The rate of resorption of calcium phosphate self-hardening materials for bone regeneration can be changed by changing the phase composition. The Ca3(PO4)2/CaCO3/Ca(H2PO4)2·H2O/Na2HPO4·12H2O system is important for the synthesis of self-curing bioactive materials with variable resorption rates by changing the ratios of the initial components. Cement compositions in twelve figurative points of a four-component composition diagram at a fixed content in the α-Ca3(PO4)2 system were studied with XRD, FTIR, SEM, calorimetric, and volumetric methods to obtain an idea of the effect of composition on solubility in vitro and resorption in vivo. It was found that the presence of the highly resorbable phase of dicalcium phosphate dihydrate in cement and the substitution of phosphate ions with the carbonate ions of hydroxyapatite increased solubility in vitro and resorption in vivo. The obtained results confirm the possibility of changing the solubility of a final product in the Ca3(PO4)2/CaCO3/Ca(H2PO4)2·H2O/Na2HPO4·12H2O system by changing the ratio of the initial components. [ABSTRACT FROM AUTHOR]

Carbonated hydroxyapatites (CAp) are very close to natural bone apatite in chemical composition and are regarded as a prospective bone mineral substitute for bone surgery and orthopedics. However, until now, the studies and applications of CAp were limited because of the amorphous nature of the synthetic CAp. In the present work, microsized highly crystalline carbonated apatites with uniform hexagonal (hCAp) or platelike (pCAp) morphology have been studied for the first time in vitro and in vivo, comparing against commercial hydroxyapatite (HAp) and β-tricalcuim phosphate (βTCP). In vitro experiments on dissolution of those calcium phosphate ceramics (CPCs) in acetate (pH 5.5) and Tris (pH 7.3) buffer solutions showed the following rank order of the dissolution rates: βTCP > hCAp > pCAp > HAp. The higher dissolution rate of hCAp in comparison with pCAp is explained by chemical anisotropy of the crystallite surfaces, which was proven by SEM studies of the changes in the morphology of hCAp and pCAp crystallites during hydrolysis. A 5-week experiment on subcutaneous implantation of CPC species showed the following rank order of bioresorption rates: βTCP > pCAp > hCAp > HAp. pCAp matrixes exhibited the highest biocompatibility, confirmed by histomorphological analysis. Three-month bone regeneration experiments involving a rat tibial defect model were conducted with 250-500 μm granules of pCAp and pCAp-PEPA [pCAp, pretreated with 2 wt % poly(ethylene phosphoric acid)]. Notably, pCAp-PEPA implants were resorbed at higher rates and induced the formation of more mature osseous tissue, a compact bone with Haversian systems.