Purpose: To investigate the esthetic outcomes based on the color differences in zirconia (Zr) of varying thickness, resin cement color, and types of titanium (Ti) implant surface treatments. Materials and Methods: Overall, 28 high-translucency monolithic zirconia (HTMZ) specimens were arranged into four groups based on Zr thickness: 1.0, 1.5, 2.0, and 2.5 mm (n = 7 per thickness). Each group was tested using two resin cement colors (clear and opaque) in combination with six surface-treated Ti groups (n = 7), including untreated titanium (UT), anodization (AN), 50-µm alumina airborne-particle abrasion followed by AN (SBAN), AN followed by 50-µm alumina airborne-particle abrasion (ANSB), 9.5% hydrofluoric acid followed by AN (HFAN), and AN followed by 9.5% hydrofluoric acid (ANHF). This created a total of 48 experimental groups, including the use of composite resin (n = 7, shade A2D) for four control groups. All specimens were measured using a spectrophotometer and subsequently compared with composite resin (control) with the corresponding Zr thickness to establish color differences. A color difference of < 2.7 was considered clinically acceptable. The data obtained were statistically analyzed using ANOVA and post hoc test (P = .05). Results: Zr thickness, resin cement color, and type of Ti implant surface treatment significantly affected the observed color differences (P < .05). When using 2.5-mm HTMZ with clear resin cement on AN, UT, SBAN, HFAN, and ANSB, the mean color differences were below the clinically acceptable values, and the 95% CIs of color differences were below the clinically acceptable values for AN, UT, and SBAN groups. Conclusions: HTMZ with a minimum thickness of 2.5 mm and clear resin cement on AN, UT, and SBAN groups potentially result in acceptable color matching with 95% CIs. [ABSTRACT FROM AUTHOR]

Purpose: To compare the color dimensions, color discrepancies (E00), and surface roughness of milled materials before and after application of a bleaching agent. Materials and Methods: A total of 10 extracted molars were obtained. Each tooth was cut in transverse sections to create disks (3-mm thick, 10-mm diameter; control group). Disk specimens of eight materials (n = 10 per group) were fabricated: polymethyl methacrylate (PMMA) interim material (PMMA-Telio group), two resin nanoceramics (RNC-Ultimate group and RNC-Cerasmart group), two hybrid ceramics (HC-Shofu group and HC-Enamic group), lithium disilicate (LD-Emax group), zirconia-reinforced glass ceramic (ZGC-Suprinity group), and zirconia (Zr-InCeram group). Color measurements were obtained using a spectrophotometer before and after applying 35% hydrogen peroxide-based bleaching agent. Pre- and postbleaching surface roughness (Sa) analyses were completed using a profilometer. Results: Significant L*, a*, b*, and E00 value differences were found (P < .05). Color discrepancies (E00) ranged from 0.30 ± 0.14 to 4.82 ± 0.10. The highest color discrepancies were measured on the PMMA-Telio group, while the lowest color discrepancies were computed for ZGC-Suprinity, RNCUltimate, and RNC-Cerasmart. Significant surface roughness differences were found (P < .05). The largest increase of surface roughness values between the pre- and postbleaching measurements was obtained in the PMMA-Telio group with a mean Sa value of 4.73 ± 3.02, while the largest decrease of surface roughness values between the pre- and postbleaching measurements was obtained in the Zr-InCeram group with a mean Sa value of -1.58 ± 0.10. Conclusions: The milled materials showed significant pre- and postbleaching color and surface roughness discrepancies. [ABSTRACT FROM AUTHOR]

Surface contaminants on customized implant abutments could trigger an inflammatory response in the peri-implant tissues. The aim of this randomized controlled study was to assess the radiographic bone changes around implants restored with customized, platform-switched abutments, with and without autoclave treatment, 12 months after definitive restoration. Dental implants were placed 1 mm subcrestally in 64 systemically healthy patients (mean age: 63.3 ± 10.0 years; 31 patients had a history of periodontitis) to replace single or multiple missing teeth. According to a randomization list, abutments were subjected to steam and autoclave sterilization (43 implants, test group) or steam cleaning alone (44 implants, control group). Periapical standardized radiographs were taken at implant placement, prosthetic abutment connection, and 12 months after definitive cement-retained restoration. All implants were clinically stable without any sign of infection at the 12-month follow-up. An average marginal bone loss of 0.25 ± 0.19 mm was found in the test group compared to 0.35 ± 0.23 mm in the control group (no statistically significant difference), while the percentage of bleeding sites was significantly higher in the control group (8.7% ± 13.1% vs 19.1% ± 19.8%; P = .035). Autoclave treatment of customized abutments seems to reduce the inflammatory response around subcrestally placed implants. [ABSTRACT FROM AUTHOR]

Purpose: To compare the effect of taper, length, angle, and number of vertical axial walls on the retentive strength of a cemented crown on a partially customized hybrid abutment in the esthetic zone. Materials and Methods: A total of 35 metal copings were used and divided into two groups. One group had 30 copings cemented to their corresponding 8-degree tapered abutment with lengths from 3 to 8 mm, increasing in 1-mm increments (5 copings per length). The other group had the remaining 5 copings and consisted of a standardized metal coping that matched a hexagonal abutment with 3-mm vertical axial walls and the sequential removal of 1, 2, and 3 contiguous vertical axial walls. Dislodgment tests were performed for all copings in both groups. Maximum retentive forces were measured in retentive strength (kgF), with a conversion factor of 9.807 N = 1 kgF. Results: At each tapered abutment length, the retentive strength increased proportionally and was significantly different, ranging from 31.67 ± 4.10 kgF to 67.68 ± 11.22 kgF (F [5,24] = 20.46, P < .001). An unmodified hexagonal abutment demonstrated the highest retentive strength (70.15 ± 12.97 kgF). The sequential removal of 1, 2, and 3 contiguous vertical axial walls of the hexagonal abutment resulted in retentive strength values of 59.89 ± 10.06 kgF, 57.01 ± 9.62 kgF, and 55.99 ± 9.35 kgF, respectively, with no significant difference (P > .05) in strength. Conclusions: A partially customized abutment with vertical axial walls on one side and a profile reduction on the opposite side can provide comparable retention to cemented copings at one-third the length and at one-sixth the surface area of an 8-mm abutment with an 8-degree taper. [ABSTRACT FROM AUTHOR]

Purpose: To measure the surface temperature distribution after using a CO2 laser to heat titanium dental implants via different power settings, application intervals, and irradiation times. Materials and Methods: A total of 10 tissue-level titanium implants (Screw-Line Promote Plus, Camlog; 4.3 × 11 mm) were placed (EpoFix, Struers) and irradiated with a CO2 laser (Denta 2, Lutronic) with a wavelength of 10.6 µm at power levels of 4 watts (Group 1), 6 watts (Group 2), 8 watts (Group 3), and 10 watts (Group 4). A continuous beam mode (setting I) and noncontinuous beam modes with 5-second (setting II) and 10-second (setting III) pause intervals were used. For each setting, a total irradiation time of 50 seconds was used and repeated 10 times. The temperature was measured using external thermocouple (Testo) in contact with the implant surface at the implant shoulder, middle, and apex. A linear regression model was used to analyze the data (P = .05). Results: Setting I demonstrated the most rapid increase in implant surface temperature in all three test sites as well as the greatest total temperature at 50 seconds of irradiation time. The greater the pause interval (settings II and III) during the 50 seconds of irradiation, the lower the rate of temperature increase as well as the total temperature in all three test sites and with all power levels. The average temperature difference between the apex and shoulder site was significant for setting III for all groups, but not for any groups in settings I and II. Conclusions: Heating the internal aspect of an implant with a CO2 laser produces different temperature distribution profiles depending on the laser power level and the application interval. Laser-beam irradiation leads to a temperature gradient, which is greatest at the implant apex and smallest at the implant shoulder. [ABSTRACT FROM AUTHOR]

