Search

In this study, textile fiber prototypes based on polyester and different Cu nanoparticles (CuNP) content were produced using melt-spinning to obtain bi-component multifilament fibers and melt-blowing to obtain non-woven fabrics. The prototypes were tested against pathogenic microorganisms such as S. aureus, E. coli, and C. albicans. It was shown that bi-component fibers offer excellent protection against pathogens, with up to 99% growth inhibition with 0.5% w/w for S. aureus and E. coli; meanwhile, non-woven fabric only shows activity against E. coli from 0.1% w/w of CuNP. Using different analytical techniques, it was possible to identify that the CuNP were confined exclusively in the outer cover of the bi-component fibers which may be associated with increased antimicrobial activity compared to the fibers in the non-woven fabric. The use of polymeric nanocomposites based on polyester/copper offers an alternative of great interest due to the versatility of the raw material and the high efficiency of copper nanoparticles as an antimicrobial additive. [ABSTRACT FROM AUTHOR]

Maleic anhydride-grafted polypropylene (PP-g-MA) was reacted with aniline (NH2C6H5) to produce PP-g-NHC6H5 and used as a compatibilizer in polypropylene/carbon nanotube composites. Infrared spectroscopy (FTIR) and nuclear magnetic resonance confirmed the reaction between PP-g-MA and aniline. PP-g-NHC6H5 resulted a better compatibilizer than PP-g-MA, producing good dispersion and homogeneous distribution of the carbon nanotubes with less agglomerates, as observed by SEM analysis. Improved dispersion and distribution is assumed to be due to the π-π interactions between the -C6H5 ring in the prepared compatibilizer and the hexagonal carbon structure in the nanotubes. In addition, a higher degree of crystallinity (12%) was promoted, since it was favored by π-π interactions. This achieved higher crystallinity promoted an increase in tensile modulus, with only slight changes in tensile strength but with an adverse effect on elongation at break. [ABSTRACT FROM AUTHOR]

Metamaterial behavior of polymer nanocomposites (NCs) based on isotactic polypropylene (iPP) and multi-walled carbon nanotubes (MWCNTs) was investigated based on the observation of a negative dielectric constant (ε'). It is demonstrated that as the dielectric constant switches from negative to positive, the plasma frequency (!p) depends strongly on the ultrasound-assisted fabrication method, as well as on the melt flow index of the iPP. NCs were fabricated using ultrasound-assisted extrusion methods with 10 wt % loadings of MWCNTs in iPPs with different melt flow indices (MFI). AC electrical conductivity (σ(AC)) as a function of frequency was determined to complement the electrical classification of the NCs, which were previously designated as insulating (I), static-dissipative (SD), and conductive (C) materials. It was found that the SD and C materials can also be classified as metamaterials (M). This type of behavior emerges from the negative dielectric constant observed at low frequencies although, at certain frequencies, the dielectric constant becomes positive. Our method of fabrication allows for the preparation of metamaterials with tunable !p. iPP pure samples show only positive dielectric constants. Electrical conductivity increases in all cases with the addition of MWCNTs with the largest increases observed for samples with the highest MFI. A relationship between MFI and the fabrication method, with respect to electrical properties, is reported. [ABSTRACT FROM AUTHOR]

Isotactic polypropylenes (iPP) with different melt flow indexes (MFI) were used tofabricate nanocomposites (NCs) with 10 wt % loadings of multi-wall carbon nanotubes (MWCNTs) using ultrasound-assisted extrusion methods to determine their effect on the morphology, melt flow, and electrical properties of the NCs. Three different types of iPPs were used with MFIs of 2.5, 34 and 1200 g/10 min. Four different NC fabrication methods based on melt extrusion were used. In the first method melt extrusion fabrication without ultrasound assistance was used. In the second and third methods, an ultrasound probe attached to a hot chamber located at the exit of the die was used to subject the sample tofixed frequency and variable frequency, respectively. The fourth method is similar to the first method, with the difference being that the carbon nanotubes were treated in a fluidized air-bed with an ultrasound probe before being used in the fabrication of the NCs with no ultrasound assistance during extrusion. The samples were characterized by MFI, Optical microscopy (OM), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), electrical surface resistivity, and electric charge. MFI decreases in all cases with addition of MWCNTs with the largest decrease observed for samples with the highest MFI. The surface resistivity, which ranged from 1013 to 105 W/sq, and electric charge, were observed to depend on the ultrasound-assisted fabrication method as well as on the melt flow index of the iPP. A relationship between agglomerate size and area ratio with electric charge was found. Several trends in the overall data were identified and are discussed in terms of MFI and the different fabrication methods. [ABSTRACT FROM AUTHOR]

ABSTRACT The effect of multiwall carbon nanotubes (MWNT) concentration and cooling rate on the morphological, structural and electrical properties of non-isothermally crystallized Poly(ethylene naphthalate) nanocomposites (PEN/MWNT) was studied. PEN/MWNT nanocomposites containing 1 and 2 wt % of nanotubes were prepared by melt blending in a mini twin screw extruder. Nanocomposite samples with different degree of crystallinity ( Xc) were obtained via non-isothermally crystallization at cooling rates of 2, 10, 20, and 300°C min−1. In this study it was demonstrated that carbon nanotubes and cooling rate strongly influence morphological and structural characteristics of PEN. Calorimetric results showed that the peak crystallization temperature ( Tc) of PEN nanocomposites was increased ∼9° through heterogeneous nucleation with respect to pure PEN. X-ray diffraction revealed that carbon nanotubes modify the crystalline structure of PEN favoring the formation of β-crystals, and this effect increases with the nanotubes content. On the basis of X-ray scattering analysis, the variation of lamellar thickness revealed that nanotubes promote the formation of lamellar crystals with average thickness of 20 nm at different cooling rates. These structural and morphological changes play an important role on the electrical properties of nanocomposites. It was found that higher concentration of nanotubes and crystallinity promotes electrical conductivity of nanocomposites in the order of semiconductors (until 1 × 10−4 S cm−1) as well as permittivity of 20 at different tested frequencies. This may due to the interconnected networks of nanotubes throughout the crystalline structure formed in PEN nanocomposites. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 41765. [ABSTRACT FROM AUTHOR]

Ultrasound-assisted melt-extrusion method (USME) is a high-quality process used to produce polymeric compounds with an adequate homogeneous dispersion. This study evaluates white-color films of linear low-density polyethylene (LLDPE) prepared using TiO 2 masterbatch obtained by ultrasound-assisted melt-extrusion at variable frequencies (USME-VF). LLDPE with three different melt-flow indices (2, 20 and 50 g/10 min) were used as the polymer matrix. The films were obtained from the dilution of masterbatches of LLDPE (melt-flow index = 2) at a concentration of 7 wt% TiO 2 . The morphology, pigmentation, TiO 2 reactivity, and the mechanical stability of the films were assessed. The masterbatch compounds were evaluated by melt-flow index (MFI) and scanning electron microscopy (SEM). The contrast ratio, yellowness index and mechanical properties of films were also measured. The properties of whiteness and elongation at break improved in the films prepared using masterbatches with higher dispersion. Though the reactivity of the TiO 2 particles increased during accelerated aging, it did not affect the elongation to rupture. The yellowness index was moderately affected in films that included TiO 2 particles processed using USME-VF.