Search

Polydopamine coatings have been shown to allow to coat almost all materials with conformal films having a tunable thickness from a few up to more than 100 nm (and even more in some specific cases). These films are able to reduce metal cations, to be modified with many chemical moieties and advent hence as a “Holy Grail” in surface chemistry with an impressive amount of applicative papers published since 2007. However, the broad application field and ease of deposition from aqueous solutions hidden the complexity of the deposition mechanism(s). The discovery that polydopamine (PDA) films also form at air/water interfaces (in the absence of stirring or in stirring dependent manner) to yield membranes with physicochemical properties different than PDA films deposited at solid/water interfaces highlighted for the first time that the nature of the interfaces plays a major role in the PDA film growth mechanism and in the film properties. More recent research allowed to show that the surface chemistry of the used solid substrate modifies the composition of the thin deposited PDA film during the early stages of the deposition process with further deposition yielding to an almost substrate-independent PDA film. It is the aim of this review to describe complex surface effects occurring in PDA deposition and hence to complement other reviews which described the complexity of the chemistry yielding to PDA coatings.

Background: Electrodeposition of functional films from polyphenol-containing solutions has emerged as a new field of surface functionalization from bio-sourced molecules. There is, however, almost no knowledge about the chemical structure of such complex films. It is the aim of this research to use the known electrodeposition of films made from catechol and resorcinol, two isomers of dihydroxybenzene, to understand the electrodeposition of a more complex polyphenol, quercetin, which is constituted from a fused catechol and resorcinol moiety. The aim of this article is hence to introduce some methodology in the interpretation of the electrochemical behavior of complex polyphenols starting from their building blocks. Methods: Cyclic voltammetry (CV) is used to deposit films from quercetin and from equimolar blends of catechol and resorcinol on amorphous carbon and gold working electrodes. The main experimental parameter was the potential sweep rate used during the CVs. Results: The CV of quercetin is not the exact sum of the CV of the catechol + resorcinol blends, but the major features are conserved, namely the presence of two main oxidation peaks affiliated to those of catechol and resorcinol but shifted to less anodic potentials. In addition, the anodic electron transfer coefficients of the two oxidation waves of quercetin are higher than those measured in the catechol resorcinol blend. However, film deposition ability is reduced with quercetin compared to catechol + resorcinol blend in probable relationship to steric hindrance occurring during the non-electrochemical crosslinking of the deposit. The quercetin-based films deposited at 10 mV·s−1 on gold electrodes are conformal and display some antioxidant activity. [ABSTRACT FROM AUTHOR]

Sucrose and glycerol have gained attention as additives for hydrogels, owing to their capacity to exert considerable influence over the physicochemical, mechanical, and biological characteristics of these materials. Herein, these effects on agarose hydrogels (AHs) are explored. A series of AHs are synthesized using sucrose (30% and 300% w/v) and glycerol as additives. The storage modulus (10.0–13.7 kPa) and hydrophilicity of the hydrogels (contact angle < 50°) do not vary significantly with sucrose or glycerol addition. However, sucrose enhances the hydration capacity of the hydrogels by up to 170%, whereas glycerol reduces it. Interestingly, sucrose and glycerol individually do not have bacteriostatic effects against Staphylococcus epidermidis, but their combination significantly (p ≤ 0.001) inhibits the growth of both S. epidermidis and Pseudomonas aeruginosa by 63% and 29%, respectively, in comparison to native agarose. Cytotoxicity testing on NIH/3T3 murine fibroblasts reveals that sucrose increases cell viability up to 98%, while glycerol reduces it below 60%. Overall, these hydrogels hold promise for antibacterial biomedical applications as wound dressing materials and surface coatings for medical devices and can also be used to formulate bioinks for 3D bioprinting. [ABSTRACT FROM AUTHOR]

Bioinspired adhesives have been increasingly developed, especially towards a biomedical application. Therefore, in this study, dopamine (DA) was oxidized into polydopamine (PDA) in a gelatin mixture via titration with NaIO4 as a strong oxidant to easily obtain an adhesive antioxidant and self-healing PDA–gelatin hydrogel. Rheology experiments show a stiffness in the order of kPa and a thermal resistance above 50 °C, much above the gel–sol transition temperature of pristine gelatin. After heating at 55 °C, the gel is self-healing. In addition, just after formulation, it shows strong peeling-rate-dependent adhesion to steel with a tensile work per unit area (W) of up to 100 ± 39 J/m2, which is 2.5 times higher than that of the same gel without PDA at a peeling rate of 1000 µm/s. The increase in W between peeling rates of 10 and 1000 µm/s was studied and interpreted in terms of the gels' viscoelasticity. Moreover, this hydrogel offers significant antioxidant activity (measured by DPPH scavenging) that lasts with storage for at least over 15 days, this being then prolonged for 2 additional days, which seems particularly relevant considering the importance of reactive oxygen species (ROS) in wound healing. To summarize, PDA–gelatin gel is a promising strong and antioxidant adhesive. [ABSTRACT FROM AUTHOR]