Purpose: To investigate how well an implant stability quotient (ISQ) represents resonance frequency. Materials and Methods: Benchtop experiments on standardized samples that replicated a mandibular premolar site were conducted to correlate an ISQ value and a resonance frequency to synthetic bone density and an incremental insertion torque; then, a frequency spectrum analysis was performed to check the validity of the resonance frequency analysis (RFA). Brånemark Mk III implants (4 × 11.5 mm; Nobel Biocare) were placed in Sawbones test models of five different densities (40, 30, 40/20, 20, and 15 PCF). An incremental insertion torque was recorded during implant placement. To perform stability measurements, the test models were partially clamped in a vise (unclamped volume: 10 × 20 × 34 mm). A MulTipeg (Integration Diagnostics) was attached to the implants, and a Penguin (Integration Diagnostics) RFA measured ISQ. Simultaneously, the MulTipeg motion was monitored via a laser Doppler vibrometer and processed by a spectrum analyzer to obtain the resonance frequency. Tightness of the clamp was adjusted to vary the resonance frequency. A statistical analysis produced a linear correlation coefficient (R) among the measured ISQ, resonance frequency, and incremental insertion torque. Results: The resonance frequency had high correlation to the incremental insertion torque (R = 0.978), confirming the validity of using RFA for this study. Measured ISQ data were scattered and had low correlation to the resonance frequency (R = 0.214) and the incremental insertion torque (R = 0.386). The spectrum analysis revealed the simultaneous presence of multiple resonance frequencies. Conclusions: For the designed benchtop tests, resonance frequency does indicate implant stability in view of Sawbones density and incremental insertion torque. However, ISQ measurements do not correlate to the resonance frequency and may not reflect the stability when multiple resonance frequencies are present simultaneously. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the dimensional accuracy of implant impressions obtained using five different tray types and two techniques. Materials and Methods: A partially dentate maxillary Kennedy Class II model was created as a reference model through 3D printing. Then, implant analogs 4.3 mm in diameter were placed at the first premolar, first molar, and second molar sites. Five types of trays were used to create impressions: (1) metal stock trays, (2) plastic stock trays, (3) custom trays fabricated using liquid crystal display (LCD), (4) custom trays fabricated using fused deposition modeling (FDM), and (5) custom trays fabricated using urethane dimethacrylate (UDMA) resin. Open and closed tray techniques were also compared. In total, 150 impressions were obtained. The reference model and impressions were scanned using a laboratory scanner. Additionally, the positional and angular deviations of implants with different tray types and techniques were evaluated using the superimposition method. Results: There was no statistically significant difference (P > .05) between the impression accuracy with the different tray types and impression techniques. The angular deviations with plastic and UDMA trays were greater than those with metal, FDM, and LCD trays. Angular deviation at the second molar was greater when using closed plastic trays compared to open plastic trays. The highest and lowest positional deviations were observed at the first molar implant with an open plastic tray impression (mean ± SD of 62.46 ± 28.54 mm) and a closed LCD tray impression (36.59 ± 29.93 mm). The greatest angular deviation was observed with an open FDM tray impression at the first premolar implant (0.067 ± 0.024 degree), and the lowest angular deviation was observed with a closed metal stock tray impression at the second molar implant (0.039 ± 0.025 degree). Statistical differences were detected using the Mann-Whitney U test for paired groups and the Kruskal-Wallis test for groups with more than three comparisons (P > .05). Conclusions: Plastic and metal stock trays or conventional and 3D-printed custom trays can be used to obtain implant impressions for maxillary partially edentulous arches with similar dimensional accuracy. The five tray types and two techniques may be safely used to obtain impressions of partially edentulous maxillary arches with three implants. [ABSTRACT FROM AUTHOR]

The article discusses studies which show that full-ceramic prosthetic restorations for single crowns (SCs) and fixed dental prostheses (FDPs) are high quality and have a satisfactory survival rate comparable to porcelain-fused-to-metal (PFM). These studies include the survival outcome and complications in a retrospective clinical study of complete-arch fixed implant-supported prostheses (CAFIPs), the prevalence of prosthetic complications, and clinical performance of implant-supported FDPs.

Purpose: To investigate the screw loosening and fracture resistance of different hybrid abutment crown restorations after thermomechanical aging. Materials and Methods: Restorations were produced from zirconia, lithium disilicate, and hybrid ceramics with a CAD/CAM system (n = 10). Restorations and titanium bases (Ti-bases) were cemented, and the abutment screws were torqued to 30 Ncm. They were retorqued after 10 minutes, and then the removal torque values (RTVs) were measured. After 250,000 and 500,000 cycles of thermomechanical aging were completed, the RTVs were measured again, and removal torque loss (RTL) ratios were calculated. The specimens were subjected to a fracture resistance test after 750,000 cycles of thermomechanical aging, and the load at failure was recorded as the fracture resistance (N). The results were statistically analyzed (a = .05). Results: Aging was effective on the RTVs and RTL ratios (P < .001). The highest RTV was observed before aging; however, the RTVs significantly decreased and RTL ratios significantly increased after aging (P < .05). The fracture resistance values significantly differed among the ceramic materials. All lithium disilicate and hybrid ceramic specimens showed restoration fracture and most of the zirconia specimens showed Ti-base-related failure. Conclusions: Hybrid abutment crowns made of zirconia, lithium disilicate, and hybrid ceramics can withstand the average occlusal forces in the molar region; however, the ceramic type may affect the failure type. Retightening of the abutment screws after 10 minutes following the first tightening and annually may be beneficial to prevent the adverse effects of screw loosening on the integrity of the implant-abutment connection. [ABSTRACT FROM AUTHOR]

Background: Platelet-rich fibrin (PRF) is used to prepare "sticky bone" by combining it with bone graft material. The present study investigated the ability of different bone grafts to absorb growth factors from the PRF and release them over time. Materials and Methods: Human blood was collected from 10 healthy volunteers for liquid PRF preparation. Bovine bone, allograft (mineralized and demineralized), and synthetic bone were each mixed with the PRF to prepare a sticky bone. All sticky bone samples were incubated for up to 4 days. The absorption and release pattern kinetics of two selective growth factors within the PRF--platelet-derived growth factor (PDGF) and bone morphogenetic protein-2 (BMP-2)--were quantified with immunofluorescence staining and enzyme-linked immunoassay (ELISA) testing. Results: All bone graft materials adsorbed the examined growth factors from the PRF. ß-TCP showed the highest adsorption levels, followed by the xenograft, and the allografts showed the lowest adsorption levels. Furthermore, PDGF showed a fast-release pattern from the grafts, whereas BMP-2 was released at a later stage. Similar to the adsorption pattern, the ß-TCP and xenograft were better able to sustain the release of the PRF growth factors from the graft than the allografts. Conclusions: The adsorption of PDGF and BMP-2 differ between graft materials, with superior results for ß-TCP, followed by xenograft, then allograft materials. [ABSTRACT FROM AUTHOR]

This clinical case outlines a comprehensive digital workflow for a minimally invasive multidisciplinary treatment. The process utilizes one open-source software for digital wax-up and one low-cost software to address esthetic concerns related to teeth misalignment. The patient's function was stabilized with a digitally made occlusal splint. The application of the described digital workflow technique, incorporating open-source, lowcost, and closed software, played a pivotal role in attaining a straightforward and predictable outcome with minimally invasive treatment. Furthermore, the continual evolution of technology contributes to the growing precision of dental procedures. The presented digital workflow helped formulate a predictable treatment plan, replicate a diagnostic digital wax-up, and achieve precise teeth alignment. This approach satisfactorily addressed the patient's esthetic concerns, providing an outstanding approximation of the definitive result. [ABSTRACT FROM AUTHOR]

Objectives: The objective was to evaluate the polymerization efficiency of different bulk-fill resin-based composites cured by monowave and polywave light-curing units, by assessment of the degree of conversion and Vickers microhardness at different depths. Method and materials: Two commercially available bulk-fill resin-based composites were used: Filtek One Bulk Fill Restorative (3M ESPE) and Tetric N-Ceram Bulk Fill (Ivoclar Vivadent). The light-curing units utilized were two LED light-curing units: a monowave LED light-curing unit (BlueLEX LD-105, Monitex) and a polywave LED light-curing unit (Twin Wave GT-2000, Monitex). For each test, 20 cylindrical specimens (4 mm diameter, 4 mm thickness) were prepared from each bulk-fill resin-based composite using a split Teflon mold. Ten specimens were light-cured by the monowave light-curing unit and the other ten were light-cured by the polywave light-curing unit according to the manufacturer's recommendations. Attenuated total reflectance-Fourier transform infrared spectroscopy (ATRFTIR) was used to assess the degree of conversion, and a Vickers microhardness tester was used to assess Vickers microhardness. Statistical analysis was performed using three-way ANOVA and Tukey post-hoc tests (P < .05). Results: The degree of conversion and Vickers microhardness in bulk-fill resin-based composites containing only camphorquinone as photoinitiator were similar when cured with either monowave or polywave light-curing units. However, bulk-fill resin-based composites containing a combination of photoinitiators exhibited significantly higher degree of conversion and Vickers microhardness when cured with a polywave light-curing unit. Although all groups showed statistically significant differences between the top and bottom surfaces regarding degree of conversion and Vickers microhardness, all of them showed bottom/top ratios > 80% regarding degree of conversion and Vickers microhardness. Conclusion: The polywave light-curing unit enhanced the polymerization efficiency of bulk-fill resin-based composites especially when the latter contained a combination of photoinitiators, but does not prevent the use of a monowave light-curing unit. [ABSTRACT FROM AUTHOR]

