Presents a study which investigated the deposition of in situ boron-doped polycrystalline silicon-germanium films grown at low temperatures. Use of an ultrahigh-vacuum/chemical-vapor deposition system in the study; Description of the system; Experimental details.

The aim of this study was to investigate the effect of incorporating low copper (0, 0.5, 1, 1.5, and 2 wt.%) additions into as-forged AISI 304 stainless steel (304SS). The microstructures and mechanical properties of the steel were examined using scanning electron microscopy and a universal testing machine. The antibacterial properties of the Cu-bearing 304SS specimens were investigated using Escherichia coli. Each specimen was soaked in artificial saliva to detect the release of copper ions through inductively coupled plasma atomic emission spectrometry. The addition of copper had no significant effect on the microstructure of the as-forged Cu-bearing 304SS, but it slightly increased its maximum tensile strength. The antibacterial rate of the as-cast and as-forged 304SS with 2 wt.% Cu was over 80%, which corresponded to an increase in the release of copper ions. This study demonstrates that low-Cu-content stainless steel can reduce bacteria and can be a suitable material for the oral environment because of the low release of Cu ions. [ABSTRACT FROM AUTHOR]

The effects of the addition of silver on the microstructural variation and antibacterial performance of 2205 duplex stainless steel after solution and aging treatment were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM, and antibacterial testing. The microstructure showed that 2205Ag is composed of a ferrite (α) + austenite (γ) duplex phase and Ag-rich nano-precipitates (Ag-NPs). The morphology of the Ag-NPs varied from spherical to polygonal after aging treatment at 450 °C for 4 h. These precipitates were identified as face-centered-cubic structures with a lattice parameter of a = 0.354 nm and a mismatch of δ = 0.84% relative to the austenite matrix. Notably, 2205Ag with polygonal Ag-NPs exhibited excellent antibacterial properties that were superior to those of 2205Ag with spherical Ag-NPs. [ABSTRACT FROM AUTHOR]

In this study, the effects of spinodal decomposition on the microstructures and mechanical properties of a TiZrNbTa alloy are investigated. The as-cast TiZrNbTa alloy possesses dual phases of TiZr-rich inter-dendrite (ID) and NbTa-rich dendrite (DR) domains, both of which have a body-centered cubic (BCC) structure. In the DRs of the as-cast alloy, the α and ω precipitates are found to be uniformly distributed. After homogenization at 1100 °C for 24 h followed by water quenching, spinodal decomposition occurs and an interconnected structure with a wavelength of 20 nm is formed. The α and ω precipitates remained in the structure. Such a fine spinodal structure strengthens the alloy effectively. Detailed strengthening calculations were conducted in order to estimate the strengthening contributions from the α and ω precipitates, as well as the spinodal decomposition microstructure. [ABSTRACT FROM AUTHOR]