Search

Ternary system piezoelectric ceramics 0.7PbZrxTi1−xO3-0.3Pb(Zn1/3Nb2/3)O3 (abbreviated as 0.7PZTx-0.3PZN) were prepared by a traditional solid-phase process. With the increase in Zr content, the electrical properties of the ceramics were significantly improved, and this result could be attributed to the change in the ceramic phase structure. The relationship between the change in Zr content and the ceramic phase structure and properties was investigated in detail by component modulation. X-ray diffraction (XRD) analyses showed that the phase structure of the ceramics undergoes a transition from the coexistence of tetragonal (T) and rhombohedral (R) phases to the predominance of rhombohedral (R) phases as the Zr content x increases. The phase structure of the ceramics at x = 0.49 is closer to the morphotropic phase boundary (MPB), with about 32% of the T-phase and 68% of the R-phase, and possesses good electrical properties: d33 = 483 pC/N, kp = 0.69, εr = 2171.7, tanδ = 0.016, Tc = 292.5°C, Pr = 35.9 μC/cm2, Ec = 7.7 kV/mm. Constructing the MPB of 0.7PZT-0.3PZN piezoelectric ceramics by varying the Zr content can be effective in improving the electrical properties and understanding more broadly how the change in Zr/Ti composition affects the piezoelectric behavior. [ABSTRACT FROM AUTHOR]

In the preparation of (Ba,Ca)(Zr,Ti)O3 lead-free piezoelectric ceramics, different Ca2+ and Zr4+ contents will greatly affect the phase structure, microstructure, and electrical properties of the ceramics. XRD shows that all samples have pure perovskite phase structure, and the (Ba0.85Ca0.15)(ZryTi1−y)O3 ceramics morphotropic phase boundary region from tetragonal phase to rhombohedral phase near 0.08 ≤ y ≤ 0.1. From the dielectric temperature curve, the phase transition temperature (TO-T) was found near room temperature at 0.12 ≤ x ≤ 0.18 for the (Ba1−xCax)(Zr0.1Ti0.9)O3 ceramics. Both Ca2+ and Zr4+ increase have a significant decrease on the Curie temperature Tc. All samples were revealed as relaxers with diffusivities in the range 1.29 ≤ γ ≤ 1.82. Different from the undoped ceramics, ceramics doped with Ca and Zr ions exhibit saturated P–E hysteresis loops, and their ferroelectric properties are significantly optimized. In particular, the (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 ceramic demonstrated optimal properties, namely d33 = 330 pC/N, kp = 0.41, εr = 4069, Pr = 4.8 μC/cm2, and Ec = 3.1 kV/cm, indicating that it is a viable lead-free piezoelectric contender. Variations in Ca and Zr content have a significant effect on the crystal grain sizes and densities of ceramics, which is strongly associated with their piezoelectricity. [ABSTRACT FROM AUTHOR]

0.55BaSrTiO-0.45MgO composite ceramics (BST-MgO, x = 0.5-0.65) co-modified with CuO and MnO were prepared by conventional soild state reaction method. The microstructure, phase and morphology were investigated. The results showed the formation of the perovskite BST phase and MgO phase. The dielectric constant ( ε) and tunability ( T) of the ceramic samples increased with increasing Ba content. The dielectric loss (tan δ) and figure of merit achieved their minimum and maximum at x = 0.6, respectively. The obtained ceramic sample with x = 0.6 exhibited favorable properties, which are listed as follows: ε = 190, tan δ = 0.22 %, T = 16 %, E = 5.6 kV/cm and FOM = 72.7. [ABSTRACT FROM AUTHOR]

Quaternary piezoelectric ceramics Pb(Ni1/3Nb2/3)O3–Pb(Fe1/2Nb1/2)O3–Pb(Zr0.3Ti0.7)O3–xZnO (PNN–PFN–PZT–xZ, x=0.0–0.08 in molar ratio) were prepared by the conventional mixed-oxide method. The effects of ZnO content on the microstructure and piezoelectric properties were systematically investigated. Increasing ZnO additive promotes the phase structure transformation from rhombohedral to tetragonal, indicating the presence of the morphotropic phase boundary in the ZnO-modified PNN–PFN–PZT system. The results show that ZnO doping significantly improves the coercive field (E c ), Curie temperature (T c ), and temperature stability (Δf r /f r 30°C, Δd 31/d 31 30 °C) of the PNN–PFN–PZT–xZ ceramics, although the piezoelectric constant (d 33, d 31) decreases slightly with increasing ZnO content. Taking into consideration the piezoelectric property and temperature stability, the obtained ceramic sample with x=0.04 exhibited favorable properties, which are listed as follows: d 33=810pC/N, k p =0.647, ε r =6243, tan δ=2.74%, E c =4.7kV/cm, and T c =136°C. [ABSTRACT FROM AUTHOR]

Abstract: 0.55Pb(Ni1/3Nb2/3)O3–0.45Pb(Zr0.3Ti0.7)O3(PNN–PZT) ceramics with different concentration of xFe2O3 doping (where x =0.0, 0.8, 1.2, 1.6mol%) were synthesized by the conventional solid state sintering technique. X-ray diffraction analysis reveals that all specimens are a pure perovskite phase without pyrochlore phase. The density and grain size of Fe-doped ceramics tend to increase slightly with increasing concentration of Fe2O3. Comparing with the undoped ceramics, the piezoelectric, ferroelectric and dielectric properties of the Fe-doped PNN–PZT specimens are significantly improved. Properties of the piezoelectric constant as high as d 33 ~956 pC/N, the electromechanical coupling factor k p ~0.74, and the dielectric constant ε r ~6095 are achieved for the specimen with 1.2mol% Fe2O3 doping sintered at 1200°C for 2h. [Copyright &y& Elsevier]

Abstract: Li/Ta/Sb co-doped lead-free (K0.4425Na0.52Li0.0375)(Nb0.93−x Ta x Sb0.07)O3 (abbreviated KNLNST x ) piezoelectric ceramics, with Ta-doping ratio of x ranging from 0.0275 to 0.0675, were synthesized using the conventional solid-state reaction method at the sintering temperature of 1130°C. The effects of Ta content on the microstructure, dielectric properties, and phase transition behavior of the prepared ceramics were systematically investigated. The X-ray diffraction results show that all KNLNST x ceramics formed a secondary phase, which is assigned to the tetragonal tungsten-bronze type (TTB) structure phase, and showed a phase transition from an orthorhombic symmetry to a tetragonal symmetry across a composition region of 0.0375

Abstract: Two-step sintering was applied to manufacture a typical Li- and Ta/Sb-modified alkaline niobate-based lead-free piezoelectric ceramics. The sintering condition dependences of dielectric constants and piezoelectric properties were investigated. Under the optimal condition, dense specimens have an average grain size of approximately 5μm, and show good dielectric and piezoelectric properties. Significantly, the (K0.4425Na0.52Li0.0375) (Nb0.8925Sb0.07Ta0.0375)O3 ceramics sintered under the condition “1130/10/1020/15” show the peak values of the piezoelectric coefficient (d 33), electromechanical coupling coefficient (k p), and dielectric constant (ɛ), which are 281pC/N, 50% and 1500, respectively, owing to the densest microstructure of typical bimodal grain size distributions. Furthermore, the KNLNST ceramics maintain relatively low dielectric loss over wide temperature ranges. The result indicates that the KNLNST ceramics sintered by two-step sintering exhibit good temperature stability. [Copyright &y& Elsevier]