This canine in vivo study assessed the effect of recombinant human platelet-derived growth factor (rhPDGF) on the healing of periapical tissues following apical surgery. From a total of 96 premolar teeth, 64 teeth from six beagle dogs (2 years old) were classified as experimental and were randomly assigned to four experimental groups (16 teeth per group). After having the pulp extirpated, leaving teeth open to the oral cavity for 1 week, and sealing with an immediate restorative material for 8 weeks, nonsurgical endodontic treatment was performed. A split-mouth design was used, and intra-animal randomization of treatment sides was applied to the groups as follows: apical curettage + 1.5-mm root-end resection (Group 1); apicoectomy + mineral trioxide aggregate (MTA) root-end filling (Group 2); apicoectomy + MTA root-end filling + rhPDGF (Group 3); and apical curettage + rhPDGF (Group 4). The animals were sacrificed 24 months after apical surgery, and histologic and µCT analyses were performed for bone volume loss (BVL). Group 1 showed partial resolution of the periapical lesions without signs of tissue regeneration (BVL: 49.09 ± 10.97 mm3). Group 2 had minimal bone regeneration and showed cementum reformation in 9 teeth, with no direct attachment to the MTA (BVL: 35.34 ± 10.97 mm3). Group 3 showed regeneration of all damaged apical tissues without direct contact between the cementum and MTA (BLV: 4.51 ± 1.55 mm3). Group 4 showed regeneration of PDL, bone, and cementum and attachment of functional cementum fibers (BVL: 2.82 ± 2.3 mm3). The difference in BVL was statistically significant only for Groups 1 and 2 (P < .05). rhPDGF may help regenerate apical tissue structures following apical surgery. [ABSTRACT FROM AUTHOR]

This study aimed to evaluate the periodontal responses of subgingival proximal margins elevated using different restorative materials. A total of 120 proximal cavities with dentin/cementum gingival margins were elevated using one of four materials (resin-modified glass ionomer, glass hybrid, flowable bulk-fill resin composite, or bioactive ionic resin) and completed with the same overlaying resin composite. At 2 weeks (baseline), 6 months, 1 year, and 2 years postrestoration, periodontal parameters and the radiographic distance between the restoration margin and bone crest were evaluated. Appropriate statistical analyses were performed. The values of all periodontal parameters increased with time, although only the increases in Plaque Index and probing depth within each material group were statistically significant. There were no statistically significant differences in any of the periodontal parameters between the different materials within the same evaluation period, nor between different time points or material groups in the radiographic distances. Both glass ionomer--based and resin-based materials were periodontally safe as subgingival open sandwich restorations. [ABSTRACT FROM AUTHOR]

Purpose: To analyze the effectiveness of coating of abutments with antimicrobial agents and their influence on the physicochemical and biologic properties of the coated materials. Materials and Methods: This work was registered in Open Science Framework (osf.io/6tkcp) and followed the PRISMA protocols. A search of two independent reviewers of articles published up to October 29, 2021, was performed in the Embase, PubMed, Science Direct, and Scopus databases. Results: The databases found a total of 1,474 references. After excluding the duplicates, 1,050 remained. After reading the titles and abstracts and applying the inclusion criteria, 13 articles remained and were read in full. A total of 8 articles were included in this systematic review. Different antimicrobial agents have been used to coat abutments, including graphene oxide, polydopamine, titanium and zirconium nitride, lactoferrin, tetracycline, silver, and doxycycline with varied release times. Titanium-coated silver showed a better antimicrobial agent release time of up to 28 days. Chemical analysis confirmed the presence of antimicrobials on the surface after coating. Different pathogenic microorganisms, such as Streptococcus sanguinis, Streptococcus oralis, and Staphylococcus aureus, were inhibited when in contact with the coated surface. Conclusions: This review showed that there is still no consensus on which is the better antimicrobial agent and which coated materials have the better performance. However, the association of surface coating of abutments with antimicrobials is feasible and can benefit many patients, which can support their clinical use to favor the healing process and prevent infections that can lead to treatment failure with dental implants. [ABSTRACT FROM AUTHOR]

Objectives: To compare marginal gap width and depth with different cementation systems, excess removal, and after polishing. Method and materials: In total, 80 composite crowns were milled, divided into ten groups, and cemented on identical artificial teeth. Eight crowns per group were fixed with (i) zinc phosphate cement (ZnOPh), (ii) glass-ionomer cement (GIC), (iii) resin-reinforced glass-ionomer cement (GIC mod), (iv) dual-curing adhesive composite (Comp dual), or (v) dual-curing self-adhesive composite (Comp SE dual). Excess removal was performed with a scaler after brief light-cure (tack-cure), final light-cure, during rubber or gel phase or by wiping with foam pellet. Curing was completed in chemical, dark cure, or light-curing modus. The specimens were polished and stored in water (37°C). The margins were digitized using a 3D laser-scanning microscope (VK-X100 series, Keyence). The width and the depth of the marginal gap were measured at 10 points between the crown margin and the preparation margin. Results: The width after excess removal varied between 65.1 ± 15.7 µm (Comp dual, wipe, with polishing) and 208.6 ± 266.7 µm (Comp SE dual, dark cure, without polishing). The depth varied between 29.8 ± 22.2 µm (Comp dual, wipe, with polishing) and 89.5 ± 45.2 µm (Comp SE dual, dark cure, without polishing). The impact on gap width and depth was detected for fixation material, excess removal, and polishing. Conclusion: The gap depth and width depend on the luting material and the mode of access removal. Polishing can improve the gap quality, especially for GIC and resin-based systems. [ABSTRACT FROM AUTHOR]

Objectives: To evaluate the effect of sonic oscillation on penetration depth and marginal adaptation of resin-based fissure sealants. Method and materials: Thirty-six extracted human third molars were randomized into three groups: in the HF group, teeth were sealed with a filled-resin-based sealant (Helioseal F); in the Sonic-HF group, teeth were sealed with Helioseal F and subjected to sonic oscillation (Compothixo Device, 140 Hz vibration frequency and ± 150 µm amplitude) before curing; in the CO group, teeth were sealed with an unfilled-resin-based sealant (Clinpro). All teeth were thermocycled for 1,500 cycles at 5°C and 55°C, then sectioned buccolingually into four sections (mesial, two middle, and distal). Sections were evaluated under SEM for marginal adaptation and scored. For penetration depth, three independent measurements from each tooth were recorded under SEM, and data were subjected to statistical analysis. Results: The group subjected to sonic oscillation (Sonic HF) resulted in significantly superior penetration depth and marginal adaptation compared with the HF group, but with no significant difference compared with the CO group. Conclusions: Sonic activation of resin-based sealant increased penetration depth into fissures and marginal adaptation to the enamel wall without decreasing filler load or compromising sealant mechanical properties. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the marginal leakage of three different types of bonding agents used with two posterior composites and a giomer, available commercially. Material and methods: Class II box-only cavities were prepared on 90 mandibular first molars with margins extending 1 mm beyond the cementoenamel junction. The samples were divided into nine groups based on three different bonding agents, two different composites, and a giomer. Cavities were restored per the manufacturer's description. Teeth were subjected to a thermocycling procedure (500Ã--, 5°C to 55°C) and dye penetration by immersing in a 2% methylene blue solution (Merck Specialties) for 24 hours. The marginal adaptation was evaluated as a continuous margin at the gingival level under a stereomicroscope. The results were analyzed using the Kruskal-Wallis and Mann-Whitney U tests. Results: The results of the groups with the total-etch technique showed no statistical difference between the nanohybrid Filtek Z250 XT (3M ESPE) and fine hybrid SwissTEC composite (Coltène\Whaledent AG). The groups with the self-etch technique showed no statistical difference when used with either of the two composites. The acid-etch technique showed better marginal adaptation than the self-etch technique. When the giomer (Beautifil II, Shofu) was used with the total-etch technique, it showed better adaptation than when used with the self-etch technique but overall showed more marginal leakage than the composites. Conclusion: The total-etch technique provided better marginal adaptation for the composites and giomer compared to the self-etch technique. Clinical significance: The demand for esthetic restorations continues to increase, and composite restorations are now considered the material of choice for Class II cavities. There are various concerns with composite restorations, one of them being good marginal adaptation to increase the life of the restoration. This study evaluated marginal leakage with the nanohybrid composite Filtek Z250 XT, fine hybrid composite SwissTEC, and a giomer when used with the total-etch technique and self-etch technique and reported satisfactory adaptation with the total-etch technique. [ABSTRACT FROM AUTHOR]

Periodontal intrabony defects (IBDs) are commonly encountered in dental practice and are usually treated by open flap debridement (OFD) with or without bone grafts and/or guided tissue regeneration (GTR), platelet-rich fibrin (PRF), or other additives. A difficulty with these approaches is maintaining the space for bone growth at the determined location. In this report, autologous sticky bone (ASB) was used and compared to a simple mixture of PRF and bone graft (PRF-BG) using the identical graft material-bioactive glass morsels-to assess its regenerative potential in IBDs, as sticky bone is known to maintain the space, according to previous research. A total of 21 IBDs were treated by OFD, PRF-BG mixture, or ASB. Regenerative assessment was clinically and radiographically performed by CBCT at 1 year. All the treatment modalities (OFD, PRF-BG, and ASB) showed statistically significant improvements clinically and radiographically at 1 year in terms of probing pocket depth reduction (PPDR), clinical attachment level gain (CALG), CBCT defect fill (CBCT-DF), and CBCT defect resolution (CBCT-DR); P < .05. The ASB group depicted the most favorable results (P < .05) in terms of the parameters at 1 year followed by the PRF-BG group and then the OFD group. Treatment of periodontal IBDs with ASB resulted in significant improvements in clinical and CBCT parameters compared to baseline at 1 year, and intrasurgical graft handling was much better in the ASB group. [ABSTRACT FROM AUTHOR]

