in this mode. All adhesives showed higher SFS:SBS ratios in total-etch mode than in self-etch mode. With regard to the adhesive systems used in this study, universal adhesives showed higher enamel bond strengths in total-etch mode. Although the influence of different etching modes on the enamel-bonding performance of universal adhesives was found to be dependent on the adhesive material, total-etch mode effectively increased the enamel bond strength and durability, as measured by fatigue testing. [ABSTRACT FROM AUTHOR]

Purpose: To examine the effect that a stainless steel (SS) matrix band has on the depth and distribution of cure of a resin-based composite (RBC) in a simulated Class II cavity. Methods: RBC was cured for 20 seconds in a simulated Class II cavity with and without a SS matrix band, and after 24 hours the specimens were scraped back and ground to expose a vertical central plane where Knoop micro-hardness (KHN) mapping was conducted from 0.05 - 1.5 mm from the band and in 0.5 mm intervals from the top of the specimens. The effect of different angles of the light guide on the distribution of hardness was also examined. Results: KHN values near the SS matrix band were significantly lower (P< 0.05) than within the bulk of the specimen and were lower than those found without the matrix band. Angles of incidence for the curing light-guide produced changes in the distribution of KHN within the specimens, but particularly near the matrix band, and with a 35° angle of incidence, the depth of cure was significantly different from that of normal incidence of the light. [ABSTRACT FROM AUTHOR]

This study examined the effect of different enamel and dentin conditioning times on the shear bond strength of a resin composite using etch-and-rinse and self-etch adhesive systems. Shear bond strengths were determined following treatment of flat ground human enamel and dentin surfaces (4000 grit) with 11 adhesive systems: 1) AdheSE One Viva Pen-(ASE), 2) Adper Prompt L-Pop-(PLP), 3) Adper Single Bond Plus-(SBP), 4) Clearfil SE Bond-(CSE), 5) Clearfil S³ Bond-(CS3), 6) OptiBond All-In-One-(OBA), 7) OptiBond Solo Plus-(OBS), 8) Peak SE-(PSE), 9) Xeno IV-(X4), 10) Xeno V-(X5) and 11) XP Bond-(XPB) using recommended treatment times and an extended treatment time of 60 seconds (n=10/group). Composite (Z100) to enamel and dentin bond strengths (24 hours) were determined using Ultradent fixtures and debonded with a crosshead speed of 1 mm/minute. The data were analyzed with a three-way Analysis of Variance (ANOVA) and Fisher's LSD post hoc test. The highest shear bond strengths (MPa) to enamel were achieved by the three etch-and-rinse systems at both the recommended treatment time (SBP-40.5 ± 6.1; XPB-38.7 ± 3.7; OBS- 35.2 ± 6.2) and the extended treatment time (SBP-44.5 ±8.1; XPB-40.9 ± 5.7; OBS-35.0 ± 4.5). Extending the enamel treatment time did not produce a significant change (p>0.05) in bond strength for the 11 adhesive systems tested. OBS generated the highest (46.2 ± 7.9) bond strengths to dentin at the recommended treatment time. At the extended treatment time X4 (42.2 ± 11.7), PSE (42.1 ± 9.7) and OBS (41.4 ± 8.0) produced the highest bond strengths to dentin. The bond strength change between recommend and extended treatment times was significant (p<0.05) for PSE, but the other 10 systems did not exhibit any significant change. [ABSTRACT FROM AUTHOR]

Abstract: Purpose: To examine the reduction in enamel demineralization provided by fluoride release from a conventional glass-ionomer, a resin-modified glass-ionomer and an experimental fluoride-releasing resin-based composite compared To a conventional resin-based composite control, and to correlate the level of fluoride release with demineralization. Materials and Methods: Enamel surfaces of extracted human incisors had a 0.4 mm thick layer of the specified test material carefully placed in a band across the mid-facial enamel to simulate a cement layer beneath an orthodontic bracket. The top surface of the test material was covered with nail varnish, leaving only the edges of the material exposed to release fluoride. The teeth were additionally covered with nail varnish to within 1 mm of the test material. Each group of teeth was placed into separate volumes of unstirred demineralizing solution at a pH of 4.7 for 4 days. The specimens were sectioned and examined by polarized light microscopy. Lesion areas were measured at distances from 100-300 µm away from the test material. Fluoride release for the test materials was measured for periods up to 5 months. Results: All of the fluoride-releasing materials demonstrated a statistically significant (P< 0.05) degree of protection of enamel from demineralization compared to the non-fluoride control material. The degree of protection was greatest near the material, but lesion areas increased with distance in an inverse relationship to the amount of fluoride release. Lesions were displaced from the region near the materials and the mean displacement was directly related to amount of fluoride release. The mean lesion areas for each distance decreased with the logarithm of the cumulative fluoride release. [ABSTRACT FROM AUTHOR]

Purpose: To determine if resin penetrated into the enamel etch pattern, in the absence of a polymerized outer surface film, could reduce the degree of demineralization of enamel subjected to a simulated caries challenge, and to evaluate whether the addition of fluoride to the resin would enhance reductions in demineralization. Materials and Methods: Enamel surfaces of extracted human incisors were acid-etched. One-half of the etched area was treated with an unfilled bonding resin, while the other one-half was left untreated as a control. In another group, this same procedure was followed except the unfilled bonding resin contained fluoride. The applied resin was aggressively air thinned to ensure oxygen inhibition throughout the external surface film thickness. The thinned film was visible light-cured and the area was wiped with an ethanol swab to remove the inhibited layer. The specimens were exposed to a buffer solution of pH = 4.7 for 4 days, and were sectioned and examined by polarized light microscopy and microradiography. Results: In each of the two test groups, the demineralization of the resin-treated side was significantly lower than the control side (P < 0.015). Under the conditions of this study, the experimental fluoride resin did not produce statistically significant reductions in demineralization compared with the non-fluoride resin. [ABSTRACT FROM AUTHOR]