Nb2O5 is a Li+ intercalation metal oxide that is of current interest for lithium ion battery electrodes. The electrophoretic deposition (ED) of Nb2O5 thin-films from aqueous, NbOx colloidal solutions is reported here. For films ranging in thickness from 38 to 144 nm, the mass loading of Nb2O5 on the electrode is correlated with the coulometry of ED using quartz crystal microbalance gravimetry. Crystalline, phase pure films of orthorhombic, T-Nb2O5, are obtained by postdeposition calcination. These films exhibit unusually high specific capacities for Li+-based energy storage as a consequence of ≈70% porosity. For example, a 60 nm thick film displays a specific capacity, Csp, of 420 mAh/g at 5 A/g and 220 mAh/g at 50 A/g, which can be compared with the theoretical Faradaic capacity of 202 mAh/g. T-Nb2O5 films also have a specific energy density in the range from 770-486 Wh/kg, and a specific power density in the range from 9 to 90 kW/kg. These excellent energy storage metrics are attributed to augmentation of the Faradaic capacity by high double-layer capacities enabled by the mesoporous structure of these films.

The influence of hexamethylenetetraamine (HMTA) on the morphology of δ-MnO2 and its properties for electrical energy storage are investigated, specifically for ultrathick δ-MnO2 layers in the micron scale. Planar arrays of gold@δ-MnO2, core@shell nanowires, were prepared by electrodeposition with and without the HMTA and their electrochemical properties were evaluated. HMTA alters the MnO2 in three ways: First, it creates a more open morphology for the MnO2 coating, characterized by "petals" with a thickness of 6 to 9 nm, rather than much thinner δ-MnO2 sheets seen in the absence of HMTA. Second, the electronic conductivity of the δ-MnO2 is increased by an order of magnitude. Third, δ-MnO2 prepared in HMTA shows a (001) interlayer spacing that is expanded by ≈30% possibly accelerating Li transport. The net effect of "HTMA doping" is to dramatically improve high rate performance, culminating in an increase in the specific capacity for the thickest MnO2 shells examined here by a factor of 15 at 100 mV/s. [ABSTRACT FROM AUTHOR]

The influence of hexamethylenetetraamine (HMTA) on the morphology of δ-MnO 2 and its properties for electrical energy storage are investigated-specifically for ultrathick δ-MnO 2 layers in the micron scale. Planar arrays of gold@δ-MnO 2 , core@shell nanowires, were prepared by electrodeposition with and without the HMTA and their electrochemical properties were evaluated. HMTA alters the MnO 2 in three ways: First, it creates a more open morphology for the MnO 2 coating, characterized by "petals" with a thickness of 6 to 9 nm, rather than much thinner δ-MnO 2 sheets seen in the absence of HMTA. Second, the electronic conductivity of the δ-MnO 2 is increased by an order of magnitude. Third, δ-MnO 2 prepared in HMTA shows a (001) interlayer spacing that is expanded by ≈30% possibly accelerating Li transport. The net effect of "HTMA doping" is to dramatically improve high rate performance, culminating in an increase in the specific capacity for the thickest MnO 2 shells examined here by a factor of 15 at 100 mV/s.