This study investigated the effect of erbium, chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser conditioning on dentin bond strength and nanoleakage of different universal and self-etch adhesives. A total of 84 intact human third molar teeth were cut at the dentin level, and half of them were laser conditioned. The specimens were divided into three groups; two different universal resins and one self-etch adhesive resin were applied and composite resin restorations were created. For the microtensile bond strength (pTBS) test, 20 microspecimens were prepared from the laser and control group of each adhesive (n = 20) and tested with a universal device. For nanoleakage observation, 10 specimens were prepared from each group (n = 10) and stored in silver nitrate solution, and then the amount of nanoleakage was analyzed by field emission scanning electron microscopy (FESEM). Data were analyzed with two-way ANOVA, Tukey's honestly significant difference, and chi-square tests. The mean dentin bond strength of all adhesives in the laser groups was found to be statistically significantly lower than those of the control groups (P < .05). No difference was found between the mean bond strength of the adhesives in the laser and control groups (P > .05). Higher nanoleakage was observed in all adhesives in the laser groups compared to the control groups (P < .05). Irradiation of the dentin surface with Er,Cr:YSGG could adversely affect the piTBS and nanoleakage, likely by affecting the structure of the hybrid layer. [ABSTRACT FROM AUTHOR]

This article evaluated tooth discoloration after the use of calcium silicate-based materials to examine the effect of internal bleaching on tooth discoloration. The specimens were randomly divided into two experimental groups (n = 45) and a control group (n = 6). Cavities were filled with ProRoot MTA (Dentsply Sirona) in Group 1 and Biodentine (Septodont) in Group 2. Color measurements were taken with a spectrophotometer before and after the application of materials at 1 week, 13 weeks, and 6 months. After 6 months, Groups 1 and 2 were divided into three subgroups according to internal bleaching techniques. All color change ratios and lightness differences were calculated using the CIE L*a*b* system. Data were analyzed using repeated ANOVA and Kruskal-Wallis test (P = .05). There were statistically significant differences between Groups 1 and 2 at all time intervals (P < .05). Group 1 showed more discoloration than Group 2 (P < .05). There were no significant differences between the bleaching agents (P > .05). Additionally, specimens in both groups became lighter than their initial color (P < .05). Teeth treated with ProRoot MTA exhibited darkening at 1 week that increased over time, whereas those treated with Biodentine maintained the lightness for 6 months. [ABSTRACT FROM AUTHOR]

Purpose: To examine the stresses caused by different All-on-4 surgical techniques—conventional, a combination of monocortical and bicortical, bicortical, and nasal floor elevation—on the implant and the surrounding bone using 3D finite element analysis (FEA). Materials and Methods: A 3D bone model of the atrophic maxilla was created based on CT imaging of the fully edentulous adult patient. All implants used in the models were 4 mm in diameter, and the length was 13 mm in the anterior and 15 mm in the posterior. Implants were applied to four different atrophic maxillary models with the All-on-4 technique: anterior and posterior monocortical implants in the first model, anterior monocortical and posterior bicortical in the second model, anterior and posterior bicortical in the third model, and anterior and posterior bicortical with nasal floor elevation in the fourth model. Eight linear analyses were performed by applying force from both vertical and 45-degree oblique directions to the four models prepared in our study. Results: When the cortical and cancellous bone around the anterior implants was examined, it was observed that the oblique and vertical loading conditions and the stresses around the implant were similar in all models. When the posterior implants were examined, model 1 (ie, anterior and posterior monocortical implants) showed the greatest oblique compression, vertical compression, and vertical tension forces. According to the Von Mises stress (VMS) analysis results for anterior and posterior implants, higher values were observed in model 1 compared to models 3 and 4 under oblique and vertical forces. It was observed that bicortical placement of the implants reduced the stresses on the bone and implant-abutment system but had no significant effect on the stress on the bar. Conclusions: According to the results of our study, in the All-on-4 technique, bicortical placement of the implants reduced the stresses on the bone and implant when the anatomical limitations allowed. In addition, nasal floor elevation can be applied in the atrophic maxilla in appropriate indications. [ABSTRACT FROM AUTHOR]

The article discusses research published in the 2021 issue of the "International Journal of Environmental Research and Public Health" which evaluated the use of short dental implants compared to standard dental implants. The research reviewed studies on short implants and standard-length implants placed in augmented and nonaugmented edentulous sites, short implant survival, stability and marginal bone levels, and implants placed in the posterior maxilla and in medically compromised patients.

Fluorapatite glass-ceramic (GC) and yttria-stabilized zirconia (YSZ) are two commonly used ceramic materials for dental prosthetic restorations. Fluorapatite GCs are known for their outstanding biocompatibility and aesthetic characteristics, moreover, they can release fluoride ions which have anticaries effect. Nevertheless, they often lack the requisite strength and toughness to withstand high occlusal forces. Conversely, YSZ exhibits remarkable mechanical properties, however, it is susceptible to excessive wear on opposing teeth. To address these limitations, a novel fluorapatite GC-YSZ composite ceramic was designed and formed through vat photopolymerization. The effect of composition ratios of fluorapatite GC particles and YSZ fibers (0˗40 wt% YSZ) on the forming precision, mechanical properties, and tribological compatibility with GC was thoroughly investigated. The results demonstrated that optimal comprehensive performance was achieved when the YSZ fiber content reached 40 wt%, which resulted in a fracture toughness of 1.68 MPa m1/2, marking a 98.8 % increase over pure GC. The specific wear rates of the sample and the antagonistic titanium ball were reduced by 75.6 % and 63.8 %, respectively, compared with GC. In addition, the dimensional accuracy error of the green body was reduced by approximately 44 %. The design and fabrication of GC-YSZ composites offer an approach for developing high-performance all-ceramic dental materials. [ABSTRACT FROM AUTHOR]

Objectives: Investigate the effect of different postpolymerization protocols, aging, and 3D printing systems on the flexural strength (σ), dimensional stability, and roughness of resins used to fabricate occlusal splints, dental models, and temporary restorations. Material and methods: 180 bars (25 × 2 x 2 mm—ISO 4049) of each type of resin (T—Temporary/Cosmos Temp, Yller; OS—Occlusal splint/Cosmos Splint, Yller; MO – Models/ Cosmos Model, Yller) were printed and divided into 12 groups (n = 15) according to the factors: “Postpolymerization” (Ctr – Control; UV – Ultraviolet oven and MW – Microwave); “Printer” (SLA- stereolithography (Forms 2/Formslab); LCD- liquid crystal display (FlashForge Foto 6.0/FlashForge)) and “Aging” (TC – 10,000 thermocycling cycles and Without). Each bar was measured with a digital caliper at 11 points before and after postpolymerization to evaluate dimensional stability. The samples were subjected to the σ test (100Kgf;1 mm/min). Data was evaluated using Three- and Two-way ANOVA, and Tukey’s test (5%). Weibull analysis, Scanning Electron Microscopic and optical profilometry was performed. Results: LCD printing system and UV oven postpolymerization exhibited the highest σ (P <.05). The groups printed in SLA and post-polymerized in microwave ovens showed the greatest variations in their dimensions, for the occlusal splint resin, the OS-SLA-MW group (-4.29 ± 3.15)A showed a shrinkage of 40.2%. The resins for models (3.31 ± 0.66)A and temporary (-2.06 ± 1.52)A showed a shrinkage of 33% and 20.6%, respectively. Conclusions: LCD printing with UV light postpolymerization was the most effective method for resins used in occlusal splints, dental models, and temporary restorations. SLA printing with UV postpolymerization showed the most significant dimensional changes, leading to shrinkage in occlusal splint resins, while model resins and temporary restorations expanded. Clinical relevance: Resins for 3D printing should ideally be post-polymerized with UV light and printed using LCD technology, as this approach results in better mechanical properties and less dimensional change compared to microwave oven post-polymerization. [ABSTRACT FROM AUTHOR]

