Search

Purpose: To investigate the effect of adhesive type and long-term aging on the shear bond strength (SBS) between silicabased ceramics and composite cement (CC). Materials and Methods: Lithium-silicate (LS), feldspathic (FD) and polymer-infiltrated ceramic (PIC) blocks were sectioned (10 x 12 x 2 mm) and divided into 24 groups considering the factors: "ceramics" (LS, FD, and PIC), "adhesive" (Ctrl: without adhesive; 2SC: 2-step conventional; 3SC: 3-step conventional; 1SU: 1-step universal), and "aging" (non-aged or aged [A]). After the surface treatments, CC cylinders (n = 15, ɸ=2mm; height = 2mm) were made and half of the samples were subjected to thermocycling (10,000) and stored in water at 37°C for 18months. The samples were submitted to SBS testing (100 kgf, 1mm/min) and failure analysis. Extra samples were prepared for microscopic analysis of the adhesive interface. SBS (MPa) data was analyzed by 3-way ANOVA and Tukey's test (5%). Weibull analysis was performed on the SBS data. Results: All factors and interactions were significant for SBS (p<0.05). Before aging, there was no significant difference between the tested groups and the respective control groups. After aging, the LS_1SU (22.18±7.74) and LS_2SC (17.32±5.86) groups exhibited significantly lower SBS than did the LS_Ctrl (30.30±6.11). Only the LS_1SU group showed a significant decrease in SBS after aging vs without aging. The LS_1SU (12.20) group showed the highest Weibull modulus, which was significantly higher than LS_2SC_A (2.82) and LS_1SU_A (3.15) groups. Conclusion: No type of adhesive applied after silane benefitted the long-term adhesion of silica-based ceramics to CC in comparison to the groups without adhesive. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the biaxial flexural strength of different porcelain-to-zirconia thickness ratios and bonding strategies of a stress-free bilayer CAD/CAM ceramic system.Materials and Methods: A total of 60 zirconia discs (diameter: 15 mm; thickness: 0.3 or 0.5 mm; n = 30 for each thickness) were divided into six groups (n = 10 each) according to porcelain-to-zirconia ratio and bonding strategy: VM/Zr (control): zirconia discs veneered with a feldspathic ceramic (VM 9, Vita) in 0.9-mm and 0.7-mm thicknesses using a conventional hand-layering technique; VB/Zr-SBU: zirconia discs airborne particle-abraded with 50-μm Al2O3 particles followed by an MDP primer application (Single Bond Universal, 3M) and bonded to the porcelain with a resin cement (Panavia F 2.0, Kuraray); and VB/Zr-RC: zirconia discs airborne particle-abraded with 30-μm silica-coated Al2O3 particles and silanized and bonded to the porcelain with the same resin cement. Before cementation, the VB (Vitablocs II) discs were etched with 5% hydrofluoric acid (60 seconds), followed by silane application. The bilayers (thickness = 1.2 mm) were loaded with 750 g while light curing the resin cement. Two porcelain-to-zirconia thickness ratios were evaluated: 0.9: 0.3 mm and 0.7: 0.5 mm. All groups were subjected to 106 mechanical cycles, followed by a biaxial flexural test. Data (MPa) were subjected to two-way analysis of variance (ANOVA), Tukey test (5%), and Weibull analyses.Results: Two-way ANOVA revealed that the factor porcelain-to-zirconia ratio (P = .0556) was not significant; however, the bonding strategy factor was statistically significant. Among the 0.5-mm zirconia groups, the VB/Zr-SBU group presented higher flexural strength (s) than the VM/Zr or VB/Zr-RC groups. Similar results were also found for the 0.3-mm zirconia groups, in which the VB/Zr-SBU group also presented higher strength than the others, which were similar in comparison (Tukey). The Weibull modulus was similar among the groups; however, the characteristic strength was significantly different (P = .000).Conclusion: The zirconia bonding strategy with 50-μm Al2O3 airborne-particle abrasion, followed by a primer application, increases the flexural strength of a stress-free bilayer CAD/CAM ceramic system. [ABSTRACT FROM AUTHOR]

Purpose: Using the microshear bond strength (μSBS) test, this study investigated the bond strength between a hybrid ceramic and the extrinsic characterization layer after different ceramic surface treatments. Materials and Methods: Hybrid ceramic blocks (Vita Enamic, Vita Zahnfabrik) were sectioned and randomly divided into 4 groups (N = 120) according to the surface treatment and aging (n = 15): P: polishing; E: acid etching with HF; A: aluminum oxide blasting; S: self-etching ceramic primer. The specimens were silanized, then cylinders of light-curing characterization material (Vita Enamic Stain, 1.6 mm diameter x 2 mm height) were fabricated, followed by glazing. The specimens were subsequently immersed in distilled water for 24 h and subjected to the μSBS test using a universal testing machine (load cell 0.5 mm/min, 50 kgf) or tested after thermocycling for 10,000 cycles in water (5ºC–55ºC). After treatment, the specimen surfaces were analyzed using SEM, with failure types defined as adhesive, predominantly adhesive, or cohesive. The data were analyzed by two-way ANOVA followed by Tukey’s test (p < 0.05). Results: The most frequent failure type was predominantly adhesive between ceramic and the characterization layer. There were statistically significant differences between the surface treatments (p < 0.05). Thermocycling did not lead to statistically signifcant different results (p > 0.05). For groups P and A, a sharp decrease in SBS was observed. Conclusion: The absence of surface treatment drastically reduced the microshear bond strength between the ceramic and the characterization layer. Conditioning with 5% hydrofluoric acid for 60 s is the most suitable treatment for adhesion of the characterization layer to hybrid ceramic. [ABSTRACT FROM AUTHOR]