Search

Short wave-length exchange-dominated propagating spin waves will enable magnonic devices to operate at higher frequencies and higher data transmission rates.1 While GMR based magnetic nano-contacts are highly efficient injectors of propagating spin waves2,3, the generated wave lengths are 2.6 times the nano-contact diameter4, and the electrical signal strength remains much too weak for practical applications. Here we demonstrate nano-contact based spin wave generation in magnetic tunnel junction stacks, and observe large discrete frequency steps consistent with the hitherto ignored possibility of second and third order propagating spin waves with wave lengths of 120 and 74 nm, i.e. much smaller than the 150 nm nano-contact. These higher-order propagating spin waves will not only enable magnonic devices to operate at much higher frequencies, but also greatly increase their transmission rates and spin wave propagating lengths, both proportional to the much higher group velocity.

This work provides a detailed investigation of the measured in-plane field-swept homodyne-detected ferromagnetic resonance (FMR) spectra of an extended Co/Cu/NiFe pseudo spin valve stack using a nanocontact (NC) geometry. The magnetodynamics are generated by a pulse-modulated microwave current and the resulting rectified dc mixing voltage, which appears across the NC at resonance, is detected using a lock-in amplifier. Most notably, we find that the measured spectra of the NiFe layer are composite in nature and highly asymmetric, consistent with the broadband excitation of multiple modes. Additionally, the data must be fit with two Lorentzian functions in order to extract a reasonable value for the Gilbert damping of the NiFe. Aided by micromagnetic simulations, we conclude that (i) for in-plane fields the rf Oersted field in the vicinity of the NC plays the dominant role in generating the observed spectra, (ii) in addition to the FMR mode, exchange dominated spin waves are also generated, and (iii) the NC diameter sets the mean wavevector of the exchange dominated spin wave, in good agreement with the dispersion relation., Comment: 7 pages, 7 figures

Spin transfer torque (STT) affords magnetic nanodevices the potential to act as memory, computing, and microwave elements operating at ultra-low currents and at a low energy cost. Spin transfer torque is not only effective in manipulating well-known magnetic structures, such as domain walls and vortices, but can also nucleate previously unattainable nano-magnetic objects, such as magnetic droplets and skyrmions. While the droplet and the skyrmion are both solitons, the former is inherently dynamic and non-topological, whereas the latter is static but topologically protected. Here we show that it is possible to combine these properties into a novel topologically protected dynamical skyrmion, which adds additional degrees of freedom, and functionality, to both droplet and skyrmion based applications. Unlike static skyrmions, the dynamical skyrmion can be nucleated and sustained without Dzyaloshinskii-Moriya interaction (DMI) or dipole-dipole interaction (DDI), and is a generic soliton solution independent of STT and damping once nucleated. In the presence of large DMI, the dynamical skyrmion experiences strong breathing with particular promise for skyrmion-based memory and microwave applications.

We report on the magnetization depth profile of a hybrid exchange spring system in which a Co/Pd multilayer with perpendicular anisotropy is coupled to a CoFeB thin film with in-plane anisotropy. The competition between these two orthogonal anisotropies promotes a strong depth dependence of the magnetization orientation. The angle of the magnetization vector is sensitive both to the strength of the individual anisotropies and to the local exchange constant, and is thus tunable by changing the thickness of the CoFeB layer and by substituting Ni for Pd in one layer of the Co/Pd stack. The resulting magnetic depth profiles are directly probed by element specific x-ray magnetic circular dichroism (XMCD) of the Co, Fe, and Ni layers located at different average depths. The experimental results are corroborated by micromagnetic simulations.

We have observed distinct temperature-dependent magnetization reversal modes in a perpendicular (Co/Pd)4/Co/Cu/(Co/Ni)4/Co pseudo-spin-valve, which are correlated with spin-transport properties. At 300 K, magnetization reversal occurs by vertically correlated domains. Below 200 K the hysteresis loop becomes bifurcated due to laterally correlated reversal of the individual stacks. The magnetic configuration change also leads to higher spin disorders and a significant increase in the giant magnetoresistance effect. First order reversal curve measurements reveal that the coupled state can be re-established through field cycling, and allow direct determination of the interlayer coupling strength as a function of temperature., Comment: 16 pages, 4 figures, 1 table

A ratchet effect (the rectification of an ac injected current) which is purely magnetic in origin has been observed in a superconducting-magnetic nanostructure hybrid. The hybrid consists of a superconducting Nb film in contact with an array of nanoscale magnetic triangles, circular rings or elliptical rings. The arrays were placed into well-defined remanent magnetic states by application of different magnetic field cycles. The stray fields from these remanent states provide a magnetic landscape which influences the motion of superconducting vortices. We examined both randomly varying landscapes from demagnetized samples, and ordered landscapes from samples at remanence after saturation in which the magnetic rings form parallel onion states containing two domain walls. The ratchet effect is absent if the rings are in the demagnetized state or if the vortices propagate parallel to the magnetic reflection symmetry axis (perpendicular to the magnetic domain walls) in the ordered onion state. On the other hand, when the vortices move perpendicular to the magnetic reflection symmetry axis in the ordered onion state (parallel to the domain walls) a clear ratchet effect is observed. This behavior differs qualitatively from that observed in samples containing arrays of triangular Ni nanostructures, which show a ratchet of structural origin., Comment: 16 pages, 6 figures and 1 table

We demonstrate pseudo spin valves with a (112)-textured DO_22 MnGa (MnGa) tilted magnetization fixed layer and an in-plane CoFe free layer. Single D0_22 MnGa films exhibit a small magnetoresistance (MR) typically observed in metals. In MnGa/Cu/ CoFe spin valves a transition from a negative (-0.08%) to positive (3.88%) MR is realized by introducing a thin spin polarizing CoFe insertion layer at the MnGa/Cu interface and tailoring the MnGa thickness. Finally, the exchange coupling between the MnGa and CoFe insertion layer is studied using a first-order reversal curve (FORC) technique., Comment: 5 pages, 4 figures, submitted to IEEE Magnetics Letters