Introduction: In this study, the effects of adding titanium dioxide nanotubes (TiO2) to 3D‐printed denture base resin on the mechanical and physical properties of denture bases were examined for the first time. Methods: The specimens were digitally created using 3D builder software from Microsoft Corporation through computer‐aided design. In accordance with the test specifications for transverse strength, impact strength, hardness, surface roughness, and color stability, specimens were designed and printed with certain dimensions following relevant standards. TiO2 nanotubes (diameter: 15–30 nm and length: 2–3 μm) were added to the 3D‐printed denture base resin (DentaBase, Asiga, Australia) at 1.0% and 1.5% by weight. Flexural strength, impact strength (Charpy impact), hardness, surface roughness, and color stability were evaluated, and the collected data were analyzed with ANOVA followed by Tukey's post hoc test (α = 0.05). Field emission scanning electron microscopy (FESEM) and energy dispersive x‐ray spectroscopy (EDX) mapping were used to evaluate the dispersion of the nanotubes. Results: Compared with those of the control group (0.0 wt.% TiO2 nanotubes), the average flexural, impact, and hardness values of the 1.0 and 1.5 wt.% TiO2 nanotube reinforcement groups increased significantly. Both nanocomposite groups showed significant color changes compared to that of the pure resin, and there was a considerable reduction in the surface roughness of the nanocomposites compared to that of the control group. Conclusion: Adding TiO2 nanotubes to 3D‐printed denture base materials at 1.0 and 1.5 wt.% could enhance the mechanical and physical properties of the material, leading to better clinical performance. Clinical Significance: In terms of clinical applications, 3D‐printed denture base material has been shown to be a viable substitute for traditional heat‐cured materials. By combining this with nanotechnology, existing dentures could be significantly enhanced, promoting extended service life and patient satisfaction while addressing the shortcomings of the current standard materials. [ABSTRACT FROM AUTHOR]

Background: Different pulp capping materials have different origins and compositions, require different preparations, and may vary in their bioactive properties. Aim: The purpose of this study was to evaluate the antibacterial activity, biocompatibility, and mineralization‐inducing potential of calcium silicate‐based pulp capping materials. Design: Six contemporary calcium silicate‐based cements, ProRoot MTA, MTA Angelus, Biodentine, EndoSequence, NeoMTA 2, and NeoPutty, were evaluated. The antibacterial effects of these materials against Streptococcus mutans UA159 and Enterococcus faecalis ATCC 29212 were determined by the agar diffusion assay and the direct culture test. The biocompatibility and mineralization‐inducing potential of these materials in preodontoblastic 17IIA11 cells were evaluated by the MTT assay and by Alizarin Red S staining, respectively. Results and Conclusion: In agar diffusion test, only Biodentine showed distinct antibacterial effects against S. mutans. All the tested materials, however, showed antibacterial effects against S. mutans and E. faecalis in the direct culture test, with Biodentine showing the strongest growth inhibition against both S. mutans and E. faecalis. All the tested materials showed acceptable biocompatibility and mineralization‐supporting potential in our experimental conditions. In summary, ProRoot MTA, MTA Angelus, Biodentine, EndoSequence, NeoMTA 2, and NeoPutty demonstrated acceptable in vitro antimicrobial, biocompatible, and mineralization‐supporting properties. [ABSTRACT FROM AUTHOR]

Background: Children with dental caries are treated with stainless steel metal crowns (SSC), but the aesthetics and precision still need to be improved. Currently, both 3D‐printed resin crowns (PRC) and computer‐aided design/computer‐aided manufacture (CAD/CAM) resin crowns (CRC) meet the clinical requirements for crown applications in terms of strength, production time, cost, and aesthetics. Aim: This study replaced SSC with customized resin crowns by 3D printing and CAD/CAM. Design: In this study, PRC, CRC, and SSC were used for incisor and molar restorations, and 60 crowns were made with 10 for each group. The fabrication efficiency, surface characteristics, marginal fit, and stability of the two different crowns were evaluated. Results: PRC and CRC show superior color and surface characteristics, though production times are longer (5.3–12.4 times and 3.3–9.1 times, respectively) than for SSC (p <.05). They, however, can be completed within 80 min. Edge gaps for PRC and CRC are significantly lower (13.0–19.2 times and 13.0–13.7 times) than for SSC (p <.05). All materials exhibit good stability. Conclusion: The 3D‐PRCs and CAD/CAM resin crowns may replace SSCs as a potential choice for clinical child caries. [ABSTRACT FROM AUTHOR]

Background: The evidence underpinning caries management for children has progressed dramatically over the past 20 years. Anecdotally, this is not reflected in the teaching provided to undergraduate dental students, with the ongoing teaching of outdated methods within some dental schools. Aim: To capture the current undergraduate teaching provision and clinical treatment experience requirement relative to caries management in paediatric dentistry in UK dental schools. Design: Cross‐sectional analysis of current teaching methods on paediatric caries management was obtained using a piloted online data collection form. Question content included current caries teaching methods, assessment of student exposure and competence. The results were analysed descriptively. Results: Of the 16 UK dental schools, 14 participated. Discrepancy in teaching content was apparent. Many schools (n = 9) taught biological caries management through therapeutic fissure sealants, yet this was not reflected in assessment and clinical requirements. Some schools (n = 4) taught amalgam placement in children, and most (n = 12) operatively taught treatments that would no longer be routinely provided in general dental practice in the UK, including primary tooth pulpotomy. Conclusion: There is substantial variation in the paediatric caries management techniques that are taught across UK dental schools, demonstrating a need for a national consensus to address these disparities. [ABSTRACT FROM AUTHOR]

Background: Paediatric‐preformed zirconia crowns have been associated with several issues, primarily their inability to be crimped and the need for extensive tooth preparation. Additionally, the capacity to adjust the size, shape, and fit of these crowns is very limited. Aim: To evaluate and compare the fracture strength of four different types of dental crowns intended for paediatric patients. Design: The fracture resistance of four types of paediatric crowns was evaluated using the universal testing machine; freshly extracted primary molars received one of the following: preformed zirconia crowns, custom‐made computer‐aided design and computer‐aided manufacturing (CAD–CAM) zirconia crowns, custom‐made CAD–CAM ceramic crowns, and custom‐made CAD–CAM hybrid composite crowns. Data were statistically compared using the Kruskal–Wallis test followed by the Bonferroni test, and the level of significance was set at 5%. Results: Results showed that there was a statistically significant difference among the four groups (p <.001). The highest value of fracture force was observed for the milled zirconia crown and the lowest for the prefabricated zirconia. Conclusion: The implementation of the CAD–CAM digital crown fabrication technique has the potential to address issues associated with preformed crowns in paediatric patients, particularly in terms of fracture resistance. [ABSTRACT FROM AUTHOR]

Surface properties of dental implant materials, whether they are physical, chemical, mechanical, or biological, influence the processes of osseointegration and the development of the biological seal at the implant-soft tissue interface. In turn, successful occurrence of these steps prevents peri-implant diseases. This goal can be achieved through the application of surface treatments of a bioactive nature leading to an effective implant-bone union. Our work focuses on a thorough characterization of bioactive surface properties obtained through alkaline treatment on two different surfaces used in the dental implant industry, namely, a surface blasted with calcium phosphate particles and a micro-arc anodized surface. The results show that the alkaline treatment modifies the surface properties of both blasted and anodized samples. Modification is related to the formation of a nanoporous amorphous sodium titanate hydrogel that exhibits high bioactivity in an SBF medium. To assess in vitro biocompatibility and bioactivity, a 48-hour cell culture assay was conducted using dental pulp mesenchymal stem cells. All samples demonstrated cell adhesion, growth, and intercellular communication, indicating that the surfaces are biocompatible and non-cytotoxic. However, samples subjected to alkaline treatment exhibited qualitatively superior bioactivity and in vitro behavior and among them, the blasted sample produced the surface with best performance. [ABSTRACT FROM AUTHOR]

Highlights The characterization of S. persica (Salvadora persica) extract, which involved evaluating its antibacterial activity, demonstrated the extract's strong efficacy. Additionally, incorporating it into PMMA/HA showcased the composite's good antibacterial activity. The objective of this work is to evaluate how the incorporation of S. persica extract affects the wear resistance of the dental composite PMMA/HA, considering the critical importance of wear resistance in dental applications. The wear response of this biocomposite was tested against an Alumina ball using a pin‐on‐disc tribometer. Initially, the hydroxyapatite (HA) micro particles demonstrate a remarkable influence on wear behavior when incorporated at an optimal percentage (10%wt). This optimal inclusion rate not only significantly increases the wear rate but also instigates a shift in the wear mechanism, favoring abrasive wear while minimizing adhesive wear comparing to PMMA. The addition of the extract nanoparticles to the composite PMMA/HA decreases the wear rate except the composite containing 10 wt% of each filler. Additionally, it introduces adhesive wear, in addition to the existing fatigue and abrasion wear. Thus, the composite PMMA/HA could accommodate up to 10 wt% of the S. persica extract as the optimal percentage that provides antibacterial activity to this biocomposite without exhibiting a deterioration in wear performance. The evaluation of the effect of incorporating S. persica extract, which provides antibacterial activity, on the wear resistance of the PMMA/HA dental composite generally demonstrates a reduction in this property. The addition of S. persica extract introduces adhesive wear in addition to the fatigue and abrasion wear already present in the PMMA/HA composite. The composite PMMA/HA can accommodate up to 10 wt% of S. persica extract without compromising its wear performance. [ABSTRACT FROM AUTHOR]

