Search

Background. Material tribology has widely expanded in scope and depth and is extended from the mechanical field to the biomedical field. The present study aimed to characterize the nanocoating of highly pure (99.9%) niobium (Nb), tantalum (Ta), and vanadium (V) deposited on 316L stainless steel (SS) substrates which considered the most widely used alloys in the manufacturing of SS orthodontic components. To date, the coating of SS orthodontic archwires with Nb, Ta, and V using a plasma sputtering method has never been reported. Nanodeposition was performed using a DC plasma sputtering system with three different sputtering times (1, 2, and 3 hours). Results. Structural and elemental analyses were conducted on the deposited coatings using XRD, FESEM, and EDS showing a unique phase of coating metals over their substrates with obvious homogeneous even deposition. A highly significant positive correlation was found between sputtering time and thickness of the achieved coatings. AFM revealed a reduction in the surface roughness of 316L SS substrates sputtered with all coating materials, significantly seen in V coatings. Conclusions. Sputtering time and coating material play a significant role in terms of microstructure and topography of the achieved coatings being the best in the Ta group; moreover, surface roughness was significantly improved by V coatings. Likewise, it is found to be sputtering time independent for all used coatings.

Background. Nanocoating of biomedical materials may be considered the most essential developing field recently, primarily directed at improving their tribological behaviors that enhance their performance and durability. In orthodontics, as in many medical fields, friction reduction (by nanocoatings) among different orthodontic components is considered a substantial milestone in the development of biomedical technology that reduces orthodontic treatment time. The objective of the current research was to explore the tribological behavior, namely, friction of nanocoated thin layer by tantalum (Ta), niobium (Nb), and vanadium (V) manufactured using plasma sputtering at 1, 2, and 3 hours on substrates made of 316L stainless steel (SS), which is thought to be one of the most popular alloys for stainless steel orthodontic archwires. The friction of coated 316L SS archwires coated with Ta, Nb, and V plasma sputtering is hardly mentioned in the literature as of yet. Results. An oscillating pin-on-plate tribological test using a computerized tribometer was performed by applying a load of 1 N for 20 minutes under the dry condition at room temperature (25°C) to understand their role in the tribological behavior of the bulk material. Ta and Nb were found to reduce the friction of their SS substrate significantly (45 and 55%, respectively), while V was found to deteriorate the friction of its substrate. Moreover, sputtering time had no substantial role in the friction reduction of coatings. Conclusions. Nanocoating of 316L SS bulk material by Nb and Ta with a 1-hour plasma sputtering time can enhance dramatically its tribological behavior. Higher coating hardness, smaller nanoparticle size, intermediate surface coating roughness, and lower surface binding energy of the coatings may play a vital role in friction reduction of the coated 316L SS corresponding to SS orthodontic archwires, predicting to enhance orthodontic treatment.

Background: This study aims to assess the prevalence of malposed canines among students of College of Dentistry/ University of Baghdad and evaluate the relation between canine malposition and occlusal features. Material and method: The prevalence of buccally malposed canines was estimated by intra-oral visual examination of 250 young adult subjects (106 males and 144 females), their ages were between 19-24 years. Results: The prevalence of the mandibular malposed canine (12%) was higher than the maxillary buccally malposed canine (10%). Generally, malposed canines were found higher in females than in males and mostly seen in class l Angle’s classification and buccally more than lingually. Conclusion: A relationship exists between canine malposition and other occlusal features. Keywords: tooth malposition, occlusal features, Angle classification