Search

One of the most revolutionary aspects of Laser Powder Bed Fusion (LPBF) is to be able to lift the design constraints from conventional manufacturing. However, as a rule of thumb, any surfaces lower than 45° with respect to the horizontal plane would still require sacrificial supports in order to complete the printing. Fundamentally, it is unclear whether it is feasible to print a 1st layer 0° overhang nor how the print parameters for the 1st layer can be optimised. This research demonstrates that large 1st layer 0° overhangs can be printed with a coverage above 90%. For the first time, the parameter space of laser power, scan speed and hatch spacing for the 1st layer has been simultaneously explored efficiently. The use of the rate of change of the mushy zone is proposed for the parameter selection instead of the average melt pool temperature. Adaptive Parameter 28 (AP28: 250W_4000 mm/s_50 µm) is the best choice. Several surface morphological phenomena are discussed. The core parameter (285W_960 mm/s_110 µm) causes severe balling and its mechanism is revealed. The average melt pool temperature of the 1st layer by the core parameter is lower than that of the bulk. The ramifications beyond the 1st layer are also illustrated.

This work investigates the viability of fabricating Ti-3Al-8V-6Cr-4Mo-4Zr (Beta-CTM) using laser-based and powder-fed directed energy deposition. To determine an appropriate ageing strategy, heat treatments were conducted at 440 °C and 480 °C over different periods of time and their effectiveness were determined through hardness testing. After identifying an optimal ageing treatment, tensile properties were investigated on the samples in the as-built and aged conditions. The microstructure, hardness and tensile properties of the as-built sample was found to resemble that of a conventionally-manufactured and solution-treated alloy. However, as compared to conventionally-manufactured Ti-3Al-8V-6Cr-4Mo-4Zr subjected to the same ageing temperature, the ageing process was much quicker with the DED-processed alloy because of its high dislocation density. Furthermore, the latter can also achieve much higher strength while also having comparable ductility. To achieve a similar ageing response and tensile behavior, conventionally-manufactured Ti-3Al-8V-6Cr-4Mo-4Zr would require cold-working prior to ageing. Carbon additions were also investigated to further accelerate the ageing response and to refine the β grain size. While the ageing response was much quicker and a much harder alloy can be produced, the carbon amount added was insufficient for β grain refinement, which resulted in reduced ductility without a change in strength.

One of the most revolutionary aspects of Laser Powder Bed Fusion (LPBF) is to be able to lift the design constraints from conventional manufacturing. However, as a rule of thumb, any surfaces lower than 45° with respect to the horizontal plane would still require sacrificial supports in order to complete the printing. Fundamentally, it is unclear whether it is feasible to print a 1st layer 0° overhang nor how the print parameters for the 1st layer can be optimised. This research demonstrates that large 1st layer 0° overhangs can be printed with a coverage above 90%. For the first time, the parameter space of laser power, scan speed and hatch spacing for the 1st layer has been simultaneously explored efficiently. The use of the rate of change of the mushy zone is proposed for the parameter selection instead of the average melt pool temperature. Adaptive Parameter 28 (AP28: 250W_4000 mm/s_50 µm) is the best choice. Several surface morphological phenomena are discussed. The core parameter (285W_960 mm/s_110 µm) causes severe balling and its mechanism is revealed. The average melt pool temperature of the 1st layer by the core parameter is lower than that of the bulk. The ramifications beyond the 1st layer are also illustrated. [ABSTRACT FROM AUTHOR]