Summary Background Study design Objectives Methods Results Main limitations Conclusions Dentigerous cysts are well‐known congenital defects in horses, and the literature on this condition is extensive. Recently, a third type of dentigerous cyst, associated with an exostosis arising from the temporal bone, has been described. Today, computed tomography (CT) is often available and provides detailed information about the exact location and extent of dentigerous cysts, allowing for the description of new findings.This is a case series outlining the clinical, radiographic and computed tomographic features of dentigerous cysts in seven horses presented to the Equine Clinic at the Vetsuisse Faculty, University of Zurich, Switzerland.The aim of this case series was to describe the radiographic and computed tomographic findings, and the occurrence of exostoses arising from the temporal bone, in horses with dentigerous cysts.The medical records of the Equine Hospital at the University of Zurich were reviewed for horses admitted with dentigerous cysts between 2007 and 2023. Data collected and analysed included patient signalment, clinical history, clinical signs and their duration prior to referral, diagnostic imaging results, treatment and outcomes.The most common location for the cysts was the base of the ear, although in one case, the maxillary sinus was involved. Of the seven cases, four were Icelandic horses. CT proved superior to standard radiography for determining the extent and precise location of the cysts, as well as for identifying dental material and exostoses in the temporal region. CT also facilitated detailed surgical planning. All cysts were surgically removed with good long‐term outcomes.Overall, the incidence of dentigerous cysts in horses was low. The relatively high occurrence of dentigerous cysts in Icelandic horses in this study is an interesting finding, though the small sample size calls for further research.Two of the cases in this series were similar to a recently described variant of a ‘temporal dentigerous cyst associated with an exostosis in the temporal region’ and were closely connected to the bony structure and draining tract. [ABSTRACT FROM AUTHOR]

Background: This clinical study aims to compare postoperative pain after single-visit root canal treatment of teeth with asymptomatic apical periodontitis using epoxy-resin-based AH Plus and calcium silicate-based Endosequence BC sealers with or without sonic activation. Methods: This study included 72 individuals with one first or second mandibular premolar tooth with asymptomatic apical periodontitis. They were randomly divided into four groups according to the root canal sealer (AH Plus or Endosequence BC) and activation protocol (sonic activation or non-activation) (n = 18). The participants were ask to rate their postoperative pain intensity on a NRS scale as none, minimal, moderate, or severe after 24 h, 48 h, 72 h, and 7 days following treatment. Patients were also asked to record the number of prescribed analgesic medication tablets (400 mg of ibuprofen) taken. Statistical analysis were performed using the Mann-Whitney U test, the Friedman test, the Spearman's correlation test, the Chi-square test. Significance level was established at 0.05. Results: There was no statistically significant difference in postoperative pain scores or analgesic intake between AH Plus and Endosequence BC sealers regardless of the activation protocol (p > 0.05). There was no statistically significant difference in postoperative pain scores between the sonic activation and non-activation groups (p > 0.05). A weak positive correlation was detected between Endoactivator sonic activation and sealer extrusion (r = 0.36). Conclusions: AH Plus and EndoSequence BC root canal sealers showed similar results in terms of prevalance and intensity of postoperative pain. Sonic activation and non-activation groups had similar postoperative pain scores. Clinical trial registration: The study was retrospectively registered with ClinicalTrials.gov (NCT06403293). Date of Registration: 07/05/24. [ABSTRACT FROM AUTHOR]

Background: Effective endodontic treatment requires the use of a root canal sealer with optimal properties to ensure a hermetic seal, prevent reinfection, and promote healing. Despite the availability of various sealers, a standardized evaluation system still needs to be improved. Objectives: To develop a Clinical Utility Index (CUI) that systematically evaluates and ranks root canal sealers based on their sealing ability, antimicrobial efficacy, flow rate, and solubility. Methods: The CUI was developed through a structured process involving expert identification, panel discussions, and the establishment of scoring criteria. Five sealers were evaluated (Sealers A, B, C, D, and E). Mean values for the core properties were calculated, and sealers were ranked accordingly. The total CUI for each sealer was computed based on the assigned scores for each property. Results: Sealer B achieved the highest CUI at 95%, demonstrating superior performance across all core properties. Sealer C followed with a CUI of 80%, while Sealer A ranked third with 60%. Sealers D and E showed the lowest performance, with CUIs of 30% and 35%, respectively, highlighting deficiencies in multiple properties. Discussion: The CUI provides a comprehensive evaluation framework for root canal sealers, facilitating informed decision-making by practitioners. Sealer B's high CUI underscores the importance of balancing sealing ability, antimicrobial effect, flow rate, and solubility. The results align with existing literature emphasizing the critical role of these properties in endodontic success. Conclusion: The CUI offers a robust and balanced method for evaluating root canal sealers, aiding in selecting the most suitable sealer based on empirical data. Future research should refine the index and validate its applicability in diverse clinical scenarios to enhance endodontic treatment outcomes. [ABSTRACT FROM AUTHOR]

Background: The materials used in root canal filling and radiotherapy (RT) application can affect the load-to-failure of the teeth. This study aimed to compare the load-to-failure of the teeth filled with AH Plus (AHP) or AH Plus bioceramic (AHPB) before or after 60 Gy- and 70 Gy-dose radiotherapy. Materials and methods: One hundred and ten maxillary incisors were endodontically prepared up to ProTaper Next X4 instruments. The teeth were randomly divided into 5 main groups as: non-irradiated, root canal treatment (RCT) before 60 Gy radiotherapy, RCT before 70 Gy radiotherapy, RCT after 60 Gy radiotherapy, RCT after 70 Gy radiotherapy. These groups were divided into 2 subgroups for filling material: AHP ve AHPB. After filling and radiotherapy procedures, the teeth were fixed on the thermoplastic mask plane. The plane were placed in the middle of a rectangular prism shaped glass phantom, and irradiated via a linear accelerator device. The teeth were then embedded in cylindrical acrylic blocks and the force (N) that caused the fracture was recorded under the Universal testing device. Student t-test was used for statistical comparisons. Statistical significance level was determined as p < 0.05. Results: After 70 Gy dose radiotherapy, the group filled with AHPB showed statistically significantly lower fracture strength than the group filled with AHP (p < 0.05). In the control group, before 60 Gy RT group, after 60 Gy RT group, and before 70 Gy RT group, the sealers had statistically significantly similar load-to-failure. (p > 0.05). Conclusion: The group filled with AHPB caused a lower fracture strength than the group filled with AHP following a 70 Gy dose of RT. The sealers in the control group, before 60 Gy RT group, after 60 Gy RT group, and before 70 Gy RT group exhibited comparable load-to-failure values. [ABSTRACT FROM AUTHOR]

This study aimed to investigate adhesive shear bond strength (SBS) on an ultrafine-grained niobium alloy (UFG-Nb) that is a potential dental implant material. SBS of three adhesive systems combined with three composites to UFG-Nb was compared to corresponding SBS to Ti-6Al-4V and to zirconia. Specimens of the substrates UFG-Nb, Ti-6Al-4V and zirconia with plane surfaces were sandblasted with Al2O3, cleaned and dried. Three adhesive systems (Futurabond U, Futurabond M + , Futurabond M + DCA; all VOCO GmbH, Cuxhaven, Germany) were applied each on specimens of each substrate and light cured. One composite (BifixSE, BifixQM, GrandioSO; all VOCO GmbH) was applied and light cured resulting in 27 groups (n = 10) for all substrate-adhesive-composite-combinations. SBS was measured after 24 h of storage. To simulate aging equally prepared specimens underwent 5000 thermocycles before SBS measurement. There was no significant difference in SBS within the non-aged groups. Among the artificially aged groups, GrandioSO-groups showed a greater variance of SBS than the other composites. All significant differences of corresponding UFG-Nb-, Ti-6Al-4V- and zirconia-groups with same adhesive-composite-combination (ACC) were observed between UFG-Nb and zirconia or Ti-6Al-4V and zirconia but never between the two metallic substrates. The similarity between these materials might show in their adhesive bonding behavior. As there were no differences comparing corresponding groups prior to and after artificial aging, it can be concluded that aging does not affect SBS to UFG-Nb, Ti-6Al-4V and zirconia using the tested ACCs. Adhesive bonding of established ACCs to UFG-Nb is possible resulting in SBS comparable to those on Ti-6Al-4V and zirconia surfaces. [ABSTRACT FROM AUTHOR]

Background: Vital pulp therapy (VPT) is recommended as an alternative treatment to root canal therapy (RCT) for management of teeth with carious pulp exposure. This randomized clinical trial aimed to compare the outcomes and postoperative pain, and to evaluate the time and cost after full pulpotomy (FP) and RCT in mature molar teeth with irreversible pulpitis (IP). Methods: A total of 160 mature molar teeth with IP were randomly divided into two treatment groups. The FP group (test group) was treated with FP using iRoot BP Plus by an endodontist, the RCT group (control group) was treated with RCT using iRoot SP as sealer by the same endodontist. Pain was recorded preoperatively and daily until day 7 postoperatively. The treatment time and cost were recorded. Clinical and radiographic assessments were collected, and pulp sensibility tests were done by electric pulp test (EPT) at 3-, 6-, 12- month postoperatively. Data were analyzed through chi-square test, Mann-Whitney U test, Fisher exact and independent t test. Results: FP and RCT had comparable success rates (Clinical, 97.3% vs. 98.6%; radiographic, 93.3% vs. 94.6%) (P > 0.05). Pain levels decreased over time from day 1 to day 7 postoperative in both groups, and the FP group had larger reductions in pain intensity than RCT at day 1 (P < 0.05). In the FP group, there were 5, 3 and 3 unresponsive teeth with EPT at 3-, 6- and 12- month follow-ups, respectively. The treatment time and cost in the FP group were significantly lower than in the RCT group (P < 0.05). Conclusions: FP could be an appropriate alternative treatment for management of mature teeth with IP in short follow-up. Trial registration: The trial was registered in Chinese Clinical Trial Registry (ChiCTR2200063380 at 05/09/2022). [ABSTRACT FROM AUTHOR]

