Search

In this work, a Pt catalyst supported on an equimolar Al2O3–CeO2 binary oxide (Pt–Al–Ce) was prepared and applied in photo-thermo-chemical dry reforming of methane (DRM) driven by concentrated solar irradiation. It was found that the Pt–Al–Ce catalyst showed good stability in DRM reactions and significant enhancements in H2 and CO production rates compared with Pt/CeO2 (Pt–Ce) and Pt/Al2O3 (Pt–Al) catalysts. At a reaction temperature of 700 °C under 30-sun equivalent solar irradiation, the Pt–Al–Ce catalyst exhibits a stable DRM catalytic performance at a H2 production rate of 657 mmol g−1 h−1 and a CO production rate of 666 mmol g−1 h−1, with the H2/CO ratio almost equal to unity. These production rates and the H2/CO ratio were significantly higher than those obtained in the dark at the same temperature. The light irradiation was found to induce photocatalytic activities on Pt–Al–Ce and reduce the reaction activation energy. In situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS) was applied to identify the active intermediates in the photo-thermo-chemical DRM process, which were bidentate/monodentate carbonate, absorbed CO on Pt, and formate. The benefits of the binary Al2O3–CeO2 substrate could be ascribed to Al2O3 promoting methane dissociation while CeO2 stabilized and eliminated possible coke formation, leading to high catalytic DRM activity and stability. [ABSTRACT FROM AUTHOR]

Metal- and nitrogen-doped carbon (M-N-C) is a promising material to catalyze electrochemical CO 2 reduction reaction (CO 2 RR). However, most M-N-C catalysts in the literature require complicated synthesis procedures and produce small quantities per batch, limiting the commercialization potential. In this work, we developed a simple and scalable synthesis method to convert metal-impurity-containing commercial carbon nanotubes (CNTs) and nitrogen-containing organic precursors into M-N-C via one-step moderate-temperature (650 °C) pyrolysis without any other treatment nor the need to add metal precursors. Batches of catalysts in varied mass up to 10 g (150 mL in volume) per batch were synthesized, and repeatable catalytic performances were demonstrated. To the best of our knowledge, the 10 g batch is one of the largest batches of CO 2 RR catalysts synthesized in the literature while requiring minimal synthesis steps. The catalyst possessed single-atomic iron-nitrogen (Fe-N) sites, enabling a high performance of >95% CO product selectivity at a high current density of 400 mA/cm 2 and high stability for 45 h at 100 mA/cm 2 in a flow cell testing. The catalyst outperformed a benchmark noble-metal nanoparticle catalyst and achieved longer stability than many other reported M-N-C catalysts in the literature. The scalable and cost-effective synthesis developed in this work paves a pathway toward practical CO 2 RR applications. The direct utilization of metal impurities from raw CNTs for efficient catalyst synthesis with minimal treatment is a green and sustainable engineering approach., Competing Interests: The authors declare no competing financial interest., (© 2023 American Chemical Society.)

Atomically dispersed metal and nitrogen co-doped carbon (M-N/C) catalysts hold great promise for electrochemical CO 2 conversion. However, there is a lack of cost-effective synthesis approaches to meet the goal of economic mass production of single-atom M-N/C with desirable carbon support architecture for efficient CO 2 reduction. Herein, we report facile transformation of commercial carbon nanotube (CNT) into isolated Fe-N 4 sites anchored on carbon nanotube and graphene nanoribbon (GNR) networks (Fe-N/CNT@GNR). The oxidization-induced partial unzipping of CNT results in the generation of GNR nanolayers attached to the remaining fibrous CNT frameworks, which reticulates a hierarchically mesoporous complex and thus enables a high electrochemical active surface area and smooth mass transport. The Fe residues originating from CNT growth seeds serve as Fe sources to form isolated Fe-N 4 moieties located at the CNT and GNR basal plane and edges with high intrinsic capability of activating CO 2 and suppressing hydrogen evolution. The Fe-N/CNT@GNR delivers a stable CO Faradaic efficiency of 96% with a partial current density of 22.6 mA cm -2 at a low overpotential of 650 mV, making it one of the most active M-N/C catalysts reported. This work presents an effective strategy to fabricate advanced atomistic catalysts and highlights the key roles of support architecture in single-atom electrocatalysis.