Search

Dysprosium (Dy)‐doped (Y1−xDyx)3Si2C2 (x = 0, 0.1, 0.3, 0.5) solid solution ceramics were successfully fabricated using an in situ reaction spark plasma sintering technology, for the first time. The effect of various Dy doping contents (x) on the microstructure, mechanical, and thermal properties of (Y1−xDyx)3Si2C2 ceramics was investigated. The (0 2 0) crystal plane spacing of (Y0.5Dy0.5)3Si2C2 was 7.813 Å, which was smaller than that of Y3Si2C2, due to the fact that the atomic radius of Dy is smaller than that of Y. The Dy doping facilitated the consolidation of (Y1−xDyx)3Si2C2, thus a highly dense (Y0.5Dy0.5)3Si2C2 ceramic material with a low open porosity of 0.14% was successfully obtained at a relatively low temperature of 1 200°C. As the content of Dy doping (x) increased from 0 to 0.5, the purity of (Y1−xDyx)3Si2C2 ceramics increased from 88.3 to 90.7 wt.%, while the grain size of (Y1−xDyx)3Si2C2 ceramics decreased from 0.59 to 0.46 µm. As a result, the Vickers hardness and thermal conductivity of the (Y0.5Dy0.5)3Si2C2 material was 7.1 GPa and 9.8 W·m−1·K−1, respectively. [ABSTRACT FROM AUTHOR]

The combined oil reservoir under the Yanchang Formation has been proven to have approximately 340 million tons of oil geological reserves, which is an important resource guarantee for Yanchang Oil to achieve the stable production target of 10 million tons. The development and research of oil reservoirs are in the initial stage, and there are many technical difficulties in the overall development, which seriously affect the sustained high and stable production of the lower combination reservoir. Therefore, nuclear magnetic resonance technology was used to conduct stress sensitivity testing on the pore structure of the Chang-8 reservoir in Fuxian County, Ordos Basin. It was recognized that large-diameter pores are easily compressed, but porosity accounts for a relatively small proportion, so the influence of confining pressure on permeability is greater.

A novel nano-laminated GdB2C2 material was successfully synthesized using GdH2, B4C, and C via an in situ solid-state reaction approach for the first time. The formation process of GdB2C2 was revealed based on the microstructure and phase evolution investigation. Purity of 96.4 wt.% GdB2C2 was obtained at a low temperature of 1500 °C, while a nearly fully pure GdB2C2 could be obtained at a temperature over 1700 °C. The as-obtained GdB2C2 presented excellent thermal stability at a high temperature of 2100 °C in Ar atmosphere due to the stable framework formed by the high-covalence four-member and eight-member B-C rings in GdB2C2. The GdB2C2 material synthesized at 1500 °C demonstrated a remarkably low minimum reflection loss (RLmin) of −47.01 dB (3.44 mm) and a broad effective absorption bandwidth (EAB) of 1.76 GHz. The possible electromagnetic wave absorption (EMWA) mechanism could be ascribed to the nano-laminated structure and appropriate electrical conductivity, which facilitated good impedance matching, remarkable conduction loss, and interfacial polarization, along with the reflection and scattering of electromagnetic waves at multiple interfaces. The GdB2C2, with excellent EMWA performance as well as remarkable ultra-high-temperature thermal stability, could be a promising candidate for the application of EMWA materials in extreme ultra-high temperatures. [ABSTRACT FROM AUTHOR]

Safe and efficient recycling of industrially generated machined chips is a high-priority technological issue. In this study, the effect of SiC particles (SiCp) on the microstructure and mechanical properties of SiCp/AZ91D composites is systematically analyzed, and the reinforcement mechanism of SiCp on composites is investigated. Different contents of SiCp/AZ91D composites are fabricated by solid-state synthesis. The results show that the incorporation of SiCp refined the grains of SiCp/AZ91D composites, which is related to the uniform distribution of SiCp at the grain boundaries. The strong bonding of SiCp with the AZ91D matrix inhibited the generation and extension of cracks, which led to the simultaneous increase in the yield strength (YS) and elongation (EL) of the SiCp/AZ91D composites. The mechanical properties of the 3 wt.% SiCp/AZ91D composites are the most superior, with an average grain size, Vickers hardness, ultimate tensile strength (UTS), YS, and EL of 6.69 ± 4.48 μm, 89.5 ± 2.5 HV, 341 ± 11 MPa, 172 ± 8 MPa, and 4.43 ± 0.18%, respectively. The reinforcement mechanisms of SiCp/AZ91D composites are mainly grain refinement and dislocation strengthening. Solid-state synthesis is an effective method for recycling magnesium alloy chips. [ABSTRACT FROM AUTHOR]

Anodic oxide films were prepared by anodic oxidation on the surface of ADC12 aluminum alloy and their corrosion properties were explored. The original samples, anodized samples, and sealed samples were placed in the salt spray corrosion chamber and were taken out at different times. Then the corrosion resistance of the ADC12 aluminum alloy was discussed, and the electrochemical corrosion test was researched. The results indicated that the surface of the original samples reveals many large-area pits after salt spray corrosion, while the sealed samples present a smoother surface. The dense oxide films on the surface of the base metals effectively prevent Cl − entering into aluminum alloys especially after sealing. Electrochemical tests including the potential polarization curve and electrochemical impedance spectroscopy (EIS) as functions of exposure time were employed to reveal the corrosion behavior of surface layers. After the sealing treatment on the oxide films, the corrosion potential moved in the positive direction, the corrosion current density decreased, and the corrosion resistance of the ADC12 aluminum alloy was significantly improved. [ABSTRACT FROM AUTHOR]