Background: While the effect of biomaterials covering the pulp tissue is considered in the success of pulpotomy treatment, the level of pulpal inflammation is still very important for treatment success. The aim of this study was to compare IL-6 and IL-8 levels, known as good indicators of pulpal inflammation, with a new biomarker, presepsin, and to evaluate the impact of biomarker levels along with the pulp capping agents used in the treatment on the one-year success of pulpotomy treatment. Methods: The study included 120 primary second molar teeth with pulpotomy indications from 75 children. To determine the pulpal inflammation status, pulpal bleeding samples were taken during treatment, and the levels of IL-6, IL-8, and presepsin were measured. During the pulpotomy treatment, MTA, NeoMTA™, and Biodentine™, and ZOE were randomly applied to groups of thirty teeth each. Patients were monitored for a period of 12 months post-treatment. Results: IL-8, IL-6, and presepsin levels were significantly higher in teeth with pathology (p < 0.001). Biomarker levels were found to be higher in the NeoMTA and Biodentine groups, but this did not result in a statistically significant difference. (p > 0.05) Following pulpotomy treatment, the most successful material groups in order were MTA, ZOE, NeoMTA™, and Biodentine™. Conclusion: Presepsin may be a usable indicator in predicting the level of inflammation. At the end of the one-year follow-up of pulpotomy treatment, more pathology was observed in the NeoMTA and Biodentine groups, where biomarker levels were higher, while no pathology was found in the MTA group, where biomarker levels were lower. Trial registration: NCT06398327/ 20,240,503. [ABSTRACT FROM AUTHOR]

Background: The passive fit of 3-unit implant supported prefabricated metal screw-retained prosthesis before implant placement might be difficult. Hence, we aim to evaluate the passive fit and time efficiency of CAD/CAM 3-unit implant supported fixed prostheses that were constructed based on virtual versus those based on actual implant positions in Kennedy Class I models. Methods: A sample of 5 Kennedy class I models with thin wiry ridges were restored by 20 frameworks bilaterally, 10 based on actual (group A) and 10 based on virtual (group V) implant positions. The models were imaged using cone beam computed tomography and scanned using an intraoral scanner. The STL (Standard Tessellation Language files) and the DICOM (Digital Imaging and Communications in Medicine) files were registered on a 3D planning software. A CAD/CAM surgical guide was planned, resin printed and used for installing 6 implants bilaterally. In group V, the framework was designed based on the virtual scan bodies and virtual multi-unit abutments, while in group A intra-oral scanning of the model after attaching the scan bodies was necessary. Frameworks of both groups were milled and tested for passive fit using 8 clinical tests. McNemar and Wilcoxon signed rank tests were used to study the effect of the group on passive fit and time efficiency, respectively. The significance level was set at P ≤ 0.05. Results: No statistically significant difference was found between group V and group A frameworks regarding passive fit (p-value = 1, OR = 0.5) and time efficiency (P = 0.179, Effect size = 0.948). Conclusion: Within the limitations of this study, it can be concluded that in free end saddle cases, prefabricated CAD\CAM 3-unit implant-supported cobalt chromium screw retained prostheses can achieve an adequate passive fit. However, their fit might be negatively affected in thin ridges and they might require some adjustments. [ABSTRACT FROM AUTHOR]

Dental caries is the most widespread form of disease, affecting over 90% of the global population. Amalgam fillings, which have been in use for nearly two centuries, will face an European Union ban by 2025. Although photocomposite fillings are a suitable alternative, health concerns persist because of potential substance release into the oral cavity. This study aimed to evaluate the release of photoinitiator substances and monomers from dental materials into various solvents at different temperatures over 30 days. Cylindrical specimens of the composite resins were submerged in different extraction solutions and incubated at 37 and 50°C. The findings demonstrated that both the extraction solvent and extraction temperature significantly influenced the quantity of leachables (p < 0.05). Furthermore, most leachables were released within the initial days, although some monomers continued to elute for over 30 days. The estimated daily intake was calculated for the worst‐case scenario, confirming the biocompatibility of the composite fillings. The weight loss of dental materials ranged up to 3.5% after 30 days, regardless of the extraction conditions and dental material (p > 0.05). In conclusion, this study contributes to filling several research gaps in the field by addressing the biocompatibility of various dental materials through quantitative and qualitative analyses supported by statistical evaluation. [ABSTRACT FROM AUTHOR]

Water treeing and water droplets are observed within adhesive layers and on the hybridized surface after bonding sound dentin using single‐bottle etch‐and‐rinse adhesives, indicating permeability of the hybrid layer to water. The aim of this study was to assess the efficacy of dentin sealing by adhesives containing propolis by quantifying the area of water transudation from dentinal tubules after dentin hybridization. Brazilian red propolis was added to experimental adhesive and Single Bond (3M/ESPE) adhesive; experimental adhesive and Single Bond without propolis were used as controls. Under simulated pulp pressure, two layers of adhesive were applied to etched human dentin discs. Three minutes after light‐curing, the hybridized dentin surface was replicated, and epoxy resin replicas were created to obtain scanning electron microscope images. Data were evaluated using ANOVA and Tukey's test. Single Bond containing propolis significantly decreased water permeation through the hybrid layer compared with the control group. Three minutes after polymerization, the experimental adhesive without propolis had formed a permeable hybrid layer. The addition of Brazilian red propolis significantly reduced surface water on hybridized dentin in a concentration‐dependent manner. Two‐step etch‐and‐rinse adhesives containing propolis were effective in reducing water permeation through the hybridized dentin surface. [ABSTRACT FROM AUTHOR]

Objective: A hybrid manufacturing technique that combines selective laser melting (SLM) and computer numerical control (CNC) has been developed for the fabrication of implant-platform/framework interfaces (PFIs) for mandibular and maxillary full-arch implant-supported titanium frameworks. The aim of this study was to compare the discrepancies in specimens fabricated using the hybrid technique (termed SLM/m hereafter) with those in specimens fabricated by conventional CNC milling. Materials and methods: Based on a mandibular four-PFI CAD model and a maxillary six-PFI CAD model, four groups of titanium frameworks (eight per group, totaling 32) were fabricated according to the fabrication technique (SLM/m or milling) and number of PFIs (four or six). The frameworks were scanned by a structured light scanner and aligned with the CAD model in Geomagic Control X. Discrepancy was defined as the difference between the PFIs of the scanned framework and those of the CAD model. Discrepancies were measured and evaluated by multilevel analysis using a mixed-effects model (α = 0.05), followed by independent samples t-tests (α = 0.0125). Furthermore, the manufacturing times and raw-material costs were recorded and compared. Results: The maximum discrepancy values for the four-PFI and six-PFI hybrid frameworks were 52.2 and 64.3 μm, respectively. Multilevel analysis revealed that the fabrication technique and the number of PFIs had no significant effect on the discrepancy value. However, a significant interaction between the two factors was observed (P = 0.020). The discrepancies for the four-PFI hybrid frameworks were significantly lower than those for the four-PFI milled frameworks (P = 0.001). No significant difference in discrepancies between the six-PFI hybrid frameworks and six-PFI milled frameworks was observed (P = 0.697). Furthermore, the hybrid frameworks required only 11% of the raw materials and 25% of the milling time required for the conventionally milled frameworks. Conclusion: SLM/m hybrid frameworks are viable, accurate alternatives to CNC-milled frameworks, with the added benefit of substantial cost reduction. [ABSTRACT FROM AUTHOR]

Highlights In polymer‐based dental composites, wear is a three‐body wear system mainly abrasive, because of the food particles and wear products suspended in the oral cavity, which are transferred to the microcavities of the surface of the replacements. Due to this fact, the incorporation of nanodiamond as reinforcement in these polymer–matrix composites, which promotes the creation of a solid lubricant tribofilm surface could be advantageous. With the reinforcement of nanodiamonds, BisGMA/TEGDMA‐based composites increase their microhardness by 95%–420%. A maximum hardness exceeding 65 HV is achieved with a reinforcement of 3.2 wt%. The specific wear rate of neat BisGMA/TEGDMA is near 10−4 mm3/Nm and the Archard's coefficient is 2.6 × 105. The incorporation of a content of 1.6 wt% ND is enough to cause a diminution of ~78% in the friction coefficient and a reduction of the specific wear rate and Archard's coefficient of ~50%. Nevertheless, the addition of relatively high contents reduces the effectiveness of photoinitiation and photocuring, which is related to the scattering and absorption of light radiation by ND. This causes a significant decline in elastic properties starting at 50 μm from the surface. Photocuring polymer resin was successfully reinforced with nanodiamonds. Microhardness increases from 95% up to 420%, close to commercial composites. Friction coefficient and wear rate are reduced with 1.6 wt% nanodiamonds. High levels of reinforcement reduce the effectiveness of photocuring. [ABSTRACT FROM AUTHOR]

