Search

There is a high iron content in nickel slag that mainly exists in the fayalite phase. Basic oxide can destroy the stable structure of fayalite which is beneficial to the treatment and comprehensive utilization of nickel slag. The research was based on the composition of the raw nickel slag, taking the CaO-SiO2-FeO-MgO system as the object and CaO as a modifier. The effect of basicity on the melting characteristics, viscosity and structure of the CaO-SiO2-FeO-MgO system was studied. The relationship between the viscosity and structure of the CaO-SiO2-FeO-MgO system was also explored. The results show as follows: (1) When the basicity is lower than 0.90, the primary phase of the slag system is olivine phase. When the basicity is greater than 0.90, the primary phase of the slag system transforms into monoxide. When the basicity is 0.90, olivine and monoxide precipitate together as the temperature continues to decrease. At the same time, the liquidus temperature, softening temperature, hemispherical temperature, and flow temperature all reach the lowest value. (2) With the increase of basicity, the critical viscosity temperature of the CaO-SiO2-FeO-MgO system decreases first and then increases. Critical viscosity temperature is the lowest at the basicity of 0.90, which is 1295 &deg, C. (3) When the slag system is heterogeneous, the viscosity of the molten slag increases rapidly because of the quantity of solid phase precipitated from the CaO-SiO2-FeO-MgO system. (4) When the slag system is in a homogeneous liquid phase, the molar fraction of O0 decreases with the increase of basicity and the mole fraction of O&minus, and O2&minus, increases continuously at the basicity of 0.38~1.50. The silicate network structure is gradually depolymerized into simple monomers, resulting in the degree of polymerization, and the viscosity, being reduced. The mole fraction of different kinds of oxygen atoms is converged to a constant value when the basicity is above 1.20.

There is a high iron content in the nickel slag that mainly exists in fayalite phase. Basic Oxide can destroy the stable structure of fayalite which is beneficial to the treatment and comprehensive utilization of nickel slag. The reseach was based on the composition of the raw nickel slag, taking CaO-SiO2-FeO-MgO system as the object and CaO as a modifier. The effect of basicity on the melting characteristics, viscosity and structure of CaO-SiO2-FeO-MgO system was studied. The relationship between the viscosity and structure of CaO-SiO2-FeO-MgO system was also explored. The results show as follows. (1) When the basicity is 0.38~0.90, the phase of primary crystal is olivine at argon atmosphere, while it is monoxide at the basicity of 0.90~1.50. The liquidus temperature, softening temperature, hemispherical temperature, and flow temperature all reach the lowest value at the basicity of 0.90. (2) With the increase of basicity, critical viscosity temperature of CaO-SiO2-FeO-MgO system decreases first and then increases. Critical viscosity temperature is the lowest at the basicity of 0.90, which is 1263 ℃. (3) When the slag system is heterogeneous, the viscosity of the molten slag increase rapidity because of the type and quantity of solid phase precipitated from CaO-SiO2-FeO-MgO system. And critical viscosity temperature of the slag system is also significantly affected. (4) When the slag system is in a homogeneous liquid phase, the molar fraction of O0 decreases with the increase of basicity and the mole fraction of O- and O2- increases continuously at the basicity of 0.38~1.50. The silicate network structure is gradually depolymerized into simple monomers, resulting in the degree of polymerization is reduced and the viscosity is reduced, too.

The utilization of nickel slag has attracted much attention due to its high-content of valuable elements. As a part of these efforts, this work focuses on whether magnetite crystals, obtained from nickel slag via molten oxidation, magnetic separation, and ball-milling can be used as a microwave absorber. The composition, morphology, microstructure, magnetic properties, and microwave absorption performance were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM), and vector network analysis (VNA). The results reveal that the magnetite crystals exhibit excellent microwave absorption properties because of the synergistic action between dielectric loss and magnetic loss. The minimum reflection loss (RL) of the particles obtained after 6 h ball-milling reaches &minus, 34.0 dB at 16.72 GHz with thickness of 5 mm. The effective frequency bandwidth (RL &le, &minus, 10 dB) is 4.8&ndash, 5.4 GHz and 15.9&ndash, 17.6 GHz. Interfacial polarization of the particles could play a crucial role in improving absorbing properties because several components contained in the particles can dissipate electromagnetic wave effectively. The current study could show great potential in the preparation of magnetite crystals and utilization of nickel slag.