CoCrFeMnNi-XZrO2 (X is a mass percentage, X = 1, 3, 5, and 10) high-entropy alloy composite coatings were successfully prepared on 0Cr13Ni5Mo martensitic stainless steel substrates using laser cladding technology. The phase composition, microstructure, mechanical properties, and cavitation erosion behavior of the composite coatings under different contents of ZrO2 were studied. The mechanism of ZrO2 particle-reinforced cavitation corrosion resistance was studied using ABAQUS2023 finite element software. The results show that the phase structure of the composite coating organization is composed of FCC phase reinforced by ZrO2 phase. The addition of ZrO2 causes lattice distortion. The coatings have typical branch crystals and an equiaxed crystal microstructure. With the increase in ZrO2 content, the microhardness of the composite coatings gradually increases. When X = 10%, the coating's microhardness reached 348 HV, which was 95.53% higher than the high-entropy alloys without ZrO2 added. Adding ZrO2 can prolong the incubation period of high-entropy alloys; the high-entropy alloy composite coating with 5 wt.% ZrO2 exhibited the best cavitation resistance, with a cumulative volume loss rate of only 15.74% of the substrate after 10 h of ultrasonic cavitation erosion. The simulation results indicate that ZrO2 can withstand higher stress and deformation in cavitation erosion, reduce the degree of substrate damage, and generate higher compressive stress on the coating surface to cope with cavitation erosion. [ABSTRACT FROM AUTHOR]

The restoration of large support rollers poses an industrial challenge due to the high energy consumption of traditional repair methods. Consequently, a novel approach for repairing support rollers has been introduced and tested on thick-walled components. Finite element simulations aided the study of welding repairs for large thick-walled components, examining element distribution, microstructure, mechanical properties, and residual stress distribution across various processes. The results indicate that employing ABAQUS2023 finite element software to analyze stress variations under different working conditions, the Dynamically Controlled Low-Stress No-Distortion method effectively mitigates residual stresses both during and post welding, reducing average transverse residual stresses by 14.5% and average longitudinal residual stresses in the weld zone by 29.1%. The Dynamically Controlled Low-Stress No-Distortion method narrows the high-temperature range of the heat source, consequently decreasing the size of the heat-affected zone by 33.3% compared to conventional welding. The microstructure featured dendrites and equiaxed columnar crystals, with the Dynamically Controlled Low-Stress No-Distortion method capable of grain refinement, transforming some equiaxed columnar crystals into cellular structures. As grains were refined, microhardness improved, with the covering layer's microhardness rising by 14.68%. A comparison between simulated and measured values of lateral and longitudinal residual stresses at corresponding points revealed discrepancies of 14.6% and 20.5% in accuracy, respectively. [ABSTRACT FROM AUTHOR]