Search

Biomass ash (BA) contains alkaline cations such as K, Ca, and Mg. Due to its high pH, direct application to the soil may result in soil salinization. Composting of BA with organic matter is an effective strategy, but the composting cycle is long and there is a large amount of insoluble residue in the product. Therefore, this research proposed for the first time using the hydrothermal method to rapidly convert BA and bamboo powder (BP) into water - soluble fertilizer (WSF) within 4 h. The insoluble hydrothermal residue was further converted into calcium - rich biochar phosphorus adsorption material by a simple pyrolysis process. WSF was neutral and contained humic acid and elements like K, Ca, Mg, and Si. A 14 - day wheat hydroponic experiment showed that the addition of 0.0125% WSF increased the fresh weight of wheat by 18.77% compared with deionized water. The calcium - based biochar adsorbent produced by pyrolysis had an ideal adsorption capacity of up to 113.6 mg P g -1 for phosphate in water, higher than many existing reports. The adsorption mechanisms mainly included surface precipitation, ion exchange, and electrostatic attraction. Moreover, the calcium - rich biochar sample slowly released phosphorus into water after adsorbing phosphate. When the pH was 3 or 4, the removal rate of Pb 2+ , Cd 2+ , and Cu 2+ at 15 - 20 mg L -1 was as high as 99%. This indicated its potential as a slow - release fertilizer and heavy metal remediation agent. This research provided a new way of thinking for the treatment and disposal of BA., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2024 Elsevier Inc. All rights reserved.)

The recovery of heavy metals from electroplating sludge is important for alleviating heavy metal pollution and recycling metal resources. However, the selective recovery of metal resources is limited by the complexity of electroplating sludge. Herein, CuFe bimetallic Fenton-like catalysts were successfully prepared from electroplating sludge by a facile room-temperature ultrasonic-assisted co-precipitation method. The prepared CuFe-S mainly consisted of nanorods with diameters of 20-30 nm and lengths of 100-200 nm and a small number of irregular particles. Subsequently, we performed tetracycline (TC) degradation experiments, and the results showed that the product CuFe-S had very good performance over a wide pH range (2-11). At an initial pH = 2, CuFe-S could degrade 91.9% of 50 mg L -1 TC aqueous solution within 30 min, which is better than that of a single metal catalyst. Free radical scavenging experiments and electron paramagnetic resonance (EPR) tests revealed that ·OH was the main active species for the degradation of TC by CuFe-S. In conclusion, a CuFe bimetallic Fenton-like catalyst was developed for the catalytic degradation of antibiotics, which provides a novel technical route for the resource utilization of electroplating sludge and shows an important practical application prospect., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2022 Elsevier Inc. All rights reserved.)