Anode materials including graphite are known to be thermodynamically unstable toward organic solvents and salts and become covered by a passivating film (Solid electrolyte interphase, SEI) which retards the kinetics because of the high electronic resistivity. To achieve high performance in lithium ion batteries (LIBs), the SEIs are required to be mechanically stable during repeated cycling and possess highly ion-conductive. In this work, we have investigated an artificial pre-SEI on graphite electrode using a polymer binder containing lithium (i.e., a Li-copolymer of isobutylene and maleic anhydride, Li-PIMA) and its effect on the anode performances. During charging, the polymer binder with the functional group (–COOLi) acts as a SEI component, reducing the electrolyte decomposition and providing a stable passivating layer for the favorable penetration of lithium ions. Hence, by using the binder containing lithium, we have been able to obtain the first Coulombic efficiency of 84.2% (compared to 77.2% obtained using polyvinylidene fluoride as the binder) and a capacity retention of 99% after 100 cycles. The results of our study demonstrate that binder containing lithium we have used is a favorable candidate for the development of high-performance LIBs.

We for the first time prepared nanoporous tungsten carbide by polymer/surfactant method, which is made up of WC nanoparticles and carbon and has a pore diameter of ca. 4.5 nm. Platinum supported on these nanoporous tungsten carbide shows higher electrocatalytic (2.5 times) activity than commercial 20%Pt-Ru E-Teck catalyst in the half cell mode and shows equivalent activity to commercial Pt-Ru commercial catalyst in the real fuel cell mode with a much less amount of noble metals.