Search

Nanolayered coatings are proposed for use in microelectronic devices where the size/performance ratio is becoming increasingly important, with the aim to achieve existing quality requirements while reducing the size of the devices and improving their ability to perform stably over multiple cycles. Si-SiO 2 -W structures have been proposed as a potential material for the fabrication of microelectronic devices. However, before such materials can be implemented in devices, their properties need to be carefully studied. In this study, Si-SiO 2 -W nanolayered structures were fabricated and subjected to numerous thermal treatment cycles at 150 °C. A total of 33 heating cycles were applied, resulting in a cumulative exposure of 264 h. The changes in chemical bonds and microstructure were monitored using Fourier Transform Infrared spectrometry (FTIR) and scanning electron microscopy (SEM). The FTIR signal at 960 cm -1 , indicating the presence of W deposited on SiO 2 , was selected to characterize the thermal stability during the heating cycles. The estimated signal intensity variation closely resembled the normal inhomogeneity of the nanolayers. The increase in slope intensity was estimated to be 1.7 × 10 -5 .

This study examines the electrical properties and layer quality of field emission microtriodes that have planar electrode geometry and are based on tungsten (W) and silicon dioxide (SiO 2 ). Two types of microtriodes were analyzed: one with a multi-tip cathode fabricated using photolithography (PL) and the other with a single-tip cathode fabricated using a focused ion beam (FIB). Atomic force microscopy (AFM) analysis revealed surface roughness of the W layer in the order of several nanometers (Ra = 3.8 ± 0.5 nm). The work function values of the Si substrate, SiO 2 layer, and W layer were estimated using low-energy ultraviolet photoelectron emission (PE) spectroscopy and were 4.71 eV, 4.85 eV, and 4.67 eV, respectively. The homogeneity of the W layer and the absence of oxygen and silicon impurities were confirmed via X-ray photoelectron spectroscopy (XPS). The PL microtriode and the FIB microtriode exhibited turn-on voltages of 110 V and 50 V, respectively, both demonstrating a field emission current of 0.4 nA. The FIB microtriode showed significantly improved field emission efficiency compared to the PL microtriode, attributed to a higher local electric field near the cathode.

The purpose of this study was to investigate the effect of Zn doped CaP coatings prepared by micro-arc oxidation method, as a possible approach to control MgCa1 alloy degradation. All the prepared coatings comprised a calcium deficient CaP phase. The control in this evaluation was performed with undoped CaP coating in SBF solution at body temperature (37 ± 0.5⁰C). The investigation involved determination of microchemical, mechanical, morphological, properties along with anticorrosive, cytocompatibility and antibacterial efficacy. The effect of sterilization process on the properties of the surfaces was also investigated. The results showed that the addition of Zn into CaP increased the corrosion resistance of MgCa1 alloy. Moreover, the adhesion strength of the coatings to MgCa1 alloy was enhanced by Zn addition. In cytotoxicity testing of the samples, extracts of the samples in MEM were incubated with L929 cells and malformation, degeneration and lysis of the cells were examined microscopically after 72 h. The results showed that all samples were cytocompatible. The degradation of MgCa1 alloy in the simulated body fluids (SBF) or DMEM was decreased by coating with CaP. Moreover, the degradation rate of CaP was further decreased by adding a small amount of Zn into the CaP matrix. The samples having CaP coatings and Zn doped CaP coating demonstrated antibacterial efficacy against E.coli. As a result, coating of magnesium alloy with Zn-doped CaP decreased the degradation rate, increased the corrosion resistance, cytocompatibility and the antibacterial effects of the alloys., Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2022 Elsevier B.V. All rights reserved.)

The ability of cells to adhere to substrates is an important factor for the effectiveness of biotechnologies and bioimplants. This research demonstrates that the statistical distribution of the sizes of the cells ( Saccharomyces cerevisiae ) attached to the substrate surface correlates with the statistical distribution of electrical potential on the substrate's surface. Hypothetically, this behavior should be taken into consideration during the processing of surfaces when cell adhesion based on cell size is required.

The paper deals with the evolution of the microstructure of AlSi10Mg alloy obtained by laser powder bed fusion (LPBF), as a function of the post-processing heat treatment temperature. This was approached by complementary methods including FE-scanning electron microscopy, scanning Kelvin probe force microscopy and exo-electron emission techniques. The fast cooling rate of the LPBF process as compared to traditional casting produces a very fine microstructure with high mechanical properties and corrosion resistance. However, the LPBF-AlSi10Mg alloy can be susceptible to selective corrosion at the edge of the melt pools generated by the laser scan tracks. Post-process thermal treatments of the Al alloy induce a marked modification of the silicon network at melt pool edges, in particular at high temperature such as 400 °C. It was found that this is associated to a more homogeneous distribution of Volta potential. Analysis of exo-electron emission confirms the silicon diffusion during thermal treatment. The modification of the silicon network structure of the LPBF-AlSi10Mg during thermal treatment reduces the susceptibility to selective corrosion.