Search

A rework of electronic assemblies and the reuse of electronic components are the most effective ways to reduce electronic waste. Since neither components nor substrates were developed with the intention of multiple usage, the question of how the integrity of lead-free solder joints is affected by multiple reflow operations is crucial for the implementation of any reuse strategy. Therefore, various types of 1206 multilayer ceramic capacitors (MLCCs) differing in their capacitance value and dielectric type (X5R, X7R, Y5V, NP0) were soldered on test printed circuit boards (PCBs) having a pure Cu-metallization surface in order to investigate the intermetallic reactions during multiple reflows. The metallization system on the MLCC-component side consisted of a thick film of Ni covered by galvanic-deposited Sn. The reflow experiments were conducted using a hypoeutectic SnAgCu solder. The results show the formation of a Cu6Sn5 intermetallic phase on both metallizations, which grows homogeneously with the number of reflows. Moreover, an ongoing decomposition of the solder into Ag-enriched and depleted zones was observed. The effect of these microstructural changes on the functionality of the solder joint was investigated by mechanical shear experiments and electrical four-point capacitance measurements. [ABSTRACT FROM AUTHOR]

A rework of electronic assemblies and the reuse of electronic components are the most effective ways to reduce electronic waste. Since neither components nor substrates were developed with the intention of multiple usage, the question of how the integrity of lead-free solder joints is affected by multiple reflow operations is crucial for the implementation of any reuse strategy. Therefore, various types of 1206 multilayer ceramic capacitors (MLCCs) differing in their capacitance value and dielectric type (X5R, X7R, Y5V, NP0) were soldered on test printed circuit boards (PCBs) having a pure Cu-metallization surface in order to investigate the intermetallic reactions during multiple reflows. The metallization system on the MLCC-component side consisted of a thick film of Ni covered by galvanic-deposited Sn. The reflow experiments were conducted using a hypoeutectic SnAgCu solder. The results show the formation of a Cu6Sn5 intermetallic phase on both metallizations, which grows homogeneously with the number of reflows. Moreover, an ongoing decomposition of the solder into Ag-enriched and depleted zones was observed. The effect of these microstructural changes on the functionality of the solder joint was investigated by mechanical shear experiments and electrical four-point capacitance measurements.

The formation of high-melting-point Cu6Sn5 interconnections is crucial to overcome the collapse of Sn-based micro-bumps and to produce reliable intermetallic interconnections in three-dimensional (3D) packages. However, because of multiple reflows in 3D package manufacturing, Cu6Sn5 interconnections will experience cyclic polymorphic transitions in the solid state. The repeated and abrupt changes in the Cu6Sn5 lattice due to the cyclic polymorphic transitions can cause extreme strain oscillations, producing damage at the surface and in the interior of the Cu6Sn5 matrix. Moreover, because of the polymorphic transition-induced grain splitting and superstructure phase formation, the reliability of Cu6Sn5 interconnections will thus face great challenges in 3D packages. In addition, the Cu6Sn5 polymorphic transition is structure-dependent, and the η′↔η polymorphic transition will occur at the surface while the η′↔ηs↔η polymorphic transition will occur in the deep matrix. This study can provide in-depth understanding of the structural evolution and damage mechanism of Cu6Sn5 interconnections in real 3D package manufacturing. [ABSTRACT FROM AUTHOR]