Background: Osseointegrated dental implants are widely established as a first-choice treatment for the replacement of missing teeth. Clinical outcomes are however often compromised by short or longer-term biological complications and pathologies. Nanoparticle-coated materials represent a very active research area with the potential to enhance clinical outcomes and reduce complications of implant therapy. This scoping review aimed to summarize current research on various types of nanoparticles (NPs) used as surface modifiers of dental implants and their potential to promote biological and clinical outcomes. Methods: A systematic electronic search was conducted in SCOPUS, PubMed and Google Scholar aiming to identify in vivo, in situ, or in vitro studies published between 2014 and 2024. Inclusion and exclusion criteria were determined and were described in the methods section. Results: A total of 169 articles (44 original papers from Scopus and PubMed, and 125 articles from Google Scholar) were identified by the electronic search. Finally, 30 studies fit the inclusion criteria and were further used in this review. The findings from the selected papers suggest that nanoparticle-coated dental implants show promising results in enhancing bone regeneration and promoting angiogenesis around the implant site. These effects are due to the unique physicochemical properties of nanoparticle-coated implants and the controlled release of bioactive molecules from nanoparticle-modified surfaces. Conclusion: Nanoscale modifications displayed unique properties which could significantly enhance the properties of dental implants and further accelerate revascularization, and osseointegration while facilitating early implant loading. Yet, since many of these findings were based on in-vitro/in-situ systems, further research is required before such technology reaches clinical application. [ABSTRACT FROM AUTHOR]

Background: This study evaluates the fracture strength and patterns of feldspathic porcelain restorations made using CAD/CAM technology for lower first molars with extensive crown destruction. The restorations include post-core and full-contour crown, composite resin core and full-contour crown, and endocrown. This research provides insights into effective restorative options to address tooth fracture risk, supporting minimally invasive procedures and CAD/CAM integration in dental practices. Methods: This study utilized 80 permanent mandibular first molars, which were divided into four groups: Group I (Post-Core-Full-contour crown), Group II (Core- Full-contour crown), Group III (Endocrown), and Group IV (Control). Root canal treatment was performed on all samples except for the control group. Following access cavity preparation, restorations for each tooth were fabricated using the CAD/CAM system and cemented with resin cement. The specimens were embedded in acrylic blocks. After undergoing thermomechanical aging, the samples were subjected to fracture resistance testing using a universal testing machine, which applied force until fracture occurred. The fracture patterns were subsequently analyzed, and the data were statistically evaluated using the Kruskal-Wallis and Chi-Square tests (p < 0.05). Results: A significant difference in fracture values under axial forces was observed (p < 0.05). The control group had the highest fracture strength (1830 ± 277 N), while the Core- full-contour crown group showed the lowest (1532 ± 371 N). Failure types varied significantly among the groups (χ2 = 26.886, df = 9, p = 0.001). The most common failure type was Type-2 (33.75%), characterized by restorable fractures, while Type-3 fractures, unrestorable, were the least common (12.5%). Conclusions: The findings underscore the significance of technological advancements in CAD/CAM for effectively restoring endodontically treated teeth with extensive crown damage. This study contributes valuable insights, emphasizing the clinical relevance of selecting appropriate restorative options to mitigate the risk of tooth fracture associated with coronal restoration failures. [ABSTRACT FROM AUTHOR]

Purpose: This study aimed to evaluate the accuracy of detecting vertical root fractures in Biodentine™-filled teeth using the Promax 3Dmax cone-beam computed tomography (CBCT) unit compared to periapical radiographs. It tested hypotheses regarding CBCT's diagnostic superiority in non-root-filled and Biodentine™-root-filled maxillary central incisors and assessed the impact of smaller field of view and lower intensity settings on detection accuracy. Materials and methods: Extracted maxillary incisors were divided into groups based on fracture status and root filling material, then placed in a Thiel-embalmed skull to simulate clinical conditions. The teeth were imaged using periapical radiographs and the CBCT unit under different settings. Fracture thickness was measured with microcomputed tomography for accuracy benchmarking. Multiple observers assessed the images, and statistical analyses were conducted to evaluate diagnostic performance. Results: Intra-rater reliabilities of consensus scores ranged from good to very good. Specificities were generally higher than sensitivities across all imaging modalities, but sensitivities remained constantly low. None of the Area Under the Curve scores exceeded 0.6, indicating poor overall accuracy for all imaging modalities. Paired comparisons of the area differences under Receiver Operator Characteristic curves revealed no significant differences between the CBCT and periapical radiograph techniques for detecting vertical root fractures in either Biodentine™-filled or non-root-filled teeth. Conclusions: There was no significant accuracy improvement of the current CBCT device (Promax 3Dmax, Planmeca, Finland) over periapical radiographs in detecting small vertical root fractures in both non-root-filled and Biodentine™-root-filled maxillary central incisors. A smaller field of view with lower intensity did not enhance detection accuracy. These results highlight the challenges in accurately detecting small VRFs, emphasizing the need for further research and technological advancements in this domain. [ABSTRACT FROM AUTHOR]

Objectives Optimum flexural strength and viscosity are essential for longevity while efficiently handling dental luting composite. This study aims to investigate the effects of zirconia and alumina on the flexural strength (FS)and viscosity of dental cement made of silica rice husk. Materials and Methods Study groups with different percentages of weight (wt.): Group 1 (3 wt.% zirconia), Group 2 (3 wt.% alumina), and Group 3 (3 wt.% zirconia and 2 wt.% alumina), negative control specimen (0 wt.% zirconia/alumina) and Rely-X U200 (3M ESPE). A universal testing machine and a rheometer were used to test FS and viscosity, respectively. One-way ANOVA and post-hoc Bonferonni test were used for data analyses. Results and Discussion FS and viscosity for Group 3 (3 wt.% zirconia and 2 wt.% alumina) were significantly higher compared to the negative control (p<0.05). Conclusion: Adding zirconia and alumina improved flexural strength without compromising the viscosity of dental luting composite. This experimental dental luting cement using hybrid fillers could be an alternative to resin luting cement. [ABSTRACT FROM AUTHOR]

This study aims to evaluate the adsorptive, adhesive, and wetting energetic properties of five commercially available cleansers in contact with model dental polymer (PMMA). It was assumed that the selected parameters allow for determining the optimal concentration and place of key component accumulation for antibacterial activity in the bulk liquid phase and prevention of oral plaque formation at the prosthetic material surface. The adsorptive (Gibbs' excesses ΓLV, critical micellar concentration) and thermal (entropy and enthalpy) surface characteristics originated from surface tension γLV(T) and γLV(C) dependences. The surface wetting properties were quantified upon the contact angle hysteresis formalism on the advancing ΘA, receding ΘR contact angles, and γLV as the input data, which yield a set of wettability parameters: 2D adsorptive film pressure, surface free energy with its dispersive and polar components, work of adhesion, and adhesional tension, considered as interfacial interaction indicators. In particular, molecular partitioning Kp and ΓLV are indicators of the efficiency of particular active substance accumulation in the volume phase, while γSV, a = ΓSL/ΓLV, and WA point to the degree of its accumulation at the immersed polymer surface. Finally, the liquid penetration coefficient PC and the Marangoni temperature gradient-driven liquid flow speed were estimated. [ABSTRACT FROM AUTHOR]

(1) Objectives: This study investigated and compared the wear and flexural strength of two highly filled (injectable), one flowable and one paste composite. (2) Methods: Two highly filled flowable composites (G-aenial Universal Injectable and Beautifil Plus F00), a paste composite (Empress Direct) and a conventional flowable (Tetric EvoFlow) were tested. A two-body wear test was carried out using 10 disc-shaped samples from each group, which were subjected to 200,000 wear machine cycles to simulate wear, followed by Scanning Electron Microscope analysis. Flexural strength was tested using a three-point bend test using 15 beam samples for each of the four groups. Values were statistically compared using one-way analysis of variance (ANOVA) for flexural strength and a Kruskal–Wallis test for wear. (3) Results: The median volume loss for G-aenial Universal Injectable and Beautifil Plus F00 was statistically lower than that of both Empress Direct and Tetric EvoFlow. For flexural strength the two highly filled flowable composites both exhibited statistically higher mean flexural strength values compared to Empress Direct (p < 0.004) and Tetric Evoflow (p < 0.001). There were no statistically significant differences in the values of wear and flexural strength between the two highly filled flowable composites. (4) Conclusions/significance: Highly filled flowable composite resins with nano filler particles outperformed a conventional flowable and a paste composite resin in terms of wear resistance and flexural strength, and may be suitable to use in occlusal, load-bearing areas. [ABSTRACT FROM AUTHOR]