Search

The purpose of this study is to comprehensively analyze the influence of different fluences of irradiation with Xe 23+ heavy ions on alterations in the structural, optical, and strength properties of AlN ceramics and to establish a connection between structural distortions and alterations in the optical and mechanical properties of the ceramics. X-ray diffraction, UV-Vis and Raman spectroscopy, and indentation and single-compression methods were used as research methods. During the study, it was demonstrated that at low irradiation fluences, the main role in the changes in the properties of the AlN ceramics is played by effects related to changes in their optical properties and a fundamental absorption edge shift, which characterizes changes in the electronic properties of the ceramics (changes in the distribution of electron density). A study of the variations in the optical properties of the examined samples in relation to the irradiation fluence showed that when the fluence surpasses 5 × 10 11 ion/cm 2 , an extra-spectral absorption band emerges within the range of 3.38-3.40 eV. This band is distinctive for the creation of vacancy O N - V Al complexes within the damaged layer's structure. The presence of these complexes signifies structural deformations and the accumulation of defective inclusions within the damaged layer. An analysis of changes in the parameters of the crystal lattice showed that structural distortions in the damaged layer are due to the accumulation of tensile residual mechanical stresses, an increase in the concentration of which leads to the swelling and destruction of the damaged layer. Some correlations between the mechanical properties of ceramics and the irradiation fluence indicate the ceramics' remarkable resistance to radiation-induced brittleness and weakening. These effects become apparent only when structural damage accumulates, resulting in the swelling of the crystal lattice exceeding 2.5-3%., Competing Interests: The authors declare no conflict of interest.

The aim of this paper is to test the previously stated hypothesis and several experimental facts about the effect of the ion flux or ion beam current under irradiation with heavy ions on the radiation damage formation in the ceramic near-surface layer and their concentration. The hypothesis is that, when considering the possibilities of using ion irradiation (usually with heavy ions) for radiation damage simulation at a given depth, comparable to neutron irradiation, it is necessary to consider the rate factor for the set of atomic displacements and their accumulation. Using the methods of X-ray diffraction analysis, Raman and UV-Vis spectroscopy, alongside photoluminescence, the mechanisms of defect formation in the damaged layer were studied by varying the current of the Xe 23+ ion beam with an energy of 230 MeV. As a result of the experimental data obtained, it was found that, with the ion beam current elevation upon the irradiation of nitride ceramics (AlN) with heavy Xe 23+ ions, structural changes have a pronounced dependence on the damage accumulation rate. At the same time, the variation of the ion beam current affects the main mechanisms of defect formation in the near-surface layer. It has been found that at high values of flux ions, the dominant mechanism in damage to the surface layer is the mechanism of the formation of vacancy defects associated with the replacement of nitrogen atoms by oxygen atoms, as well as the formation of ON-VAl complexes.

The purpose of this study is to assess the effect of doping ZrO 2 ceramics with MgO on radiation swelling and polymorphic transformations, as a result of irradiation with heavy ions. Interest in these types of materials is due to the great prospects for their use as structural materials for new-generation reactors. The study established the dependences of the phase composition formation and changes in the structural parameters following a change in the concentration of MgO. It has been established that the main mechanism for changing the structural properties of ceramics is the displacement of the cubic c-ZrO 2 phase by the Zr 0.9 Mg 0.1 O 2 substitution phase, which leads to an increase in the stability of ceramic properties to irradiation. It has been determined that an increase in MgO concentration leads to the formation of an impurity phase Zr 0.9 Mg 0.1 O 2 due to the type of substitution, resulting in changes to the structural parameters of ceramics. During studies of changes in the strength properties of irradiated ceramics, it was found that the formation of a phase in the Zr 0.9 Mg 0.1 O 2 structure leads to an increase in the resistance to cracking and embrittlement of the surface layers of ceramics.